聚吡咯/海泡石一维纳米复合材料的制备及表征

刘志虎 胡小平 王朝阳 付志兵 卢涛   

  1. 西南科技大学 西南科技大学
  • 收稿日期:2012-06-01 修回日期:1900-01-01 出版日期:2012-09-26 发布日期:2012-09-26

Preparation and Characterization of Polypyrrole/Sepiolite

Zhi-hu Liu HU Xiao-Ping Chao-yang Wang Zhi-bing Fu Tao Lu   

  • Received:2012-06-01 Revised:1900-01-01 Online:2012-09-26 Published:2012-09-26
  • Contact: HU Xiao-Ping

摘要： 以三氯化铁（FeCl3）为氧化剂，十二烷基磺酸钠（SDS）为掺杂剂，通过原位聚合的方法制备了聚吡咯/海泡石（PPy/SEP）纳米复合材料。研究了吡咯（Py）用量、聚合时间、氧化剂用量以及掺杂剂用量对复合材料电导率的影响，确定了制备导电复合材料的工艺条件。结果表明，在Py用量（以SEP质量计）为25 %，聚合温度为0 ℃，聚合时间为12 h，FeCl3/Py摩尔比为2.3/1，SDS/Py摩尔比为1/5的条件下制备的PPy/SEP复合材料电导率为2.15 S/cm。采用透射电镜、红外光谱、X射线衍射及热分析表征纳米复合材料的形貌与结构。结果表明，制备的PPy/SEP纳米复合材料为具有核壳结构的一维纳米复合材料，且PPy以非晶态的形式存在于SEP表面。

关键词: 海泡石, 聚吡咯, 原位聚合, 一维纳米复合材料, 电导率

Abstract: Polypyrrole/sepiolite (PPy/SEP) nanocomposites were prepared via insitu polymerization, using ferric chloride (FeCl3) and sodium dodecylsulfonate (SDS) as oxidant and dopant, respectively. Effects of the content of pyrrole, the polymerization time, and the amount of FeCl3 and SDS on the conductivity of the nanocomposites were investigated. The conductivity of the composite reached 2.15 S/cm when the content of pyrrole was 25 % (based on the mass of SEP), the polymerization temperature was 0 ℃, the polymerization time was 12 h, the mole ratio of FeCl3 and SDS to pyrrole were 2.3∶1 and 1∶5, respectively. The morphology and structure of the nanocomposite was characterized using transmission electron microscope (TEM), Fourier transform infrared (FTIR), Xray diffraction (XRD) and thermal analysis. It showed that PPy/SEP nanocomposite had a onedimensional coreshell structure and the surface of sepiolite was coated by amorphous PPy.

Key words: Sepiolite, Polypyrrole, In-situ polymerization, One-dimensional nanocomposite, Conductivity