China Plastics ›› 2021, Vol. 35 ›› Issue (7): 58-62.DOI: 10.19491/j.issn.1001-9278.2021.07.010
• Materials and Properties • Previous Articles Next Articles
Received:
2021-01-18
Online:
2021-07-26
Published:
2021-07-21
CLC Number:
LYU Qiang. Preparation of Glass⁃fiber Reinforced Polyamide 6 with Halogen⁃free Flame Retardant and Permanent Antistatic Performance[J]. China Plastics, 2021, 35(7): 58-62.
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.plaschina.com.cn/EN/10.19491/j.issn.1001-9278.2021.07.010
样品 编号 | PA6?HY800 | GF | 阻燃剂LX?15 | 永久抗静电剂MH?2030 | 其他助剂 |
---|---|---|---|---|---|
1# | 69 | 30 | 0 | — | 1 |
2# | 64 | 30 | 5 | — | 1 |
3# | 59 | 30 | 10 | — | 1 |
4# | 54 | 30 | 15 | — | 1 |
5# | 44 | 30 | 25 | — | 1 |
6# | 64 | 30 | — | 5 | 1 |
7# | 59 | 30 | — | 10 | 1 |
8# | 54 | 30 | — | 15 | 1 |
9# | 49 | 30 | — | 20 | 1 |
10# | 34 | 30 | 15 | 20 | 1 |
11# | 29 | 30 | 20 | 20 | 1 |
12# | 24 | 30 | 25 | 20 | 1 |
样品 编号 | PA6?HY800 | GF | 阻燃剂LX?15 | 永久抗静电剂MH?2030 | 其他助剂 |
---|---|---|---|---|---|
1# | 69 | 30 | 0 | — | 1 |
2# | 64 | 30 | 5 | — | 1 |
3# | 59 | 30 | 10 | — | 1 |
4# | 54 | 30 | 15 | — | 1 |
5# | 44 | 30 | 25 | — | 1 |
6# | 64 | 30 | — | 5 | 1 |
7# | 59 | 30 | — | 10 | 1 |
8# | 54 | 30 | — | 15 | 1 |
9# | 49 | 30 | — | 20 | 1 |
10# | 34 | 30 | 15 | 20 | 1 |
11# | 29 | 30 | 20 | 20 | 1 |
12# | 24 | 30 | 25 | 20 | 1 |
样品编号 | UL 94 | 表面电阻/Ω | ||
---|---|---|---|---|
阻燃等级 | t1/s | t2/s | ||
1# | 无 | 燃至夹具 | — | 4.2×1014 |
2# | 无 | 燃至夹具 | — | 3.9×1014 |
3# | V?1 | 3.3 | 14.5 | 4.3×1014 |
4# | V?0 | 1.3 | 5.5 | 3.8×1014 |
5# | V?0 | 0.6 | 2.2 | 3.9×1014 |
6# | 无 | — | — | 2.3×1013 |
7# | 无 | — | — | 5.4×1011 |
8# | 无 | — | — | 8.6×108 |
9# | 无 | — | — | 1.1×108 |
10# | V?1 | 3.3 | 16.2 | 1.1×108 |
11# | V?1 | 2.7 | 11.3 | 1.2×108 |
12# | V?0 | 2.1 | 5.2 | 1.1×108 |
样品编号 | UL 94 | 表面电阻/Ω | ||
---|---|---|---|---|
阻燃等级 | t1/s | t2/s | ||
1# | 无 | 燃至夹具 | — | 4.2×1014 |
2# | 无 | 燃至夹具 | — | 3.9×1014 |
3# | V?1 | 3.3 | 14.5 | 4.3×1014 |
4# | V?0 | 1.3 | 5.5 | 3.8×1014 |
5# | V?0 | 0.6 | 2.2 | 3.9×1014 |
6# | 无 | — | — | 2.3×1013 |
7# | 无 | — | — | 5.4×1011 |
8# | 无 | — | — | 8.6×108 |
9# | 无 | — | — | 1.1×108 |
10# | V?1 | 3.3 | 16.2 | 1.1×108 |
11# | V?1 | 2.7 | 11.3 | 1.2×108 |
12# | V?0 | 2.1 | 5.2 | 1.1×108 |
1 | 张 强,秦 凡. 连续长玻纤增强PA6复合材料的制备与性能研究[J]. 塑料科技, 2020,34(8):21⁃24. |
ZHANG Q, QIN F. Preparation and Properties of Continuous Long Glass Fiber Reinforced PA6 Composites[J]. Plastics Science and Technology,2020,34(8):21⁃24. | |
2 | 周 进, 何 敏, 刘玉飞,等. 长玻纤增强PA6/OMMT/NMA复合材料的力学性能及热性能[J]. 塑料, 2018,47(3):5⁃8. |
ZHOU J, HE M, LIU Y F, et al. Mechanical Properties and Thermal Properties of PA6/OMMT/NMA Composite Reinforced with Long Glass Fiber[J]. Plastics, 2018,47(3):5⁃8. | |
3 | 孙 鹏, 金 涛, 田 帅,等. 玻璃纤维增强PA6的偶联剂种类优选[J]. 塑料工业, 2014,42(11):80⁃84. |
SUN P, JIN T, TIAN S, et al. Selection of The Coupling Agent Types for Glass Fiber Reinforced PA6[J]. China Plastics Industry, 2014,42(11):80⁃84. | |
4 | 杨 阑. 工程塑料在煤矿中的应用现状与前景[J]. 淮南职业技术学院学报, 2002,2(4):67⁃68. |
YANG L. Present Situation and Prospect of Application of Engineering Plastics in Coal Mine[J].Journal of Huainan Vocational & Technical College, 2002,2(4):67⁃68. | |
