Study on the Effect of Natural Environment on Coating Agent Performance of Aerostat Skin Materials

doi:10.19491/j.issn.1001-9278.2021.09.019

Abstract

Abstract:

Coating agent is an important part of skin material，which directly affects the mechanical properties of skin materials. In order to understand a change rule in the properties of coating agent in skin materials under the natural environment. Taking the URETEK?5972 material as research object，this material was exposed to the natural environment for 0 to 4 years. The characteristic functional groups and mechanical properties of the URETEK?5972 were characterized using Gas permeameter and infrared spectrometer and mechanical testing machine. The influence of exposure time under the natural environment on the performance of functional layer was analyzed， and the change rule of coating agent was explored. The results indicated that the proportion of free carbonyl group in the coating agent decreased with an increase in natural environment exposure time. The intermolecular force between the coating agent and functional layers decreased， leading to a reduction in the connection fastness between the functional layers.

Key words: coating agent, skin material, natural environment, functional layer, free carbonyl group, intermolecular force

CLC Number:

323.8

LIU Pingping, LU Huan, ZHU Lifang, DING Yongzhi. Study on the Effect of Natural Environment on Coating Agent Performance of Aerostat Skin Materials[J]. China Plastics, 2021, 35(9): 122-127.

Figures/Tables 9

References 26

1	胡文琳，从力田.平流层飞艇预警探测技术进展及应用展望［J］.现代雷达，2011，33（1）：5⁃7.
	HU W L，CONG L T. Technologies Progress and Applied Expectation of Stratospheric Airship［J］.Modern Radar，2011，33（1）：5⁃7.
2	李智斌，黄宛宁，张钊.2018年临近空间科学热点回眸［J］.科技导报，2019，37（1）：44⁃51.
	LI Z B，HUANG W N，ZHANG Z. Summary of the Hot Spots of Near Space Vehicles in 2018［J］.Science & Technology Review，2019，37（1）：44⁃51.
3	彭桂林，万志强.中国浮空器遥感遥测应用现状与展望［J］.地球信息科学，2018，21（4）：504⁃511.
	PENG G L，WAN Z Q.The Present Situation and Prospect of Aerostat Applied to Remote Sensing and Remote Survey in China［J］.Journal of Geo⁃information Science，2018，21（4）：504⁃511.
	梁军民，李立钢.一种应急救灾飞艇部署与规划方法研究［J］.遥感技术与应用，2014，29（4）：639⁃645.
	LIANG J M，LI L G.Research on the Emergency Relief Airship Deployment and Planning Method［J］.Remote Sensing Technology and Application，2014，29（4）：639⁃645.
4	张振国，孙旭，孙文峰.无人机用于空军战略预警作战的可行性分析［J］.现代雷达，2012，32（10）：6⁃10.
	ZHANG Z G，SUN X，SUN W F.Feasibility Analysis of UAV Applying in Air Force Strategic Early Warning Operation［J］. Modern Radar，2012，32（10）：6⁃10.
5	彭越，徐洋，高晨，等.基于飞艇捕获的运载火箭空中回收方案设计及关键技术［J］.导弹与航天运载技术，2018（3）：27⁃35.
	PENG Y，XU Y，GAO C，et al.A Novel⁃Air Recovery Method of Launch Stage Based on Interception with Airships［J］.Missiles and Space Vehicles，2018（3）：27⁃35.
6	胡勤友，张正儒，刘侠.浮空载具在海事领域的应用［J］.中国航海，2014，37（3）：90⁃94.
	HU Q Y，ZHANG Z R，LIU X.Application of Aerostat in Maritime Field［J］.Navigation of China，2014，37（3）：90⁃94.
7	张爱武，郭超凡，鄢文艳.区间优化提高牧草粗蛋白含量遥感估算精度［J］.农业工程学报，2018，34（14）：149⁃156.
