Research and application progress of epoxy resin sealant used in highway engineering

doi:10.19491/j.issn.1001-9278.2025.01.011

Abstract

Abstract:

This paper summarized the research progress of epoxy resin materials used as road sealants， introduced the constituent materials and preparation processes of road epoxy resin sealants， analyzed the performance research and modification mechanism of road epoxy resin sealants， and investigated the application of epoxy resin sealants in the field of highway engineering. Finally， the existing problems and deficiencies in the research and application of epoxy resin sealant for road were put forward， and the development prospect was prospected， so as to provide the basis for the further research and promotion of epoxy resin sealant.

Key words: epoxy resin sealant, constituent materials, properties, application, highway engineering

CLC Number:

TQ323.5

JI Jiajun, ZHANG Zengping, LI Junhui, SHI En, LI Qingxu. Research and application progress of epoxy resin sealant used in highway engineering[J]. China Plastics, 2025, 39(1): 63-74.

Figures/Tables 18

References 78

1	Elseifi A M， Ozer H. Cracking in flexible pavements and asphalt mixtures： theories， modeling and testing for mitigation［J］. International Journal of Pavement Engineering， 2018， 19（3）： 191⁃191.
2	薛爱新，王洁光，王海军，等. 高速公路沥青路面裂缝发展对路面结构性能的影响研究［J］. 中外公路， 2019， 39（3）： 59⁃63.
3	Chen Qiqi， Wang Guanhu. Research on relationships among different disease types of cement concrete pavement based on structural equation model［J］. Mathematical Problems in Engineering， 2020， 2020： 9580616.
4	Wang Huaping， Guo Yanxin， Wu Mengyi， et al. Review on structural damage rehabilitation and performance assessment of asphalt pavements［J］. Reviews on Advanced Materials Science， 2021， 60（1）： 438⁃449.
5	刘曼毓. 沥青路面裂缝修补技术研究［D］. 南京：东南大学， 2021.
6	Mazumder M， Kim H H， Lee S， et al. Crack treatment performance on pavement marking， joint and shoulder lanes in Texas［J］. Innovative Infrastructure Solutions， 2019， 4（1）： 16.
7	Smith K L， Romine A R. FHWA⁃RD-99⁃147 materials and procedures for sealing and filling cracks in asphalt⁃surfaced pavements［R］. McLean， Virginia： FHWA， U.S. Department of Transportation， 1999.
8	况栋梁，赵喆，吴永畅，等. 环氧树脂在道路工程中的应用研究进展［J］. 长安大学学报（自然科学版）， 2024， 44（3）： 1⁃19.
	KUANG D L， ZHAO Z， WU Y C， et al. Research progress of epoxy resin in road engineering［J］. Journal of Chang'An University：Natural Science Edition， 2024， 44（3）： 1⁃19.
9	成元海，杨渭，李蕾，等. 路用环氧沥青材料研究进展［J］. 橡塑技术与装备， 2023， 49（2）： 1⁃5.
10	魏涛，汪在芹，薛希亮，等. CW系化学灌浆材料的研制［J］. 长江科学院院报， 2000（6）： 29⁃31.
11	魏涛，董建军. 环氧树脂在水工建筑物上的应用［M］. 北京：化学工业出版社， 2007：42⁃46.
12	敖运亨，王文鹃，邵光盛. 钢筋混凝土梁桥的黏接加固及胶料的选配［J］. 黏接， 1985（5）： 29⁃34.
13	毛杰. 机场混凝土道面快速修复的两种工艺［J］. 中国民航飞行学院学报， 2000（1）： 46⁃47.
14	鲍旭初，周红锋，李承昌. 环氧树脂灌缝胶的固化特性及对施工工艺的影响［J］. 山东交通科技， 2004，（4）： 37⁃38+48.
15	黄志为，刘少宏，陈子军. 水泥混凝土路面养护修补的实践［J］. 广东公路交通， 1995（1）： 1⁃6.
16	郝鹏举，伍思豫，向豪，等. 环氧树脂在公路工程中的应用研究综述［J］. 青海交通科技， 2023， 35（1）： 48⁃54.
	HAO P J， WU S Y， XIANG H， et al. A review of the application of epoxy resin in highway engineering［J］. Qinghai Transportation Science and Technology， 2023， 35（1）： 48⁃54.
