Effect of oil⁃resistant compatibilizer POE⁃g⁃AN on properties of EVA/PE⁃LLD cable materials

doi:10.19491/j.issn.1001-9278.2022.10.008

Abstract

Abstract:

The effects of ethylene⁃octene copolymer grafted acrylonitrile （POE⁃g⁃AN） oil⁃resistant compatibilizer on oil resistance， mechanical properties and electrical properties of EVA/PE⁃LLD cable materials were studied. The results showed that with the increase of the amount of POE⁃g⁃AN， the tensile strength， oil resistance and electrical properties of the material all showed a trend of increasing or decreasing first， while the elongation at break increased continuously. When the amount of the graft was 6 wt%， The interphase compatibility improvement effect is the best. At this time， the oil resistance of the modified cable material：the absolute value of the tensile strength， the absolute value of elongation at break， the absolute value of mass and volume change rate is the smallest， which are 35.7 %， 34.6 %， 15.69 %，15.35 %，and the tensile strength increased by 8.5 % to 13.02 MPa， and the elongation at break was 274.15 %； the maximum DC breakdown field strength was 199 kV/mm， and the maximum volume resistivity was 7.84×10¹² Ω·m.

Key words: ethylene?octene copolymer, acrylonitrile, oil resistance, grafting, cable material

CLC Number:

TQ325.5

ZHANG Wenlong, ZHANG Lin, CHEN Yu. Effect of oil⁃resistant compatibilizer POE⁃g⁃AN on properties of EVA/PE⁃LLD cable materials[J]. China Plastics, 2022, 36(10): 54-59.

Figures/Tables 9

References 18

1	张伟，陈杰，李陈莹，等.无卤阻燃聚烯烃电力电缆料的应用现状［J］.中国塑料，2022，36（1）：184⁃191.
	ZHANG W， CHEN J， LI C Y，et al. Applications of halogen⁃free flame⁃retardant polyolefin power cable materials ［J］. China Plastics，2022，36（1）：184⁃191.
2	李孟哲，姜青松，石亚梅，等.耐油条件对交联聚烯烃型电缆材料性能的影响［J］.电线电缆，2021（6）：28⁃30.
	LI M Z， JIANG Q S， SHI Y M， et al. Effect of oil resistance conditions on properties of crosslinked polyolefin cable material［J］. Electric Wire Cable，2021（6）：28⁃30.
3	Prasertsri H， Kurakanok K， Sukkapan N. Physico-mechanical properties and automotive fuel resistance of EPDM/ENR blends containing hybrid fillers［J］. Polymer Research 2016，23（11）：228⁃232.
4	蒋正勇，夏明慧，冷静，等.机车车辆电缆用耐油橡胶绝缘料的研制［J］.电线电缆，2019（6）：22⁃24.
	JIANG Z Y， XIA M H， LENG J， et al.Development of oil resistant rubber insulation for railway rolling stock cable［J］. Electric Wire Cable， 2019（6）：22⁃24.
5	金楷皓. 双耐油低烟无卤聚烯烃电缆料阻燃机理的研究［D］.淄博：山东理工大学，2020.
6	Nihmath A， Ramesan M T.Comparative evaluation of oil resistance， dielectricproperties， AC conductivity， and transport properties of nitrile rubber and chlorinated nitrile rubber［J］. Progress in Rubber Plastics Recycling Technology， 2021， 37（2）：131⁃147.
7	邵如，王洁雨，汪子健，等. 耐油EVA/ATH交联复合材料的制备与研究［J］. 弹性体， 2020， 30（3）：20⁃24.
	SHAO R， WANG J Y， WANG Z J . et al. Preparation and research on oil resistant EVA/ ATH crosslin ked composite［J］. China Elastomerics， 2020， 30（3）：20⁃24.
8	Zou H， Sun J， Xiao G， et al. Preparation and characterization of flame retardant and low smoke releasing oil⁃resistant EVA/NBR blends［J］. Chinese Journal of Polymer Science， 2015， 33（4）： 554⁃563.
9	邹欢，谷晓昱，孙军，等.化学交联EVA/NBR阻燃复合材料的燃烧行为及力学性能［J］.中国塑料，2013，27（6）：28⁃32.
	ZOU H， GU X Y， SUN J， et al.Investigation on flame retardancy and mechanical property of chemical cross linked EVA/NBR composites ［J］. China Plastics，2013，27（6）：28⁃32.
10	汪子健. 耐油无卤阻燃复合材料的制备与性能研究［D］.合肥：合肥工业大学，2020.
11	Paul B J， Jeffrey S W， John R.Material properties and phase behavior of crosslinkable acrylonitrile⁃butadiene copolymer/ethylene vinyl acetate/carbon black composites［J］.Polymer Composites，2021，42（5）：27⁃29.
12	闫珂华，周松，邵钰童，等. BF/PE⁃g⁃MAH/EVA复合材料的结构和性能［J］.塑料， 2018， 47（6）： 43⁃47.
	YAN K H， ZOU S， SAO Y T， et al. Structure and pro⁃perties of BF/PE⁃g⁃MAH/EVA Composite［J］ Plastics， 2018， 47（6）： 43⁃47.
13	Sung I K， Lee W K， Chan Y P. Study on the oil resistance， morphological and dynamic mechanical properties， flame retardance of ethylene vinyl acetate copolymer and ethylene propylene rubber compounds［J］. 2017，64（23）：28.
14	孙贺霞. mPE/EVA⁃g⁃AN/NBR耐油材料的制备与性能研究［D］.哈尔滨：哈尔滨理工大学，2021.
15	张文龙，于浩，张学悟，等.微波辅助POE⁃g⁃AN的制备与耐油性［J］.塑料工业，2022，50（2）：25⁃31.
	ZHANG W L， YU H， ZHANG X W， et al. Microwave⁃ assisted preparation and oil resistance of POE⁃g⁃AN ［J］.China Plastics Industry， 2022，50（2）：25⁃31.
16	张文龙，马振清，戴亚杰，等.乙烯咔唑接枝聚乙烯的制备及其介电性能［J］.高电压技术，2017，43（9）：2 813⁃2 817.
	ZHANG W L，MA Z Q，DAI Y J，et al Preparation of vinyl carbazole grafted polyethylene and its dielectric properties［J］. High Voltage Engineering. 2017，43（9）：2 813⁃2 817.
17	马超，闵道敏，李盛涛，等.聚丙烯/氧化铝纳米电介质的陷阱与直流击穿特性［J］.物理学报，2017，66（6）：281⁃289.
	MA C， MIN D M， LI S T，et al. Trap distribution and direct current breakdown characteristics in polypropylene/Al₂O₃ nanodielectrics［J］. Acta Physica Sinica， 2017，66（6）：281⁃289.
18	张文龙，吴月，杨佳明，等.EVA对MgO/聚烯烃纳米复合材料介电性能的影响［J］.高分子材料科学与程，2013，29（8）：117⁃120，125.
	ZHANG W L， WU Y， YANG J M，et al.Effects of EVA on the dielectric properties of MgO/LDPE nano⁃compo⁃sites［J］ Polymeric Materials Science and Engineering， 2013，29（8）：117⁃120，125.