	ZHANG A W，GUO C F，YAN W Y.Improving Remote Sensing Estimation Accuracy of Pasture Crude Protein Content by Interval Analysis［J］.Transaction of the Chinese Society of Agricultural Engineering，2018，34（14）：149⁃156.
8	甘晓华，郭颖.飞艇技术概论［M］.北京：国防工业出版社，2005：14⁃30.
9	刘军虎，刘振辉，纪雪梅，等.平流层飞艇蒙皮材料的研究现状［J］.信息记录材料，2010，17（2）：1⁃5.
	LIU J H，LIU Z H，JI X M，et al. Research Status of Stratospheric Airship Envelop Material［J］. Information Recording Materials，2010，17（2）：1⁃5.
11	程书通.飞艇蒙皮材料在短期老化与折皱损伤条件下单轴拉伸力学性能［D］.上海：上海交通大学，2019.
12	徐文.平流层飞艇蒙皮材料力学性能研究［D］. 上海：上海交通大学，2017.
13	李正雄.浅谈织物涂层剂［J］.印染助剂，2003，20（1）：7⁃10.
	LI Z X.An Overview of Textile Coating Agents［J］.Textile Auxiliaries ， 2003，20（1）：7⁃10.
14	高岩磊，崔文广，牟微，等.高分子材料的老化研究进展［J］.河北化工，2008，31（1）：29⁃31.
	GAO Y L，CUI G W，MOU W，et al.Progress in Aging of Polymer Materials［J］.Hebei Chemical Industry，2008，31（1）：29⁃31.
15	黄微波，车凯圆，吕平，等.聚氨酯涂层老化研究进展［J］.聚氨酯工业，2018，33（6）：1⁃4.
	HAUNG W B，CHE K Y，LV P，et al.Research Progress of Polyurethane Coating Aging［J］.Polyurethane Industry ，2018，33（6）：1⁃4.
16	叶毓辉，康伟.纳米二氧化钛防紫外线转移涂层整理［J］.针织工业，2011，11：33⁃35.
	YE Y H，KANG W.Study on Anti Ultraviolet Transfer Coating of Nano Titanium Dioxide［J］. Knitting Industries，2002，30（3）：63⁃64.
17	刘绍基.高分子老化与防老化［J］.腐蚀与防护，1994，15（1）：45⁃49.
	LIU S J.Polymer Aging and Anti⁃aging［J］.Corrosion & Protection，1994，15（1）：45⁃49.
18	顾美华，李德宏，孟家明，等.气候老化、热氧老化和光老化实验对涤纶短纤维性能结构的影响［J］.合成技术及应用，1994，9（2）：12⁃17.
	GU M H，LI D H，MENG J M，et al.Effect of Climate Aging，Thermal Oxidation Aging and Light Aging on Properties and Structure of Polyester Staple Fiber［J］.Synthetic Technology & Application，1994，9（2）：12⁃17.
19	袁卫民，孙克俭，李艳民.热氧老化对涤纶线性能的影响［J］.特种橡胶制品，2015，33（6）：45⁃46.
	YUAN W M， SUN K J， LI Y M. Effect of Thermal Oxidative Aging on Properties of Polyester Yarn［J］. Special Purpose Rubber Products，2015，33（6）：45⁃46.
20	魏屈平，倪爱清，张鸿，等.氙灯加速老化对聚酯纤维/PVC柔性复合材料力学性能影响的研究［J］.玻璃钢/复合材料，2017（9）：82⁃88.
	WEI Q P，NI A Q，ZHANG H，et al. The Study of Accelerated Aging of Artificial Xenon ARC Lamp on the Bursting and Tearing Properries of Polyester Fiber/PVC Flexible Composite［J］. Fiber Reinforced Plastics/Composites，2017（9）：82⁃88.
21	窦宝峰，逄型召，王兆希，等.浮空器用柔性复合材料的力学性能［J］.理化检验•物理分册，2009，45（12）：740⁃743.
	DOU B F ，PANG X Z ，WANG Z X，et al. Mechanical Properties of Flexible Composites for Aerostat［J］.PTCA（PART：A PHYS.TEST.），2009，45（12）：740⁃743.
22	邓新华，袁哓燕，孙元.聚氯乙烯蒙皮材料撕破强度研究［J］.上海纺织科技，2002，30（3）：63⁃64.
	DENG X H，YUAN X Y，SUN Y.Study on Tear Strength of PTFE Coated Fabric［J］.Shanghai Textile Science & Technology，2002，30（3）：63⁃64.
23	陈维涛，李树材.水性聚氨酯结构与微相分离的研究［J］.涂料工业，2005，35（6）：13⁃15.
	CHEN W T，LI S C.Studies on Structure and Micro Phase Separation of Waterborn Polyurethane ［J］.Paint & Coating Industry，2005，35（6）：13⁃15.
24	COLEMEN M M，LEE K H，SKROVANEK D J.Hydrogen Bonding in Polymers.4.Infrared Temperature Studies of a Simple Polyurethane ［J］.Macromolecules，1986，19：2 149⁃2 156.
25	AYRES E， ́FICE R L ORE，YOSHIDA M I.Phase Morphology of Hydrolysable Polyurethanes Derived from Aqueous Dispersions［J］.European Polymer Journal，2007，43：3 510⁃3 521.
26	氢键位阻对聚氨酯粘弹性影响研究［D］. 哈尔滨：哈尔滨工程大学，2015.上海交通大学，2017.