17	于国玲，陈宛瑶，雷东岭，等. 环氧固化剂的最新研究进展［J］. 中国涂料， 2020， 35（9）： 19⁃22.
	YU G L， CHEN W Y， LEI D L， et al. Latest progress in research on epoxy curing agents［J］. CHINA Coatings， 2020， 35（9）： 19⁃22.
18	王壹，田林波，叶晓兰，等. 短链有机硅环氧的制备及其对双酚A型环氧树脂的增韧改性研究［J］. 塑料科技， 2022， 50（2）： 14⁃18.
	WANG Y， TIAN L B， YE X L， et al. Study on preparation of short chain organosilicon epoxy monomer and its application on toughening modification of bisphenol a type epoxy resin［J］. Plastics Science and Technology， 2022， 50（2）： 14⁃18.
19	Mi Xiaoqian， Liang Nuo， Xu Haifeng， et al. Toughness and its mechanisms in epoxy resins［J］. Progress in Materials Science， 2022， 130： 100977.
20	Wang Linbing，庞鑫，叶周景. 活性稀释剂对环氧树脂基的影响［J］. 北京工业大学学报， 2023， 49（2）： 235⁃244.
	WANG L B， PANG X， YE Z J. Effect of reactive diluent on epoxy resin for self⁃healing［J］. Journal of Beijing University of Technology， 2023， 49（2）： 235⁃244.
21	张敏鑫，杜俊涛，王振中，等. 活性稀释剂对冷拌环氧沥青性能的影响研究［J］. 公路， 2023， 68（11）： 46⁃50.
22	李志林，陈炳耀，彭小琴，等. 偶联剂对环氧树脂力学性能的影响研究［J］. 化学与黏合， 2021， 43（4）： 276⁃278.
	LI Z L， CHEN B Y， PENG X Q， et al. The effect of coupling agent on the mechanical properties of epoxy resin［J］. Chemistry and Adhesion， 2021， 43（4）： 276⁃278.
23	张宇娜，匡怡，郑益. 硅烷偶联剂对桥面铺装环氧树脂胶黏剂黏结性能的影响研究［J］. 中国水运（下半月）， 2021， 21（1）： 95⁃96.
24	李永生，曹大富. 高温施工环境下环氧树脂建筑结构胶缓凝性能研究［J］. 中国胶黏剂， 2021， 30（6）： 51⁃55.
25	张玉龙. 环氧胶黏剂［M］. 北京：化学工业出版社， 2017：22⁃25.
26	陈平，刘胜平，王德中. 环氧树脂及其应用［M］. 北京：化学工业出版社， 2017：176⁃179.
27	俞滨滨，刘波，张爱萍，等. 双组分高强高韧环氧树脂胶黏剂的研制［J］. 中国胶黏剂， 2023， 32（9）： 39⁃43.
28	Liu Shuang， Mo Liantong， Wang Kai， et al. Preparation， microstructure and rheological properties of asphalt sealants for bridge expansion joints［J］. Construction and Building Materials， 2016， 105： 1⁃13.
29	Šušteršič J， Zajc A， Korla J， et al. Efficient repair of crack in SFRC with low⁃viscosity epoxy adhesive［J］. Advanced Materials Research， 2015， 1129： 453⁃459.
30	He Chengping， Wu Zhigang， Huang Yu， et al. Epoxy⁃resin adhesive for seam filling and pothole repair in pavement maintenance［J］. Materials and technology， 2022， 56（6）： 661⁃667.
31	Yin Jian， Pang Qiling， Wu Hao， et al. Using a polymer⁃based sealant material to make crack repair of asphalt pavement［J］. Journal of Testing and Evaluation， 2018， 46（5）： 2 056⁃2 066.
32	Li Feng， Zhou Siqi， Cai Wenyuan， et al. Laboratory evaluation of short and long term performance of hot⁃poured sealants［J］. Construction and Building Materials， 2017， 148： 30⁃37.
33	Lu Lu， Zhao Deying， Fan Jizhou， et al. A brief review of sealants for cement concrete pavement joints and cracks［J］. Road Materials and Pavement Design， 2022， 23（7）： 1 467⁃1 491.
34	彭华，尹健，池漪，等. 沥青路面裂缝修补材料性能评价指标及方法［J］. 铁道科学与工程学报， 2014， 11（4）： 90⁃95.
	PENG H， YIN J， CHI Y， et al. Indexes and methods for evaluating the performance of crack repair material used in asphalt pavement［J］. Journal of Railway Science and Engineering， 2014， 11（4）： 90⁃95.
35	Ma Biao， Hu Yongping， Liu Fangshu， et al. Performance of a novel epoxy crack sealant for asphalt pavements［J］. International Journal of Pavement Engineering， 2022， 23（9）： 3 068⁃3 081.
36	Shen Dongya， Shi Shuang， Xu Tao. Synthesis and performance evaluation of epoxy resin⁃modified shape memory polyurethane sealant［J］. Journal of Testing and Evaluation， 2018， 46（4）： 1 452⁃1 461.
