Synthesis of Polyester⁃type Double Bond⁃terminated Polyurethane Prepolymer and Its Application in Bulk Molding Compounds

doi:10.19491/j.issn.1001-9278.2021.09.006

Abstract

Abstract:

Polyester-type double bond-terminated polyurethane prepolymer （HPU） was synthesized by using a high adhesive and high heat-resistant diol （XC-488）， toluene diisocyanate （TDI） and hydroxyethyl methacrylate （HEMA） as raw materials. The bulk molding plastics （BMC） were prepared through blending HPU with unsaturated polyester resin， short cut glass fiber， calcium carbonate， flame retardant at different loadings. Fourier-transform infrared spectroscopy， differential scanning calorimeter， mechanical property test， water absorption test， melt fluidity test， acid-base resistance test， aging test and scanning electron microscope were used to characterize the structures and properties of the resultant BMC. The results indicated that the composite achieved the optimal comprehensive mechanical properties at an HPU content of 6 wt%. They also achieved tensile strength of （47.24±0.42） MPa， bending strength of （117.76±0.65） MPa and impact strength of （33.8 ± 0.2） kJ/m².

Key words: bulk molding compound, polyurethane prepolymer, double bond termination, hydroxyethyl methacrylate

CLC Number:

TQ323.4

LIU Lei, YANG Jianjun, WU Qingyun, WU Mingyuan, ZHANG Jianan, LIU Jiuyi. Synthesis of Polyester⁃type Double Bond⁃terminated Polyurethane Prepolymer and Its Application in Bulk Molding Compounds[J]. China Plastics, 2021, 35(9): 34-39.