样品编号	EVA含量	PE⁃LLD含量	POE⁃g⁃AN含量	1010含量
0^#	70	30	0	0.6
1^#	70	30	2	0.6
2^#	70	30	4	0.6
3^#	70	30	6	0.6
4^#	70	30	8	0.6
5^#	70	30	10	0.6

样品编号	EVA含量	PE⁃LLD含量	POE⁃g⁃AN含量	1010含量
0^#	70	30	0	0.6
1^#	70	30	2	0.6
2^#	70	30	4	0.6
3^#	70	30	6	0.6
4^#	70	30	8	0.6
5^#	70	30	10	0.6

POE⁃g⁃AN 含量/%	拉伸强度/MPa	断裂伸长率/%	拉伸强度变化率/%	断裂伸长率变化率/%	体积变化率/%	质量变化率/%
POE⁃g⁃AN 含量/%	≥9	≥125	≤±50	≤±50	≤±30	≤±30
0	12.02	206.48	-70.62	-85.44	36.6	38.47
2	12.46	226.64	-66.9	-74.7	32.87	35.73
4	12.62	246.3	-54.2	-55.3	26.54	28.68
6	13.02	274.15	-35.7	-34.6	15.35	15.69
8	12.62	294.13	-39.1	-37.2	18.99	17.72
10	11.36	345.15	-45	-47.5	20.45	19.09

POE⁃g⁃AN 含量/%	拉伸强度/MPa	断裂伸长率/%	拉伸强度变化率/%	断裂伸长率变化率/%	体积变化率/%	质量变化率/%
POE⁃g⁃AN 含量/%	≥9	≥125	≤±50	≤±50	≤±30	≤±30
0	12.02	206.48	-70.62	-85.44	36.6	38.47
2	12.46	226.64	-66.9	-74.7	32.87	35.73
4	12.62	246.3	-54.2	-55.3	26.54	28.68
6	13.02	274.15	-35.7	-34.6	15.35	15.69
8	12.62	294.13	-39.1	-37.2	18.99	17.72
10	11.36	345.15	-45	-47.5	20.45	19.09

POE⁃g⁃AN含量/%	直流击穿场强/kV·mm^-1	形状因子
0	143.25	10.19
2	153.91	10.22
4	158.32	12.28
6 8 10	198.26 189.10 172.43	13.46 11.64 10.47