37	Ba Huaiqiang， Guo Luxin， Huan Haiyang， et al. Multi⁃objective optimization of epoxy resin adhesive for pavement toughened by self⁃made toughening agent［J］. Polymers， 2023， 15（8）： 1 946.
38	Liu Qian， Yang Min， Jing Hongjun， et al. Preparation and performance of cementing materials for rapid maintenance of pavement potholes［J］. DYNA， 2022， 98（4）： 426⁃432.
39	余航. 沥青路面环氧灌缝材料试验研究［D］. 长沙：长沙理工大学， 2019.
40	Wang Xiaoqing， Ma Biao， Su Wenbin， et al. Design and laboratory performance of reactive cold patching materials containing epoxy/unsaturated polyester blends［J］. Construction and Building Materials， 2023， 377： 131152.
41	Fang Yunfeng， Ma Biao， Wei Kun， et al. Performance of single⁃component epoxy resin for crack repair of asphalt pavement［J］. Construction and Building Materials， 2021， 304： 124625.
42	Tian Tian， Jiang Yingjun， Fan Jiangtao， et al. Development and performance evaluation of a high⁃permeability and high⁃bonding fog⁃sealing adhesive material［J］. Materials（Basel）， 2021， 14（13）： 3 599.
43	Li Xuelian， Ye Junhong， Zhou Zihan， et al. Preparation and performance of an asphalt pavement sealant with waterborne epoxy resin［J］. Construction and Building Materials， 2022， 350： 128827.
44	Xu Jiayun， Ma Biao， Liu Fangshu， et al. Study of the bonding performance and application of an epoxy resin pavement sealant［J］. Journal of Materials in Civil Engineering， 2023， 35（7）： 04023183.
45	Xiang Qian， Xiao Feipeng. Applications of epoxy materials in pavement engineering［J］. Construction and Building Materials， 2020， 235： 117529.
46	刘世乡，胥泽奇，赵方超，等. 环氧树脂材料的老化及防老化研究进展［J］. 装备环境工程， 2023， 20（1）： 127⁃134.
	LIU S X， XU Z Q， ZHAO F C， et al. Research progress on aging and anti⁃aging of epoxy resin materials［J］. Equipment environmental engineering， 2023， 20（01）： 127⁃134.
47	YOUNG T. An essay on the cohesion of fluids［J］. Philosophical Transactions of the Royal Society B， 1805， 95： 65⁃87.
48	FOWKES F M. Attractive forces at interfaces［J］. Journal of Industrial and Engineering Chemistry， 1964， 56（12）： 40⁃52.
49	Wu Shuyin， Liu Quan， Yang Jun， et al. Study of adhesion between crack sealant and pavement combining surface free energy measurement with molecular dynamics simulation［J］. Construction and Building Materials， 2020， 240： 117900.
50	安亚强，徐洁. 环氧树脂结构胶的特性与建筑加固应用技术［J］. 黏接， 2023， 50（9）： 11⁃14.
	AN Y Q， XU J. Characteristics of epoxy structural adhesives and application techniques for building reinforcement［J］. Adhesion， 2023， 50（9）： 11⁃14.
51	路面加热型密封胶：［S］. 北京：人民交通出版社， 2015.
52	混凝土裂缝用环氧树脂灌浆材料：［S］. 北京：中国建材工业出版社， 2007.
53	道桥嵌缝用密封胶：［S］. 北京：中国建材工业出版社， 2005.
54	混凝土裂缝修复灌浆树脂：［S］. 北京：中国建筑工业出版社， 2010.
55	Standard Specification for Epoxy Resin Adhesives：［S］. Washington， DC： American Association of State Highway and Transportation Officials， 2013.
56	树脂浇铸体性能试验方法：［S］. 北京：中国标准出版社， 2021.
57	胶黏剂黏度的测定：［S］. 北京：中国标准出版社， 1995.
58	公路工程沥青及沥青混合料试验规程：［S］. 北京：人民交通出版社， 2011.
59	公路工程水泥及水泥混凝土试验规程：［S］. 北京：人民交通出版社， 2020
60	Schoberleitner C， Archodoulaki V， Koch T， et al. Developing a sealing material： effect of epoxy modification on specific physical and mechanical properties［J］. Materials， 2013， 6（12）： 5 490⁃5 501.
