Preparation and performance of high⁃flowing and high⁃impact polystyrene

doi:10.19491/j.issn.1001-9278.2023.02.001

Abstract

Abstract:

In this study， high⁃flowing and high⁃impact polystyrene （FHIPS） was prepared through a continuous bulk polymerization process. The effect of the addition amount of mineral oil on the melt flow rate and mechanical properties of the as⁃prepared FHIPS was investigated， and its microscopic and macroscopic properties were comparatively studied with those of foreign standard products. The results indicated that the melt flow rate of FHIPS gradually increased with an increase in the addition amount of mineral oil. Compared to the similar foreign product of FHIPS （HIPS425TVL）， the FHIPS prepared in this work exhibited the same physical properties along with a higher melt flow index.

Key words: high?impact polystyrene, high?flowing polystyrene, polybutadiene rubber, continuous bulk polymerization process

CLC Number:

TQ325.2

HAO Chunbo, XIAO Dajun, LIU Quanzhong, ZHENG Shusong, WANG Chun, LI Chunhui, YAO Xiuchao. Preparation and performance of high⁃flowing and high⁃impact polystyrene[J]. China Plastics, 2023, 37(2): 1-6.

Figures/Tables 9

References 20

1	刘宏吉. 国内外聚苯乙烯工艺技术分析［J］. 弹性体， 2013， 23（3）： 72⁃77.
	LIU H J. Analysis on production technology of polystyrene at home and abroad［J］. China Elastomerics， 2013， 23（3）： 72⁃77.
2	陈朝阳，陈利傑. 国内聚苯乙烯生产工艺述评［J］. 合成树脂及塑料， 2003， 20（3）： 39⁃43.
	CHEN C Y， CHEN L J. The review of production technolo⁃gy of polystyrene in China［J］. China Synthetic Resin and Plastics， 2003， 20（3）： 39⁃43.
3	任孟萍. GPPS和HIPS本体聚合工艺评述［J］. 化工设计， 1992， 2（6）： 20⁃23.
4	胡景沧. 聚苯乙烯技术发展趋向及国产化［J］. 石油化工设计， 1998， 15（1）： 6⁃14，61.
	HU J C. Polystyrene technology developing trend and nationalization［J］. China Petrochemical Design， 1998， 15（1）： 6⁃14，61.
5	文红梅.苯乙烯聚合物的橡胶增韧探究［J］. 广东化工， 2012， 39（5）： 51⁃52，14.
	WEN H M. Research on rubber toughening styrene of polymers［J］. Guangdong Chemical Industry， 2012， 39（5）： 51⁃52，14.
6	王益波，袁博，周川，等. 本体连续法制备高抗冲聚苯乙烯树脂引发体系的研究［J］. 塑料工业， 2014， 42（1）： 9⁃13.
	WANG Y B， YUAN B， ZHOU C. Polymerization of high impact polystyrene resin initiation system by continuous bulk process［J］. China Plastics Industry， 2014， 42（1）： 9⁃13.
7	常丽，胡雁鸣，李杨，等. 本体原位法制备高抗冲聚苯乙烯［J］. 石油化工， 2011， 40（8）： 850⁃855.
	CHANG L， HU Y M， LI Y. Preparation of high impact polystyrene via in⁃situ bulk polymerization［J］. Petrochemical Technology， 2011， 40（8）： 850⁃855.
