China Plastics ›› 2023, Vol. 37 ›› Issue (10): 34-39.DOI: 10.19491/j.issn.1001-9278.2023.10.005
• Materials and Properties • Previous Articles Next Articles
GU Hainan(), YING Jie, QIU Qihao, CHEN Meng, WANG Chenye, TONG Qifeng
Received:
2023-05-06
Online:
2023-10-26
Published:
2023-10-23
CLC Number:
GU Hainan, YING Jie, QIU Qihao, CHEN Meng, WANG Chenye, TONG Qifeng. Development for applications of bio⁃based polycarbonate[J]. China Plastics, 2023, 37(10): 34-39.
样品 编号 | BPA⁃PC 02⁃10 含量 | IcC⁃PC D7340IR 含量 | PMMA CM205 含量 | AO300 含量 | M732 含量 | M577 含量 | AX8900 含量 | PTW 含量 | SAG⁃02 含量 | 加工助剂 含量 |
---|---|---|---|---|---|---|---|---|---|---|
1# | - | 100 | - | - | - | - | - | - | - | 0.5 |
2# | 100 | - | - | - | - | - | - | - | - | 0.5 |
3# | - | 50 | 50 | - | - | - | - | - | - | 0.5 |
4# | 50 | 50 | - | - | - | - | - | - | - | 0.5 |
5# | 50 | 50 | - | 3 | - | - | - | - | - | 0.5 |
6# | 50 | 50 | - | 6 | - | - | - | - | - | 0.5 |
7# | 50 | 50 | - | 9 | - | - | - | - | - | 0.5 |
8# | 50 | 50 | - | 6 | 2 | - | - | - | - | 0.5 |
9# | 50 | 50 | - | 6 | 4 | - | - | - | - | 0.5 |
10# | 50 | 50 | - | 6 | 6 | - | - | - | - | 0.5 |
11# | 50 | 50 | - | 6 | - | 2 | - | - | - | 0.5 |
12# | 50 | 50 | - | 6 | - | 4 | - | - | - | 0.5 |
13# | 50 | 50 | - | 6 | - | 6 | - | - | - | 0.5 |
14# | 50 | 50 | - | 6 | - | 4 | 2 | - | - | 0.5 |
15# | 50 | 50 | - | 6 | - | 4 | - | 2 | - | 0.5 |
16# | 50 | 50 | - | 6 | - | 4 | - | - | 2 | 0.5 |
样品 编号 | BPA⁃PC 02⁃10 含量 | IcC⁃PC D7340IR 含量 | PMMA CM205 含量 | AO300 含量 | M732 含量 | M577 含量 | AX8900 含量 | PTW 含量 | SAG⁃02 含量 | 加工助剂 含量 |
---|---|---|---|---|---|---|---|---|---|---|
1# | - | 100 | - | - | - | - | - | - | - | 0.5 |
2# | 100 | - | - | - | - | - | - | - | - | 0.5 |
3# | - | 50 | 50 | - | - | - | - | - | - | 0.5 |
4# | 50 | 50 | - | - | - | - | - | - | - | 0.5 |
5# | 50 | 50 | - | 3 | - | - | - | - | - | 0.5 |
6# | 50 | 50 | - | 6 | - | - | - | - | - | 0.5 |
7# | 50 | 50 | - | 9 | - | - | - | - | - | 0.5 |
8# | 50 | 50 | - | 6 | 2 | - | - | - | - | 0.5 |
9# | 50 | 50 | - | 6 | 4 | - | - | - | - | 0.5 |
10# | 50 | 50 | - | 6 | 6 | - | - | - | - | 0.5 |
11# | 50 | 50 | - | 6 | - | 2 | - | - | - | 0.5 |
12# | 50 | 50 | - | 6 | - | 4 | - | - | - | 0.5 |
13# | 50 | 50 | - | 6 | - | 6 | - | - | - | 0.5 |
14# | 50 | 50 | - | 6 | - | 4 | 2 | - | - | 0.5 |
15# | 50 | 50 | - | 6 | - | 4 | - | 2 | - | 0.5 |
16# | 50 | 50 | - | 6 | - | 4 | - | - | 2 | 0.5 |