61	曾柳惠，曹有名，何伟光. 有机硅改性聚氨酯/环氧树脂胶黏剂的性能研究［J］. 材料研究与应用， 2022， 16（3）： 438⁃441.
	ZENG L H， CAO Y M， HE W G. Properties of polyurethane/epoxy resin adhesives modified by organosilicon［J］. Materials Research and Application， 2022， 16（3）： 438⁃441.
62	刘虓嵩，张增平，郭茵霄，等. 用于公路工程的聚氨酯密封胶研究进展［J］. 中国胶黏剂， 2023， 32（9）： 49⁃57.
63	张大丽，刘宗旺，邹家桂，等. 耐湿热柔性聚氨酯改性环氧灌封胶的制备及性能研究［J］. 绝缘材料， 2020， 53（9）： 19⁃23.
	ZHANG D L， LIU Z W， ZOU J G， et al. Preparation and properties of epoxy pouring sealant modified by humidity and heat resistant flexible polyurethane［J］. Insulating Materials， 2020， 53（9）： 19⁃23.
64	Long Jiejie， Li Chuanxi， Li You. Enhancement of mechanical and bond properties of epoxy adhesives modified by SiO₂ nanoparticles with active groups［J］. Polymers， 2022， 14（10）： 2 052⁃2 052.
65	蔡雄睿，梅婷，冉娅，等.环氧灌浆材料研究进展［J］.功能材料，2024，55（5）：5 047⁃5 056.
66	Zhang Yingtuan， Pang Hao， Wei Daidong， et al. Preparation and characterization of chemical grouting derived from lignin epoxy resin［J］. European Polymer Journal， 2019， 118： 290⁃305.
67	Wang Shaoquan， Xu Yanliang， Liu Manyu， et al. Dynamic behavior of crack sealant bonding interface in the asphalt pavement crack repair structure under moving vehicle load［J］. Case Studies in Construction Materials， 2023， 18： e01821.
68	方云峰. 单组分环氧树脂路面灌缝胶制备与性能研究［D］. 西安：长安大学， 2022.
69	Wu Hao， Zhu Meijia， Liu Zhuo， et al. Developing a polymer⁃based crack repairing material using interpenetrate polymer network （IPN） technology［J］. Construction and Building Materials， 2015， 45（7）： 192⁃200.
70	Wang Wenzhao， Zhao Weiquan， Zhang Jinjie， et al. Epoxy⁃based grouting materials with super⁃low viscosities and improved toughness［J］. Construction and Building Materials， 2020， 267： 121104.
71	Wang Chaohui， Zhang Dan， Chen Haoyu， et al. Preparation and Properties of Silicon⁃Modified Epoxy Grouting Material for Repairing Microcracks［J］. Journal of Materials in Civil Engineering， 2022， 34（3）： 04021479.
72	Wang Chaohui， Fan Zhentong， Li Changhui， et al. Preparation and engineering properties of low⁃viscosity epoxy grouting materials modified with silicone for microcrack repair［J］. Construction and Building Materials， 2021， 290： 123270.
73	刘爽，李俊叶. 环氧树脂胶黏剂在道路新旧混凝土黏接中的应用［J］. 中国胶黏剂， 2021， 30（11）： 41⁃45.
74	Modesti A L， Vargas D S A， Schneider L E. Repairing concrete with epoxy adhesives［J］. International Journal of Adhesion and Adhesives， 2020， 101： 102645.
75	唐传辉. 环氧树脂基桥梁伸缩缝快速修复材料的研究与应用［D］. 重庆：重庆交通大学， 2021.
76	Pang Bo， Jin Zuquan， Zhang Yunsheng， et al. Ultraductile waterborne epoxy⁃concrete composite repair material： Epoxy⁃fiber synergistic effect on flexural and tensile performance［J］. Cement and Concrete Composites， 2022， 129： 104463.
77	Chen Wei， Zheng Yuanbiao， Tang Chuanhui， et al. Fatigue performance of epoxy⁃based concrete for bridge expansion joint rapid repair and the repaired concrete members［J］. Ceramics⁃Silikáty， 2021， 65（4）： 326⁃333.
78	Lin Bin. Synthesis of a flame retardant and hydrophobic epoxy resin with multiple elements synergistic effect for tunnel seepage prevention application［J］. Key Engineering Materials， 2020， 842： 314⁃325.