8	常丽. 本体原位法制备高抗冲聚苯乙烯树脂［D］.大连：大连理工大学， 2011.
9	贾忠明. 苯乙烯系增韧树脂本体原位制备技术的研究［D］.大连：大连理工大学，2009.
10	张钦文. 聚苯乙烯聚合机理［J］. 广东化工， 2008， 35（12）： 71⁃73.
	ZHANG Q W. The polyreaction principle of polystyrene［J］. Guangdong Chemical Industry， 2008， 35（12）： 71⁃73.
11	高文彬，乔庆东. 高抗冲聚苯乙烯改性的发展趋势［J］. 辽宁化工， 2004， 33（12）： 706⁃708.
	GAO W B， QIAO Q D. Development trend of modification of high⁃impact polystyrene［J］. Liaoning Chemical Industry， 2004， 33（12）： 706⁃708.
12	王淑敏. 多官能度引发体系增韧苯乙烯系树脂的研究［D］. 大连：大连理工大学， 2009.
13	伍斌. 高抗冲聚苯乙烯中的橡胶颗粒尺寸控制［J］. 塑料科技， 2002， 5： 43⁃44，63.
	WU B. Size controlling of rubber particles in HIPS［J］. Plastics Science & Technology， 2002， 5： 43⁃44，63.
14	靳忠霞. 本体聚苯乙烯树脂冲击强度影响因素分析［J］. 石化技术与应用， 2000， 18（2）： 74⁃76.
	JIN Z X. Analysis on factors affecting impact strength of bulk polystyrene resin［J］. Petrochemical Technology & Application， 2000， 18（2）： 74⁃76.
15	袁惠根，潘仁云，周其云，等. 高抗冲聚苯乙烯的研究⁃Ⅱ.本体预聚合时的相转变［J］. 合成橡胶工业， 1984，5： 347⁃351.
	YUAN H G， PAN R Y， ZHOU Q Y. A study on the molecular structure and properties of carboxylated polychloroprene latex produced in pilot plant［J］. China Synthetic Rubber Industry， 1984，5： 347⁃351.
16	冯地柏. 高抗冲聚苯乙烯生产方法的技术经济比较［J］.合成橡胶工业， 1982，1： 7⁃11.
17	王新，王兆波，吴其晔. HIPS填充体系的流变行为研究［J］. 材料科学与工艺， 2005， 13（6）： 633⁃636.
	WANG X， WANG Z B， WU Q Y. Rheological behavior of nano⁃TiO₂/HIPS matrix［J］. Materials Science & Technology， 2005， 13（6）： 633⁃636.
18	陈大柱，何平笙，姚远. 高抗冲聚苯乙烯粘土纳米复合材料的制备、热稳定性及流变性能［J］. 高分子学报， 2005，1： 102⁃107.
	CHEN D Z， HE P S， YAO Y. Thermal and rheological properties of high⁃impact polystyrene/clay nanocomposites［J］. Acta Polymerica Sinica， 2005，1： 102⁃107.
19	危学兵，余维刚，申小敏，等. 环氧大豆油对高流动苯乙烯⁃乙烯/丁烯⁃苯乙烯/聚丙烯复合材料的结构与流变性能的影响［J］. 塑料工业， 2022， 50（8）： 170⁃175.
	WEI X B， YU W G， SHEN X M. Effects of epoxidized soybean oil on the structure and rheological properties of high flow styrene⁃ethylene /butene⁃styrene /polypropylene composites［J］. China Plastics Industry， 2022， 50（8）： 170⁃175.
20	周川. 连续本体法制备ABS树脂的工艺研究［D］. 大连：大连理工大学， 2018.

工艺参数	注射温度/℃	注射位置/mm	注射压力/MPa	冷却时间/s
一段	195	127	81	60
二段	200	120	75
三段	200	91	125
四段	195	27	30

工艺参数	注射温度/℃	注射位置/mm	注射压力/MPa	冷却时间/s
一段	195	127	81	60
二段	200	120	75
三段	200	91	125
四段	195	27	30

产品	冲击强度/kJ·m^-2	弯曲强度/MPa	弯曲模量/MPa
1	14.21	48.59	2 250
2	12.98	47.12	2 247
3	11.98	45.69	2 239

产品	冲击强度/kJ·m^-2	弯曲强度/MPa	弯曲模量/MPa
1	14.21	48.59	2 250
2	12.98	47.12	2 247
3	11.98	45.69	2 239

样品	苯乙烯含量/%	丁二烯含量/%	M_n	M_w	PDI
FHIPS	92.3	7.7	57 410	191 097	2.82
国外高流动HIPS	92.1	7.9	65 321	150 394	2.31