样品编号 | AO300 含量/份 | IcC⁃PC 的Tg/℃ | BPA⁃PC 的Tg/℃ | 透光率/% |
---|---|---|---|---|
1# | 0 | 117.92 | - | 91.49 |
2# | 0 | - | 153.47 | 90.35 |
4# | 0 | 124.49 | 149.73 | 11.07 |
5# | 3 | 126.59 | 145.06 | 28.29 |
6# | 6 | 129.59 | 142.46 | 42.44 |
7# | 9 | 132.26 | 137.69 | 82.51 |
样品编号 | AO300 含量/份 | IcC⁃PC 的Tg/℃ | BPA⁃PC 的Tg/℃ | 透光率/% |
---|---|---|---|---|
1# | 0 | 117.92 | - | 91.49 |
2# | 0 | - | 153.47 | 90.35 |
4# | 0 | 124.49 | 149.73 | 11.07 |
5# | 3 | 126.59 | 145.06 | 28.29 |
6# | 6 | 129.59 | 142.46 | 42.44 |
7# | 9 | 132.26 | 137.69 | 82.51 |
样品 编号 | 相容剂 种类 | 260 ℃、5 kg下的熔体流动速率/ g·(10 min)-1 | 拉伸强度/ MPa | 断裂 伸长率/% | 弯曲强度/ MPa | 弯曲模量/ MPa | 1.80 MPa下的热变形 温度/℃ | 0.45 MPa 下的热变形 温度/℃ | 国标缺口 冲击强度/ kJ·m-2 | 美标缺口 冲击强度/ J·m-1 |
---|---|---|---|---|---|---|---|---|---|---|
12# | - | 36.7 | 64.46 | 103.2 | 102.4 | 2675 | 106.8 | 124.2 | 22.1 | 795 |
14# | AX8900 | 32.2 | 59.17 | 109.5 | 95.1 | 2534 | 110.0 | 126.1 | 64.94 | 956 |
15# | PTW | 34.0 | 61.45 | 106.7 | 95.7 | 2470 | 111.1 | 127.8 | 60.28 | 896 |
16# | SAG⁃02 | 35.5 | 62.84 | 108.6 | 100.4 | 2615 | 109.3 | 124.9 | 49.36 | 834 |
样品 编号 | 相容剂 种类 | 260 ℃、5 kg下的熔体流动速率/ g·(10 min)-1 | 拉伸强度/ MPa | 断裂 伸长率/% | 弯曲强度/ MPa | 弯曲模量/ MPa | 1.80 MPa下的热变形 温度/℃ | 0.45 MPa 下的热变形 温度/℃ | 国标缺口 冲击强度/ kJ·m-2 | 美标缺口 冲击强度/ J·m-1 |
---|---|---|---|---|---|---|---|---|---|---|
12# | - | 36.7 | 64.46 | 103.2 | 102.4 | 2675 | 106.8 | 124.2 | 22.1 | 795 |
14# | AX8900 | 32.2 | 59.17 | 109.5 | 95.1 | 2534 | 110.0 | 126.1 | 64.94 | 956 |
15# | PTW | 34.0 | 61.45 | 106.7 | 95.7 | 2470 | 111.1 | 127.8 | 60.28 | 896 |
16# | SAG⁃02 | 35.5 | 62.84 | 108.6 | 100.4 | 2615 | 109.3 | 124.9 | 49.36 | 834 |
1 | Miyashita M, Yamaguchi M. Effect of water absorption on the structure and properties of isosorbide⁃based polycarbonate[J]. Polymer, 2020, 202: 122 713⁃122 721. |
2 | 冯俊, 李进, 冯健, 等. 生物基异山梨醇聚碳酸酯的合成和性能[J]. 工程塑料应用, 2022, 50(10): 16⁃20. |
FENG J, LI J, FENG J, et al. Preparation and performance of isosorbide⁃based polycarbonate[J]. Engineering Plastics Application, 2022, 50(10): 16⁃20. | |
3 | Ma C, Xu F, Cheng W, et al. Tailoring molecular weight of bioderived polycarbonates via bifunctional ionic liquids catalysts under metal⁃free conditional[J]. ACS Sustainable Chemistry & Engineering, 2018, 6(2): 2 684⁃2 693. |
4 | 张芳芳, 孙树林, 曹春雷, 等. 核壳结构改性剂对PBT/PC共混物冲击强度的影响[J]. 中国塑料, 2007, 21(10): 31⁃35. |