研究者	材料自身性能研究	路用性能研究
Ma等^［35］	黏度、拉伸性能、压缩强度	渗透性能、黏结性能、水稳定性、低温抗裂性、耐老化性
Shen等^［36］	热稳定性、动态力学性能、形状记忆性能、拉伸性能	-
Ba等^［37］	黏度、拉伸性能	-
Liu等^［38］	黏度、拉伸性能、热稳定性、弹性恢复率	-
余航^［39］	黏度、拉伸性能	渗透性能、黏结性能、耐疲劳性
Wang等^［40］	黏度、拉伸性能、固化收缩率	压缩性能、抗弯拉性能、高温稳定性、低温抗裂性、水稳定性
Fang等^［41］	黏度、拉伸性能、热稳定性、弹性恢复率	低温抗裂性、黏结性能
Tian等^［42］	黏度	渗透性能、黏结性能、耐老化性、水稳定性
Li等^［43］	黏度、固化时间、剪切强度	黏结性能、耐老化性、水稳定性
Xu等^［44］	黏度、固化收缩率、拉伸性能	渗透性能、黏结性能

研究者	材料自身性能研究	路用性能研究
Ma等^［35］	黏度、拉伸性能、压缩强度	渗透性能、黏结性能、水稳定性、低温抗裂性、耐老化性
Shen等^［36］	热稳定性、动态力学性能、形状记忆性能、拉伸性能	-
Ba等^［37］	黏度、拉伸性能	-
Liu等^［38］	黏度、拉伸性能、热稳定性、弹性恢复率	-
余航^［39］	黏度、拉伸性能	渗透性能、黏结性能、耐疲劳性
Wang等^［40］	黏度、拉伸性能、固化收缩率	压缩性能、抗弯拉性能、高温稳定性、低温抗裂性、水稳定性
Fang等^［41］	黏度、拉伸性能、热稳定性、弹性恢复率	低温抗裂性、黏结性能
Tian等^［42］	黏度	渗透性能、黏结性能、耐老化性、水稳定性
Li等^［43］	黏度、固化时间、剪切强度	黏结性能、耐老化性、水稳定性
Xu等^［44］	黏度、固化收缩率、拉伸性能	渗透性能、黏结性能