5 | 王国超, 廖林清, 邓国红. 特殊环境用通风机玻纤增强尼龙叶轮的研制[J]. 工程塑料应用, 2001,29(11):24⁃25. |
WANG G C, LIAO L Q, DENG G H. Development of The Ventilator Impeller of Glass Fiber Reinforced Using in Special Environment[J]. Engineering Plastics Application, 2001,29(11):24⁃25. | |
6 | 杨 涛, 徐东东, 张 强,等. 抗静电阻燃增强PA6材料的漏电起痕性能研究[J]. 塑料工业, 2013, 41(2):115⁃118. |
YANG T, XU D D, ZHANG Q, et al. Study of CTI of the Antistatic and Flame Retarded PA6 Composite[J]. China Plastics Industry, 2013, 41(2):115⁃118. | |
7 | SCHARTEL B, POTSCHKE P, KNOLL U, et al. Fire Behaviour of Polyamide6/multiwall Carbon Nanotube Nanocomposites[J]. European Polymer Journal, 2005, 41(5): 1 061⁃1 070. |
8 | 左晓玲, 张凯舟, 邵会菊,等. 阻燃型LGF/PA6复合材料的制备及阻燃机理研究[J]. 塑料工业, 2013,41(6):110⁃115. |
ZUO X L, ZHANG K Z, SHAO H J, et al. Preparation and Flame⁃retardant Mechanism of Flame Retarded LGF/PA6 Composites[J]. China Plastics Industry, 2013,41(6):110⁃115. | |
9 | 左晓玲, 张道海, 罗 兴,等.阻燃长玻纤增强尼龙⁃6 的研究进展[J]. 现代化工, 2013,33(2):33⁃37. |
ZUO X L, ZHANG D H, LUO X, et al. Research Progress on Flame Retardant Long Glass Fiber Reinforced Polyamide 6[J]. Modern Chemical Industry,2013,33(2):33⁃37. | |
10 | 宗若雯, 胡 源, 汪少锋. 尼龙的阻燃研究进展[J]. 火灾科学, 2003, 12(1):46⁃50. |
ZONG R W, HU Y, WANG S F. Research Progress on Flame Retardant Nylon[J]. Fire Safety Science, 2003, 12(1):46⁃50. | |
11 | 李 颖,王建祺.阻燃聚酰胺的发展现状[J] . 高分子材料科学与工程, 1999, 15(1) : 18⁃22. |
LI Y, WANG J Q. Present Status of Flame Retardant Polyamides[J]. Polymer Materials Science and Engineering, 1999, 15(1): 18⁃22. | |
12 | GROB M C, MINDER E. Permanent Antistatic Additives: New Developments[J]. Plastics Additives & Compounding,1999,1(3):20⁃26. |
13 | 吕 强. 新型阻燃剂MPAP的合成及其协同阻燃PA6/GF6的性能[J]. 工程塑料应用, 2019, 47(12):125⁃129. |
LV Q. Synthesis of A Novel Halogen⁃free Flame Retardant MPAP and Its Performance Study on Synergistic Flame⁃retarded Glass Fiber Reinforced PA66[J]. Engineering Plastics Application, 2019, 47(12):125⁃129. | |
14 | SCHMITT E. Phosphorus⁃based Flame Retardants for Thermoplastics[J]. Plastics Additives & Compounding, 2007, 9(3):26⁃30. |
15 | 肖媛芳,许家友,邓海铭. MCA⁃ADEPH磷⁃氮协同阻燃剂的制备及其对PA6阻燃性能的影响[J]. 功能材料, 2016, 48(6):165⁃170. |
XIAO Y F, XU J Y, DENG H M. Preparation of Phosphorus⁃nitrogen Synergistic Flame Retardant MCA⁃ADEPH and Its Effects on Flame Retardancy of PA6[J]. Journal of Functional Materials, 2016, 48(6): 165⁃170. | |
16 | 高 军, 吴贵岚, 徐晓聊, 等. 高分子型抗静电剂的发展状况[J]. 科技创新与应用, 2015, 1(2):49. |
GAO J, WU G L, XU X L, et al. The Development of Polymer Antistatic Agents[J]. Scientific and Technological Innovation and Application,2015,(2):49. | |
17 | 闫东广, 张 远, 周 昱,等. 一步法制备聚酰胺聚醚弹性体及其在抗静电ABS材料中的应用[J]. 高分子材料科学与工程, 2020, 36(2):160⁃165. |
YAN D G, ZHANG Y, ZHOU Y, et al. Preparation of Polyamide⁃Block⁃Polyether Copolymer Based on One⁃Step Method and Its Application in Permanent Antistatic ABS[J]. Polymer Materials Science and Engineering, 2020,36(2):160⁃165. | |
18 | 胡 志. 无卤阻燃抗静电PA6/GF复合材料的研制[J]. 工程塑料应用, 2015, 43(2):35⁃38. |
HU Z. Preparation of Halogen⁃Free Flame Retarded Antistatic Glass Fiber Reinforced Nylon 6 Composite[J]. Engineering Plastics Application, 2015, 43(2): 35⁃38. |
[1] | WEI Simiao, SHAO Lushan, XU Zhun, LIU Yanting, ZHAO Siheng, XU Bo. Flame⁃retardant performance of PA6 modified with hypophosphite/siloxane bi⁃functional compound and diethyl aluminum hypophosphite compound [J]. China Plastics, 2022, 36(7): 129-135. |
