Research on Processing Conditions of PVF Films by Solution Casting

doi:10.19491/j.issn.1001-9278.2014.01.014

China Plastics ›› 2014, Vol. 28 ›› Issue (01): 70-73 .DOI: 10.19491/j.issn.1001-9278.2014.01.014

Research on Processing Conditions of PVF Films by Solution Casting

Received:2013-06-18 Revised:2014-04-18 Online:2014-01-26 Published:2014-01-26

Abstract

Abstract: PVF films containing different plasticizers and cosolvent were prepared by solution casting. The effects of processing parameters on the structure and properties of the films were investigated. The results showed PVF could be dissolved in DMF. The crystal structures of PVF films were destroyed, resulting in improved elongation at break and decreased tensile stress. DOP was a good plasticizer for PVF. The PVF films with good mechanical properties could be obtained with the concentration of PVF solution 3 % at 85 ℃ and 100 r/min stirring speed in the presence of deforming agent.

Key words: film, processing condition, poly(vinyl fluoride), solution casting

. Research on Processing Conditions of PVF Films by Solution Casting[J]. China Plastics, 2014, 28(01): 70-73 .

[1]	DONG Yue, DONG Xiao, ZHU Dezhao, YANG Yanxiang, LUO Chen, LI Yang, LI Jinshan. An overview of development and application prospects of polyimide products [J]. China Plastics, 2022, 36(9): 85-95.
[2]	YANG Chaoyong, GUO Jinqiang, WANG Fuyu, ZHNAG Yuxia. Research progress in preparation and modification methods of high-performance plastic films [J]. China Plastics, 2022, 36(9): 167-179.
[3]	XIONG Yiming, SONG Jiling, QIN Shuhao, LONG Xuebin, LU Xianrui. Preparation of modified thermoplastic starch and properties of its composite films with PBAT [J]. China Plastics, 2022, 36(8): 69-72.
[4]	ZHANG Xin, QUAN Shumiao. Study on current status of recycling and reutilization of waste agricultural films based on China’s policy [J]. China Plastics, 2022, 36(7): 136-142.
[5]	LI Guo, ZHU Huihao, MA Yulu, WANG Yu, JI Huajian, XIE Linsheng. Preparation and properties of microporous breathable films with high thermal conductivity [J]. China Plastics, 2022, 36(7): 14-20.
[6]	ZHU Jingyun, YI Huijun, YAN Wei, LI Dawei. Research and development of polyethylene special materials for compound films [J]. China Plastics, 2022, 36(6): 77-80.
[7]	WEI Maoqiang. Development and discussion of agricultural plastic film [J]. China Plastics, 2022, 36(6): 92-99.
[8]	ZHANG Zongyin, LYU Mingfu, GUO Peng, XU Yaohui, ZHANG Shijun. Influence of ultraviolet absorbers on weather resistance of PBST film [J]. China Plastics, 2022, 36(5): 110-115.
[9]	SUI Zhenquan, MAO Jinchao, FAN Jinshi. Preparation and applications of chitosan/poly（vinyl alcohol） liquid mulch films [J]. China Plastics, 2022, 36(3): 21-25.
[10]	LU Chunyan, WANG Gang, LIU Shuai, ZHU Tianrong, LIU Yun, WANG Haiping, HU Siqian. Preparation of high⁃transparency polyimide film by high⁃temperature polycondensation method [J]. China Plastics, 2022, 36(3): 48-52.
[11]	LI Rui, JIANG Yanfeng, WU Shuang, AN Yanjie, JIANG Zeyu, ZHANG Mingqiang. Microstructure and thermal characterization of polypropylene special material for cast films through temperature rising elution fractionation [J]. China Plastics, 2022, 36(3): 53-57.
[12]	XIE Yu, WANG Limei, QI Bin. Preparation and properties of crosslinked chitosan/montmorillonite composite films [J]. China Plastics, 2022, 36(3): 58-63.
[13]	CAO Zhifeng, ZHAO Lipin, HE Ting, MA Baijun. Preparation and properties of five⁃layer co⁃extrusion barrier films [J]. China Plastics, 2022, 36(3): 64-68.
[14]	DONG Jingwei, YAN Haiyan, WANG Yi, ZHANG Bo, CHEN Shujuan, LI Minhao, ZHANG Yue. Assembly of polyaniline crystalline film by interface induction and its gas response properties [J]. China Plastics, 2022, 36(10): 60-64.
[15]	GUAN Tonghui, FU Ye, WENG Yunxuan. Degradation behaviors of PBAT biodegradable mulch in soil [J]. China Plastics, 2022, 36(1): 67-72.

Research on Processing Conditions of PVF Films by Solution Casting

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments