Preparation of high⁃transparency polyimide film by high⁃temperature polycondensation method

doi:10.19491/j.issn.1001-9278.2022.03.008

Abstract

Abstract:

A series of polyimide （PI） films were synthesized through high?temperature melt polycondensation with different mole ratio of diamine monomer 1，3?bis（4?aminophenoxy）benzene， 2，6?diaminotoluene （2，6?DAT） and dianhydride monomer 4，4'?oxydiphthalic anhydride. The resulting PI products were characterized with infrared spectroscopy， UV?vis spectroscopy， DSC， TGA， and solubility test. The results show that the obtained PI molding powders and films were imidized completely， and the resulant PI films exhibited maximum transmittance of more than 80 %， a maximum glass transition temperature of approximately 290 ℃， and a residual carbon yield of more than 55 wt% at 800 ℃. Almost all molding powders were dissolved completely in normal organic solvents like N，N?dimethylacetamide， N?methylpyrroli?done， N，N?dimethylformamide， and dichloromethane.

Key words: polyimide, high?temperature melt polycondensation, ternary polymerization, molding powder, film

CLC Number:

TQ314.24

LU Chunyan, WANG Gang, LIU Shuai, ZHU Tianrong, LIU Yun, WANG Haiping, HU Siqian. Preparation of high⁃transparency polyimide film by high⁃temperature polycondensation method[J]. China Plastics, 2022, 36(3): 48-52.

