Abstract: UVA-340 lamp was used as an artificial acceleratedphotoaging source. The variation in carbonyl index, tensile strength, and elongation at break before and after aging was investigated, and the effect of antiaging agents on antiaging properties of drip irrigation tape was analyzed. It showed that the drip irrigation tapes with selfmade antiaging masterbatch had the best antiaging performance, compared with the 0 days aging sample, retention rate of elongation at break of the samples artificial aging for 10 days, 12 days and naturally exposed to 120 days aging were 94.3 %, 84.0 %, 61.9 %, respectively. UV340nm light at the condition of the radiation strength of 0.68 W/m2, blackboard temperature of 60 ℃, condensing temperature of 50 ℃, exposure time of 3 h, condensing time of 3 h, wind of 10 min, the aging rate was about ten times based on artificial accelerated photoaging more than that at natural environment.
Key words: drip irrigation tape, artificial aging test, UV lamps, elongation at break
mamatjan yimit shuxin di Sanawar ABLA. Research on Aging and Antiaging of Drip Irrigation Tapes[J]. China Plastics, 2013, 27(05): 60-64 .
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.plaschina.com.cn/EN/10.19491/j.issn.1001-9278.2013.05.012
https://www.plaschina.com.cn/EN/Y2013/V27/I05/60