Effect of mass ratio of PET to PBT on surface of flame retardant reinforced PET/PBT alloy

doi:10.19491/j.issn.1001-9278.2021.12.006

Abstract

Abstract:

In this paper， the effect of mas ratio of PET to PBT on the surface of flame?retardant reinforced PET/PBT Alloy was investigated. The surface fiber?floating phenomenon was characterized semi?quantitatively using a two?dimensional image tester and visual inspection. The results indicated that the surface fiber?floating phenomenon became less serious with an increase in the PBT content. When the ratio of PET to PBT was close to 1：1， the fiber floating became weakest. When the PBT content further increased， the fiber floating became worse. The flame retardant reinforced PBT exhibited weaker fiber floating than the flame retardant reinforced PET.

Key words: polybutylene terephthalate, polyethylene terephthalate, alloy, flame retardant, reinforcement, surface glass fiber revealed phenomena

CLC Number:

TQ326.3

YIN Nianwei, CHEN Feng, FU Xuejun, CAO Shaoqiang. Effect of mass ratio of PET to PBT on surface of flame retardant reinforced PET/PBT alloy[J]. China Plastics, 2021, 35(12): 32-36.

Figures/Tables 10

References 6

1	付学俊，卢立波，朱文，等. 阻燃增强PBT/PET合金的性能研究［J］. 塑料工业，2012，40（9）：41⁃43.
	FU X J， LU L B，ZHU W， et al. Properties study of reinforced and flame retardant PBT/PET alloy［J］. China Plastics Industry， 2012， 40（9）： 41⁃43.
2	马新敏，于伟东. PBT/PET 复合纤维组分的红外光谱分析技术［J］. 纺织导报，2012（7）：51⁃52.
	MA X M， YU W D. Infrared spectrum analysis technology of PBT/PET composite fiber components ［J］. China Textile Leader， 2012（7）： 51⁃52.
3	童玉华，刘佑习，葛敬银，等. 玻璃纤维增强 PBT／PET 共混复合体系的力学性能［J］. 高分子材料科学与工程，1996，12（6）：105⁃109.
	TONG Y H， LIU Y X， GE J Y， et al. Mechanical properties of PBT/PET blends reinforced by glass fibre［J］.Polymeric Materials Science and Engineering， 1996，12（6）： 105⁃109.
4	潘燕，李又兵，史文，等．GFRPP复合材料“浮纤”改善及结构与性能研究［J］．工程塑料应用，2013，41（7）：17⁃20．
	PAN Y， LI Y B， SHI W， et al. Study on “floating fiber” improvement，structure and property of GFRPP composites［J］. Engineering Plastics Application， 2013， 41（7）： 17⁃20.
5	王恒兵．聚丙烯/玻璃纤维复合材料浮纤改善及其结构性能研究［Ｄ］．重庆：重庆理工大学，2012.
6	于海舰，殷年伟，陈锋，等. 注塑模温对阻燃增强PET/PBT合金表面浮纤的影响［J］.塑料工业，2021，49（7）：52⁃56.
	YU H J， YIN N W， CHEN F， et al. Effect of injection mold temperature on the surface glass fiber revealed phenomena of flame retardant reinforced PET/PBT［J］. China Plastics Industry， 2021，49（7）：52⁃56.

实验编号	PBT	PET	炭黑	溴化聚苯乙烯	锑白	硫酸钡	玻璃纤维	其他加工助剂
BK0728Y ?1^#	0	48.5	0.5	9	2	6	32	2
BK0728Y ?2^#	11	37.5	0.5	9	2	6	32	2
BK0728Y ?3^#	22	26.5	0.5	9	2	6	32	2
BK0728Y ?4^#	24.2	24.3	0.5	9	2	6	32	2
BK0728Y ?5^#	26.5	22	0.5	9	2	6	32	2
BK0728Y ?6^#	37.5	11	0.5	9	2	6	32	2
BK0728Y ?7^#	48.5	0	0.5	9	2	6	32	2

实验编号	PBT	PET	炭黑	溴化聚苯乙烯	锑白	硫酸钡	玻璃纤维	其他加工助剂
BK0728Y ?1^#	0	48.5	0.5	9	2	6	32	2
BK0728Y ?2^#	11	37.5	0.5	9	2	6	32	2
BK0728Y ?3^#	22	26.5	0.5	9	2	6	32	2
BK0728Y ?4^#	24.2	24.3	0.5	9	2	6	32	2
BK0728Y ?5^#	26.5	22	0.5	9	2	6	32	2
BK0728Y ?6^#	37.5	11	0.5	9	2	6	32	2
BK0728Y ?7^#	48.5	0	0.5	9	2	6	32	2

实验编号	PBT	PET	炭黑	溴化聚苯乙烯	锑酸钠	硫酸钡	玻璃纤维	其他加工助剂
BK0806Y ?1^#	0	48.5	0.5	9	2	6	32	2
BK0806Y ?2^#	11	37.5	0.5	9	2	6	32	2
BK0806Y ?3^#	22	26.5	0.5	9	2	6	32	2
BK0806Y ?4^#	24.2	24.3	0.5	9	2	6	32	2
BK0806Y ?5^#	26.5	22	0.5	9	2	6	32	2
BK0806Y ?6^#	37.5	11	0.5	9	2	6	32	2
BK0806Y ?7#	48.5	0	0.5	9	2	6	32	2

实验编号	PBT	PET	炭黑	溴化聚苯乙烯	锑酸钠	硫酸钡	玻璃纤维	其他加工助剂
BK0806Y ?1^#	0	48.5	0.5	9	2	6	32	2
BK0806Y ?2^#	11	37.5	0.5	9	2	6	32	2
BK0806Y ?3^#	22	26.5	0.5	9	2	6	32	2
BK0806Y ?4^#	24.2	24.3	0.5	9	2	6	32	2
BK0806Y ?5^#	26.5	22	0.5	9	2	6	32	2
BK0806Y ?6^#	37.5	11	0.5	9	2	6	32	2
BK0806Y ?7#	48.5	0	0.5	9	2	6	32	2

实验编号	熔体流动速率/ g·（10 min）^-1	实验编号	熔体流动速率/ g·（10 min）^-1
BK0728Y ?1^#	191	BK0806Y ?1^#	48
BK0728Y ?2^#	117	BK0806Y ?2^#	48
BK0728Y ?3^#	113	BK0806Y ?3^#	50
BK0728Y ?4^#	130	BK0806Y ?4^#	52
BK0728Y ?5^#	121	BK0806Y ?5^#	52
BK0728Y ?6^#	191	BK0806Y ?6^#	50
BK0728Y ?7^#	94	BK0806Y ?7^#	60