ZHANG F F, SUN S L, CAO C L, et al. Effect of core⁃shell modifiers on the impact strength of PBT/PC blends[J]. China Plasitics, 2007, 21(10): 31⁃35. | |
5 | 韩 丹, 黄 云, 刘 波, 等. 再生PC的表面耐磨改性研究[J]. 中国塑料, 2023, 37(3): 30⁃34. |
HAN D, HUANG Y, LIU B, et al. Study on modification of surface resistance for regenerated transparent polycarbonate[J]. China Plasitics, 2023, 37(3): 30⁃34. | |
6 | 何 洋, 李洋洋, 邵景昌, 等. PC制件内应力表征及内应力开裂因素与改善措施分析[J]. 中国塑料, 2019, 33(7): 63⁃68. |
HE Y, LI Y Y, SHAO J C, et al. Characterization, analysis and improvement of internal stress cracks of PC[J]. China Plasitics, 2019, 33(7): 63⁃68. | |
7 | 陈宇宏, 詹茂盛. 压缩工艺参数对注射压缩成型聚碳酸酯透明件残余应力的影响[J]. 中国塑料, 2021, 35(12): 9⁃15. |
CHEN Y H, ZHAN M S. Effect of compression process parameters on residual of injection⁃compression⁃molded polycarbonate transparencies[J]. China Plasitics,2021, 35(12): 9⁃15. | |
8 | 赵 颖, 刘树文, 张晓略, 等. 外饰免喷涂高光钢琴黑材料的特点及应用[J]. 上海汽车, 2018(3): 51⁃55. |
ZHAO Y, LIU S W, ZHANG X L, et al. The characteristics and application of non spray high gloss piano black material for exterior decoration[J]. Shanghai Auto, 2018(3): 51⁃55. | |
9 | LI C, LONG X, WANG Q Y, et al. Studies on synthesis and optical properties of poly(isosorbide⁃co-1,4⁃cyclohexanedimethanol) carbonate[J]. Journal of Polymer Research, 2022, 29(10): 1⁃9. |
10 | 牛振威, 何 嵘, 竹文坤, 等. 聚甲基丙烯酸甲酯和聚碳酸酯各向异性光学性质理论研究[J]. 原子与分子物理学报, 2023, 40(1): 9⁃20. |
NIU Z W, HE R, ZHU W K, et al. Theoretical calculation of the anisotropic optical properties of poly⁃methyl methacrylate and polycarbonate[J]. Journal of Atomic and Molecular Physics, 2023, 40(1): 9⁃20. | |
11 | SU L L, LAI W Q, YAN J, et al. Small⁃molecule⁃induced miscibility of isosorbide⁃based polycarbonate with bisphenol a polycarbonate[J]. Journal of Applied Polymer science, 2017, 134(9): 44 537⁃44 546. |
12 | 应 杰, 邱琪浩, 张豪杰, 等.不同类型增韧剂对聚碳酸酯性能的影响[J]. 中国塑料, 2020, 34(7): 30⁃35. |
YING J, QIU Q H, ZHANG H J, et al. Effects of different types of toughening agent on properties of polycarbonate[J]. China Plasitics, 2020, 34(7): 30⁃35. | |
13 | 莫文杰, 龚德君, 陈 锐, 等. PC增韧PBT的性能和结构研究[J]. 广州化工, 2019, 47(9): 58⁃60. |
MO W J, GONG D J, CHEN R, et al. Study on property and structure of PBT toughened with PC[J]. Guangzhou Chemical Industry, 2019, 47(9): 58⁃60. |
Viewed | ||||||||||||||||||||||||||||||||||||||||||||||||||
Full text 554
|
|
|||||||||||||||||||||||||||||||||||||||||||||||||
Abstract 423
|
|
|||||||||||||||||||||||||||||||||||||||||||||||||