年份	最高气温/℃	最低气温/℃	平均气温/℃	年光照时间/h	年降雨量/mm
2016	36.5	-4.4	17.0	1 638.1	1 397.7
2017	37.7	-1.6	17.1	1 754.6	1 103.3
2018	35.6	-6.8	17.0	1 744.2	1 027.9
2019	37.6	-4.1	17.1	1 748.3	770.9
2020	36.1	-4.4	16.8	1 617.8	1 277.1

年份	最高气温/℃	最低气温/℃	平均气温/℃	年光照时间/h	年降雨量/mm
2016	36.5	-4.4	17.0	1 638.1	1 397.7
2017	37.7	-1.6	17.1	1 754.6	1 103.3
2018	35.6	-6.8	17.0	1 744.2	1 027.9
2019	37.6	-4.1	17.1	1 748.3	770.9
2020	36.1	-4.4	16.8	1 617.8	1 277.1

老化时间/年	峰位置/cm^-1			峰面积比例
老化时间/年	游离羰基	不完全氢键羰基	完全氢键羰基	游离羰基	不完全氢键羰基	完全氢键羰基	氢键化羰基
0	1 733	1 707	1 652	0.53	0.09	0.38	0.47
1	1 731	1 709	1 652	0.35	0.23	0.42	0.65
2	1 733	1 710	1 653	0.12	0.42	0.46	0.88
3	1 733	1 709	1 651	0.11	0.34	0.55	0.89
4	1 730	1 709	1 651	0.08	0.33	0.59	0.92

老化时间/年	峰位置/cm^-1			峰面积比例
老化时间/年	游离羰基	不完全氢键羰基	完全氢键羰基	游离羰基	不完全氢键羰基	完全氢键羰基	氢键化羰基
0	1 733	1 707	1 652	0.53	0.09	0.38	0.47
1	1 731	1 709	1 652	0.35	0.23	0.42	0.65
2	1 733	1 710	1 653	0.12	0.42	0.46	0.88
3	1 733	1 709	1 651	0.11	0.34	0.55	0.89
4	1 730	1 709	1 651	0.08	0.33	0.59	0.92

[1]	JIN Qingping, YI Jianming, GAO Yonghong, CAO Nannan, DENG Siyuan. Effect on mechanical properties of glass⁃fiber⁃reinforcement polymer bars exposure to alkaline solution under natural ambient temperature [J]. China Plastics, 2022, 36(2): 89-95.
[2]	ZHANG Xue, GUO Huiliang, ZHONG Zhenhua, CAI Pingxiong. Effect of Organic Coating Agent on Properties of Titanium Dioxide Products for Masterbatch [J]. China Plastics, 2020, 34(10): 32-36.