Figures/Tables 11

References 19

1	LIU B B， ZHANG B， WANG X M， et al. The preparation and properties of polyimide films modified by octa（aminopropylsilsesquioxane）［J］. Journal of Saudi Chemical Society，2019， 23（7）， 856⁃863.
2	WANG S Q， ZHANG B， LUO X M， et al. Ruling out delamination in bismuth⁃enhanced polyimide electrochemical actuator with tunable active/passive layer thickness［J］. Journal of Materials Chemistry A， 2020， 8，doi：10.1039/C9TA13003A .
3	ARRINGTON C B， MARUTI H， VISWANATH M， et al. Supramolecular salts for additive manufacturing of polyimides［J］. ACS Applied Materials & Interfaces， 13（40）：48 061⁃48 070.
4	杨木泉，张洪峰，厉蕾，等. 耐高温无色透明聚酰亚胺/SiO₂纳米复合薄膜的合成及性能研究［J］. 绝缘材料，2017（10）： 1⁃5，9.
	YANG M Q， ZHANG H F， LI L， et al. Synthesis and properties of colorless and transparent PI/SiO₂ nanocompo⁃site films with high temperature resistance［J］. Insulating Materials， 2017（10）： 1⁃5，9.
5	XIAO X L， QIU X Y， KONG D Y， et al. Optically transparent high temperature shape memory polymers［J］. Soft Matte，2016，12，doi： 10.1039/c5sm02703a .
6	LIAN R H， LEI X F， XIAO Y Y， et al. Synthesis and properties of colorless copolyimides derived from 4，4′⁃diaminodiphenyl ether⁃based diamines with different substituents［J］. Polymer Chemistry， 2021， 12， doi： 10.1039/D1PY00633A .
7	吴琳，郭一丹，刘金刚，等. 脂环族无色透明聚酰亚胺光学薄膜的阻燃化研究进展［J］. 精细与专用化学品，2020，28（12）：5⁃12.
	WU L， GUO Y D， LIU J G，et al. Recent progress on the flame retardancy of colorless and transparent alicyclic polyimide films with high thermal stability［J］. Fine and Specialty Chemicals，2020，28（12）：5⁃12.
8	ABDULHAMID M A， MA X H， GHANEM B S， et al. Synthesis and characterization of organo⁃soluble polyimides derived from alicyclic dianhydrides and a dihydroxyl⁃functionalized spirobisindane diamine［J］. ACS Applied Polymer Materials，2019， 1：63⁃69.
9	SUSA A， BIJLEVELD J， SANTANA M H， et al. Understanding the effect of the dianhydride structure on the properties of semiaromatic polyimides containing a biobased fatty diamine［J］. ACS Sustainable Chemistry & Enginee⁃ring，2018， 6（1）： 668⁃678.
10	王寿柏，吴修明，吴锦明，等.含叔丁基/异丁基二胺的可溶性透明聚酰亚胺的合成与性能［J］. 高等学校化学学报，2021 （9）： 2 944⁃2 952.
	WANG S B， WU X M， WU J M，et al. Synthesis and properties of soluble transparent polyimides containing tert⁃butyl and isobutyl groups［J］. Chemical Journal of Chinese Universities，2021 （9）： 2 944⁃2 952.
11	秦琳，李继定，郑冬菊，等. 新型侧链型聚酰亚胺膜的制备及其渗透汽化分离性能［J］. 化工学报，2013（2）： 590⁃599.
	QIN L， LI J D， ZHENG D J， et al. Synthesis of novel membranes of polyimide with side⁃chains and their pervaporation performance［J］. CIESC Journal，2013（2）： 590⁃599.
12	陈琳，鲁云华，李琳，等. 热交联型共聚聚酰亚胺薄膜的制备及性能研究［J］. 绝缘材料，2019（3）： 12⁃17.
	CHEN L， LU Y H， LI L， et al. Preparation and properties of thermal crosslinking copolymerized polyimide films［J］. Insulating Materials，2019（3）： 12⁃17.
13	蒋彩荣，汪称意，余彬，等. 一类含双叔丁基苯结构聚酰亚胺的合成与性能［J］. 高分子材料科学与工程，2021， 7（5）： 26⁃33.
	JIANG C R， WANG C Y， YU B， et al. Synthesis and properties of polyimides containing di⁃tert⁃butylbenzene［J］. Polymer Materials Science & Engineering，2021， 7（5）： 26⁃33.
14	吴琦. 含侧基的高耐热可溶透明聚酰亚胺的合成及性能研究［D］.上海：上海交通大学，2020.
15	姜海健，苏桂明，方雪，等. 相转移一步法制备聚酰亚胺模塑粉的工艺及性能表征［J］. 化学工程师，2020 （4）：12⁃15.
	JIANG H J， SU G M， FANG X， et al. Technology and performance characterization of polyimide molding powder prepared by one step phase transfer method ［J］. Chemical Engineer，2020 （4）：12⁃15.
16	张琪，张弛，钟璟，等. 磺化聚酰亚胺/木质素磺酸钠质子交换复合膜的制备与表征［J］. 化工新型材料 2022，50（1）：99⁃102，107.
	ZHANG Q， ZHANG C， ZHONG J，et al.Preparation and characterization of sulfonated polyimide/sodium lignosulfonate proton exchange composite membrane［J］.New Chemical Materials， 2022， 50（1）： 99⁃102，107.
17	崔柯雯，王轶，刘静.嵌段共聚聚酰亚胺可控制备及性能研究［J］.绝缘材料，2021（11）： 114⁃119.
	CUI K W， WANG Y， LIU J. Controlled preparation and properties of block copolyimide［J］. Insulating Materials，2021（11）： 114⁃119.
18	曹传昊. 基于不同单体的聚酰亚胺薄膜透明性及导热特性研究［D］. 哈尔滨：哈尔滨理工大学，2021.
19	陈营，魏燕红，周红梅，等. TAP⁃ODA⁃BFDA自支撑超支化聚酰亚胺薄膜的制备及性能研究［J］.塑料工业，2021，49（9）：159⁃163.
	CHEN Y， WEI Y H， ZHOU H M， et al. Preparation and properties of self⁃supporting TAP⁃ODA⁃BFDA hyperbranched polyimide films［J］. China Plastics Industry，2021，49（9）：159⁃163.

样品编号	n_2，6⁃DAT：n_TPE⁃R：n_ODPA
PI⁃0	2∶8∶10
PI⁃1	4∶6∶10
PI⁃2	5∶5∶10
PI⁃3	6∶4∶10
PI⁃4	8∶2∶10

样品编号	n_2，6⁃DAT：n_TPE⁃R：n_ODPA
PI⁃0	2∶8∶10
PI⁃1	4∶6∶10
PI⁃2	5∶5∶10
PI⁃3	6∶4∶10
PI⁃4	8∶2∶10

吸收带/cm^-1	来源
3 066、3 085	甲基乙基的振动
1 780、1 781	C=O不对称伸展
1 715、1 716	C=O对称伸展
1 358、1 359	C—N伸展

吸收带/cm^-1	来源
3 066、3 085	甲基乙基的振动
1 780、1 781	C=O不对称伸展
1 715、1 716	C=O对称伸展
1 358、1 359	C—N伸展

PI薄膜编号	膜厚/μm	截止波长/nm	450 nm透过率/%	透过率为80 %时波长/nm	最大透过率/%
PI⁃2	60	364	65.04	641	82.37
PI⁃3	35	364	60.88	739	81.11
PI⁃4	27.5	362	64.06	722	81.56