[2] | SUN Wenbo, XIN Chunling, HE Yadong, ZHAI Yujiao, YAN Baorui. Influence of micro⁃foaming injection molding process on cell structure of glass⁃fiber⁃reinforced PBT products [J]. China Plastics, 2022, 36(5): 1-7. |
[3] | CHEN Sheng, LIANG Yingchao, WU Fangjuan, FANG Hui, FAN Xinfeng, CHEN Hui, WANG Yonggang. Preparation and interfacial modification of polyamide 6/bidirectional warp⁃knitted glass fiber composites [J]. China Plastics, 2022, 36(5): 24-28. |
[4] | XU Weihua, ZHENG Yu, SHEN Xiangyang, ZHANG Yan, LIU Juwen, YAN Shijing. Effects of different POSS on properties of phosphorus⁃silicon synergistic flame retardant epoxy resin [J]. China Plastics, 2022, 36(4): 115-120. |
[5] | XU Rongxia, WEI Gang, WEI Lilan, WU Jiecui, JIANG Yujiang. Friction and wear properties of PE⁃UHMW modified with nano⁃SiO2 and PA6 [J]. China Plastics, 2022, 36(4): 47-52. |
[6] | ZHANG Jiufu, LUO Kaiqiang, XU Jun, GUO Baohua. Study on comprehensive properties and influencing factors of long glass fiber reinforced PA66 composites [J]. China Plastics, 2022, 36(3): 1-8. |
[7] | ZHANG Shucheng, TANG Wenbin, YU Tianjiao, XU Zhenzhen, XING Jian. Preparation and properties of polyurethane foams with different contents of polyether polyol [J]. China Plastics, 2022, 36(3): 104-109. |
[8] | XIE Yu, WANG Limei, QI Bin. Preparation and properties of crosslinked chitosan/montmorillonite composite films [J]. China Plastics, 2022, 36(3): 58-63. |
[9] | YU Zhixing, LI Yingcheng, WANG Hongxue, PANG Xinlei, WANG Yuyao. Study on laser direct structuring materials based on polyamide 6 and polycarbonate and their fabrication of parts with heterostructure [J]. China Plastics, 2022, 36(2): 8-12. |
[10] | HUANG Wei, LIU Hesheng, HUANG Xingyuan, ZHANG Wei, KUANG Tangqing, CHEN Zhongshi. Study on high⁃pressure water penetration behavior of square cross⁃sectional pipes based on short⁃glass⁃fiber⁃reinforced polypropylene [J]. China Plastics, 2022, 36(2): 82-88. |
[11] | JIN Qingping, YI Jianming, GAO Yonghong, CAO Nannan, DENG Siyuan. Effect on mechanical properties of glass⁃fiber⁃reinforcement polymer bars exposure to alkaline solution under natural ambient temperature [J]. China Plastics, 2022, 36(2): 89-95. |
[12] | YANG Zheng, WANG Zhenhua, LU Shike, LIU Yang, FANG Xiaoming, LI Jiantong, LIU Baoying, DING Tao. Synergistic effect of zinc borate and aluminum diethylphosphinate on flame retardancy of PA6 [J]. China Plastics, 2022, 36(1): 120-127. |
[13] | WANG Yazhen, LIU Xinyu, DONG Shaobo, LAN Tianyu, ZU Liwu. Compatibilizing effect on performance of PE⁃HD/corn stalk biochar composites [J]. China Plastics, 2022, 36(1): 128-134. |
[14] | SUN Guohua, ZHANG Xin, WU Dezhen, HOU Lianlong. Research Progress in High⁃performance Polyimide Composites [J]. China Plastics, 2021, 35(9): 147-155. |
[15] | SUN Zhengmeng, ZHANG Mingxu, ZHANG Xinning, LIANG Ce, ZHANG Hailiang, LI Yunhui, MA Yuqin. Study on Thermal Stability of Bisphenol⁃A⁃Type Epoxy Matrix Composites Doped with Nano Glass Powders [J]. China Plastics, 2021, 35(9): 15-20. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||