Figures/Tables 10

References 18

1	雷世谱，邓炳耀，徐煜东，等. 不饱和聚酯树脂成膜剂的制备和性能表征［J］. 塑料工业， 2019， 47（9）： 15⁃19.
	LEI S P， DENG B Y， YU Y D， et al. Preparation and Characterization of Film⁃forming Agent for Unsaturated Polyester Resin［J］. Plastics Industry， 2019， 47（9）： 15⁃19.
2	MIRIAM I， LUKAS M， JULIAN G， et al. Comparison of Filler⁃dependent Mechanical Properties of Jute Fiber Reinforced Sheet and Bulk Molding Compound［J］. Compo⁃site Structures， 2018， 203： 960⁃967.
3	SREENIVASAN S， SULAIMAN S， ARIFFIN M K A， et al. Physical Properties of Novel Kenaf Short Fiber Reinforced Bulk Molding Compounds （BMC） for Compression Moulding［J］. Materials Today： Proceedings， 2018， 5（1）： 1 226⁃1 232.
4	CHOWDHURY A， SINGH S K， ANTHONY P. Structural and Thermal Characterization of Castor Oil Based Unsaturated Polyester Resin［J］. Asian Journal of Chemistry， 2020， 32（7）： 1 763⁃1 767.
5	BEGUM M， TANVIR N. Fabrication and Characterization of Cane Fiber Reinforced Unsaturated Polyester Resin Composites［J］. Bangladesh Journal of Scientific and Industrial Research， 2019， 54（3）： 247⁃256.
6	滕方瑞，王小峰，蒋晶，等. 碳纳米管/纤维素在不饱和聚酯树脂中的分散性及力学性能研究［J］. 中国塑料， 2021， 35（3）： 30⁃37.
	TENG F R， WANG X F， JIANG J， et al. Dispersion and Mechanical Properties of Carbon Nanotubes / Cellulose in Unsaturated Polyester Resin ［J］. China Plastics， 2021， 35（3）： 30⁃37.
7	HUANG Z， GE H Y， YIN J J， et al. Effects of Fiber Loading and Chemical Treatments on Properties of Sisal fiber⁃reinforced Sheet Molding Compounds［J］. Journal of Composite Materials， 2017， 51（22）： 3 175⁃3 185.
8	GRISHCHUK S， KARGER K J. Modification of Vinyl Ester and Vinyl Ester⁃urethane Resin⁃based Bulk Molding Compounds （BMC） with Acrylated Epoxidized Soybean and Linseed Oils［J］. Journal of Materials Science， 2012， 47（7）： 3 391⁃3 399.
9	陈志平，冯羽风，陆春立，等. 热塑性聚氨酯/聚乳酸共混材料的制备及性能表征［J］. 绝缘材料， 2020， 53（5）： 13⁃17.
	CHEN Z P， FENG Y F， LU C L， et al. Preparation and Characterization of Thermoplastic Polyurethane / Polylactic Acid Blends ［J］. Insulating Materials， 2020， 53（5）： 13⁃17.
10	FAUDREE M C， NISHI Y， ASAKA T， et al. A “Mold Filling” Model from Viscosity Measurements in a Strengthened Injection⁃Molded Reduced Glass Fiber Length Polyester Bulk Molding Compound［J］. Materials Transactions， 2017， 58（3）： 499⁃504.
11	WU W， HUANG H. Styrene Butadiene Rubber/Silicone Rubber Blends Filled With Dough Moulding Compound［J］. Journal of Macromolecular Science Part B， 2019， 58（2）： 330⁃340.
12	王泽群，刘凉冰，张思彤，等. 玻璃纤维增强聚氨酯复合材料性能的研究［J］. 特种橡胶制品， 2019， 40（1）： 17⁃20.
	WANG Z Q， LIU L B， ZHANG S T， et al. Study on Properties of Glass Fiber Reinforced Polyurethane Composites［J］. Special Rubber Products， 2019， 40（1）： 17⁃20.
13	KASPRZYK P， SADOWSKA E， DATTA J. Investigation of Thermoplastic Polyurethanes Synthesized via Two Different Prepolymers［J］. Journal of Polymers and the Environment， 2019， 27（11）： 2 588⁃2 599.
14	WENG F， WANG M， KORANTENG E， et al. Effects of PBA⁃Based Polyurethane Prepolymer as Compatibilizer on the Properties of Polylactic Acid⁃Starch Composites［J］. Starch⁃Starke， 2018， 71：1800205.
15	彭新龙，梁卓恩. 纳米增韧不饱和聚酯基复合材料的性能研究［J］. 广东化工， 2020， 47（21）： 33⁃35.
	PENG X L， LIANG Z E. Study on the Properties of Nano Toughened Unsaturated Polyester Matrix Composites ［J］. Guangdong Chemical Industry. 2020， 47（21）： 33⁃35.
16	ZHANG H C， KANG B H， CHEN L S， et al. Enhancing Toughness of Poly （Lactic Acid）/Thermoplastic Polyurethane Blends via Increasing Interface Compatibility by Polyurethane Elastomer Prepolymer and Its Toughening Mechanism［J］. Polymer Testing， 2020， 87： 106521.
17	董平江，吕宏达，翟涛，等. 水性聚氨酯/纳米二氧化钛复合材料的制备和表征［J］. 聚氨酯工业， 2015， 30（1）： 14⁃17.
	DONG P J， LV H D， ZHAI T， et al. Preparation and Characterization of Waterborne Polyurethane/Nano Titanium Dioxide Composites［J］. Polyurethane Industry， 2015， 30（1）： 14⁃17.
18	汪传生，温南南，温潇潇，等. 热塑性聚氨酯/顺丁橡胶共混材料性能的研究［J］. 橡胶工业， 2019， 66（10）： 754⁃757.
	WANG C S，WEN N N，WEN X X，et al.Study on Properties of TPU/BR Blends［J］.China Rubber Industry，2019，66（10）：754⁃757.

原料	含量/%
UPR	15
PS	5
重质碳酸钙	45
RHTPU?015A	20
玻璃纤维	10
TBPB	3
对苯二酚	2

原料	含量/%
UPR	15
PS	5
重质碳酸钙	45
RHTPU?015A	20
玻璃纤维	10
TBPB	3
对苯二酚	2

样品编号	HPU含量/%	BMC含量/%
0^#	0	100
1^#	2	98
2^#	4	96
3^#	6	94
4^#	8	92

样品编号	HPU含量/%	BMC含量/%
0^#	0	100
1^#	2	98
2^#	4	96
3^#	6	94
4^#	8	92

HPU含量/%	拉伸强度/MPa	弯曲强度/MPa	冲击强度/kJ?m^-2
0	44.91±0.52	87.82±0.78	20.5±0.3
2	45.35±0.46	91.85±0.64	26.6±0.4
4	45.83±0.54	105.43±0.69	30.7±0.3
6	47.24±0.42	117.76±0.65	33.8±0.2
8	43.62±0.57	115.48±0.82	32.2±0.3