性能指标		环氧树脂密封胶类型							参考规范
性能指标		I级				II级			参考规范
压缩强度/MPa		≥40				≥70			JC/T 1041—2007《混凝土裂缝用环氧树脂灌浆材料》^［52］
拉伸剪切强度/MPa		≥5				≥8
拉伸强度/MPa		≥10				≥15
干黏结强度/MPa		≥3				≥4
湿黏结强度/MPa		≥2				≥2.5
抗渗压力/MPa		≥1				≥1.2
渗透压力比/%		≥300				≥400
		常温固化型				低温固化型
黏度（23 ℃）/mPa·s		≤500							JG/T 264—2010《混凝土裂缝修复灌浆树脂》^［54］
适用期（23 ℃）/min		≥30
拉伸强度/MPa		≥20
拉伸弹性模量/MPa		≥1 500
断裂伸长率/%		≥1
压缩强度/MPa		≥40
弯曲强度/MPa		≥30
拉伸剪切强度/MPa		≥10
		Ⅰ	Ⅱ	Ⅲ	Ⅳ	Ⅴ	Ⅵ	Ⅶ
黏度/Pa•s	最小	2	2	2	2	2	-	-	ASTM C881⁃10《Standard Specification for Epoxy Resin Adhesives》^［55］
黏度/Pa•s	最大	10	10	10	10	10	-	-
稠度/mm		6	6	6	6	6	6	6
凝结时间/min		30	30	30	30	30	30	30
黏结强度最小值/MPa	2天	7	-	-	7	-	7	-
黏结强度最小值/MPa	14天	10	10	10	10	10	-	7
热变形温度最小值/℃	7天	-	-	-	50	50	-	-
热变形温度最小值/℃	14天	-	-	-	-	-	50	50
抗压屈服强度最小值/MPa	7天	55	35	⁃	70	55	-	-
压缩模量/MPa	最小	1 000	600	-	1 400	1 000	-	-
压缩模量/MPa	最大	-	-	896	-	-	-	-
拉伸强度/MPa	最小	35	14	-	50	40	-	-
断裂伸长率/%	最小	1	1	30	1	1	-	-

性能指标		环氧树脂密封胶类型							参考规范
性能指标		I级				II级			参考规范
压缩强度/MPa		≥40				≥70			JC/T 1041—2007《混凝土裂缝用环氧树脂灌浆材料》^［52］
拉伸剪切强度/MPa		≥5				≥8
拉伸强度/MPa		≥10				≥15
干黏结强度/MPa		≥3				≥4
湿黏结强度/MPa		≥2				≥2.5
抗渗压力/MPa		≥1				≥1.2
渗透压力比/%		≥300				≥400
		常温固化型				低温固化型
黏度（23 ℃）/mPa·s		≤500							JG/T 264—2010《混凝土裂缝修复灌浆树脂》^［54］
适用期（23 ℃）/min		≥30
拉伸强度/MPa		≥20
拉伸弹性模量/MPa		≥1 500
断裂伸长率/%		≥1
压缩强度/MPa		≥40
弯曲强度/MPa		≥30
拉伸剪切强度/MPa		≥10
		Ⅰ	Ⅱ	Ⅲ	Ⅳ	Ⅴ	Ⅵ	Ⅶ
黏度/Pa•s	最小	2	2	2	2	2	-	-	ASTM C881⁃10《Standard Specification for Epoxy Resin Adhesives》^［55］
黏度/Pa•s	最大	10	10	10	10	10	-	-
稠度/mm		6	6	6	6	6	6	6
凝结时间/min		30	30	30	30	30	30	30
黏结强度最小值/MPa	2天	7	-	-	7	-	7	-
黏结强度最小值/MPa	14天	10	10	10	10	10	-	7
热变形温度最小值/℃	7天	-	-	-	50	50	-	-
热变形温度最小值/℃	14天	-	-	-	-	-	50	50
抗压屈服强度最小值/MPa	7天	55	35	⁃	70	55	-	-
压缩模量/MPa	最小	1 000	600	-	1 400	1 000	-	-
压缩模量/MPa	最大	-	-	896	-	-	-	-
拉伸强度/MPa	最小	35	14	-	50	40	-	-
断裂伸长率/%	最小	1	1	30	1	1	-	-

[1]	. Preparation of soybean oil reactive diluent and its effect on mechanical properties of epoxy resin [J]. , 2025, 39(2): 67-71.
[2]	XU Qiangxiang, ZHANG Guoping, HU Yihong, YANG Fayong, ZHAO Qiongyang, LI Zhigang. Performance and mechanism of desulfurization crumb rubber/SBS⁃modified asphalt [J]. China Plastics, 2025, 39(1): 13-18.
[3]	GUO Sanci, WANG Lei, YUAN Hongyue, YANG Yidan, LIU Xianhu, PAN Yamin. Research progress in radiative cooling materials and their applications [J]. China Plastics, 2025, 39(1): 132-140.
[4]	LI Rongnan, YIN Maoli, LIU Feng, HU Chenggong, XING Jian. Effect of organic⁃inorganic compound antioxidant on structure and properties of polyphenylene sulfide [J]. China Plastics, 2025, 39(1): 75-79.
[5]	WEN Qilin, JIA Xuehua, SUN Yanjun, NIU Siji, CHEN Yinghong, CHEN Ning. Research progress in preparation and applications of biodegradable plastic packaging films [J]. China Plastics, 2024, 38(9): 112-122.
[6]	CUI Bao, YANG Jianjun, WU Qingyun, WU Mingyuan, ZHANG Jianan, LIU Jiuyi. Research Progress in blending modification of polylactic acid composites and their applications [J]. China Plastics, 2024, 38(9): 129-136.
[7]	LIU Shunquan, ZHANG Xinyue, FENG Zhanmiao, FU Chenchao, XUE Ping, ZHANG Run. Research progress in modification techniques and performance optimization of PTFE [J]. China Plastics, 2024, 38(7): 112-119.
[8]	ZHAO Yongfei, ZHANG Wencai, WANG Ke, HAO Xiaogang, SHEN Jun, YANG Xiying, ZHAO Lirong, LI Jianhong, ZHAO Zhixin, QIAO Jie. Research progress in application technology of waste polyethylene⁃modified asphalt [J]. China Plastics, 2024, 38(7): 93-99.
[9]	XIE Bo, TU Zhigang, ZHOU Xianjin, ZHAG Shangxian, XIONG Ligui, YANG Ting. Development of heat shrinkable BOPP packaging film with low friction coefficient [J]. China Plastics, 2024, 38(6): 78-81.
[10]	ZHANG Zheng, LI Fangquan, LI Jie, LI Changjin, GUO Min, WANG Ying. Research progress in polyamide and its applications for medical and sanitary materials [J]. China Plastics, 2024, 38(5): 113-119.
[11]	LI Shuangyan, LU Xinyu, SU Qiong, ZHAO Mengchi, Alidan Ruzha Hong, WANGYupu , ZHAO Libin. Research progress in modification and foaming methods of environmentally friendly biomass materials [J]. China Plastics, 2024, 38(12): 163-171.
[12]	LIU Chenjun, XI Yuyang, REN Wei, YANG Xin, GE Zhenghao, WANG Chaobao. Study on performance of PPS/PA66/GF/HGM quaternary composites [J]. China Plastics, 2024, 38(12): 43-47.
[13]	. Study on the properties of HGM/GF/PA66/PPS quaternary composites [J]. , 2024, (12): 0-0.
[14]	. Research Progress on Modification and Foaming Methods of Environmentally Friendly Biomass Materials [J]. , 2024, (12): 0-0.
[15]	. The Preparation of Hydrolyzable Crystalline Poly (glycolic acid) with Poly (epoxypropoxy) silsesquioxane [J]. , 2024, (11): 0-0.