Effect of MMA quality on polymerization and polymer properties

doi:10.19491/j.issn.1001-9278.2025.03.009

Abstract

Abstract:

In this paper， homopolymerization was carried out to prepare polymethyl methacrylate （PMMA） by using methyl methacrylate （MMA） as a monomer and azobisisobutyronitrile as an initiator. The effects of the chroma of MMA， water， and inhibitor contents on the polymerization process and properties of PMMA were investigated. The results indicated that the chroma of MMA should be controlled at below 6 in order to meet a requirement of optical grade for PMMA. There was no direct influence of water content on polymerization. Considering the forming process of PMMA and avoiding the hydrolysis of PMMA， it was recommended to control water content below 500 mg/kg. When the inhibitor content was less than 10 mg/kg， there was little effect on the polymerization and properties of PMMA， and MMA could be directly used as a monomer for its polymerization.

Key words: methyl methacrylate, polymethyl methacrylate, bulk polymerization

CLC Number:

TQ325.7

SONG Yuexiao, ZHOU Guiyang, ZHANG Xiongwei, ZHOU Lixia, CHEN Yao, YANG Zheng, DENG Hangjun, LI Zihao, CAI Chenxi, YIN Hong. Effect of MMA quality on polymerization and polymer properties[J]. China Plastics, 2025, 39(3): 48-52.

Figures/Tables 8

References 20

1	Ali U， Karim K J B A， Buang N A. A review of the properties and applications of poly（methyl methacrylate）（PMMA）［J］. Polymer Reviews， 2015， 55（4）： 678⁃705.
2	陈春玉，王少楠，胡迎. 聚甲基丙烯酸甲酯的合成及应用进展［J］. 广州化工， 2021， 49（9）： 1⁃2.
	CHEN C Y， WANG S N， HU Y. Research progress on synthesis and application of polymethylmethacrylate［J］. Guangzhou Chemical Industry， 2021， 49（9）： 1⁃2.
3	宋尚德，程哲，郭志伟，等. 聚甲基丙烯酸甲酯生产工艺专利分析［J］. 弹性体， 2020， 30（4）： 65⁃71.
	SONG S D， CHENG Z， GUO Z W， et al. Domestic patent analysis of polymethylmethacrylate production process［J］. China Elastomerics， 2020， 30（4）： 65⁃71.
4	陈继新，吕洁，赵金德，等. 聚甲基丙烯酸甲酯（PMMA）生产工艺与设备研究概述［J］. 化工科技， 2012， 20（2）： 81⁃84.
	CHEN J X， LYU J， ZHAO J D， et al. Research on PMMA production process and equipment［J］. Science & Technology in Chemical Industry， 2012， 20（2）： 81⁃84.
5	Achilias D S. A review of modeling of diffusion controlled polymerization reactions［J］. Macromolecular Theory and Simulations， 2007， 16（4）： 319⁃347.
6	马占镖. 甲基丙烯酸酯树脂及其应用［M］. 北京：化学工业出版社， 2002： 127⁃128.
7	董鑫，杨金胜，刘哲，等. 聚合温度对PMMA高温本体聚合的影响［J］. 弹性体， 2018， 28（2）： 64⁃67.
	DONG X， YANG J S， LIU Z， et al. Influences of polymerization temperature on bulk polymerization of PMMA at high temperature［J］. China Elastomerics， 2018， 28（2）： 64⁃67.
8	Suzuki Y， Mishima R， Matsumoto A. Bulk polymerization kinetics of methyl methacrylate at broad temperature range investigated by differential scanning calorimetry［J］. International Journal of Chemical Kinetics， 2022， 54（6）： 361⁃370.
9	Suzuki Y， Mishima R， Kato E， et al. Analysis of the glass effect and Trommsdorff effect during bulk polymerization of methyl methacrylate， ethyl methacrylate， and butyl methacrylate［J］. Polymer Journal， 2023， 55（3）： 229⁃238.
10	黄文华，李剑寒，江力，等. 甲基丙烯酸甲酯常规自由基聚合研究［J］. 合成树脂及塑料， 2023， 40（6）： 11⁃15.
	HUANG W H， LI J H， JIANG L， et al. Free radical polymerization of MMA initiated by BPO［J］. China Synthetic Resin and Plastics， 2023， 40（6）： 11⁃15.
11	赵伟，戴培邦，田磊. 水相沉淀聚合法制备聚甲基丙烯酸甲酯的研究［J］. 塑料工业， 2022， 50（S1）： 44⁃48.
	ZHAO W， DAI P B， TIAN L. Study on preparation of poly（methyl methacrylate） by aqueous precipitation polymerization［J］. China Plastics Industry， 2022， 50（S1）： 44⁃48.
12	曹春雷，谭志勇，张子健，等. 链转移剂叔十二烷基硫醇对高温连续本体法合成PMMA热稳定性的影响［J］. 高分子材料科学与工程， 2013， 29（2）： 50⁃53.
	CAO C L， TAN Z Y， ZHANG Z J， et al. The effect of chain transfer agent t⁃dodecyl mercaptan on the thermal and thermol oxidative stability of PMMA［J］. Polymer Materials Science & Engineering， 2013， 29（2）： 50⁃53.
13	Çetinkaya O， Demirci G， Mergo P. Effect of the different chain transfer agents on molecular weight and optical properties of poly（methyl methacrylate）［J］. Optical Materials， 2017， 70： 25⁃30.
14	秦增增，李雅芙，王姝，等. 国内外聚甲基丙烯酸甲酯本体聚合过程概述［J］. 天津科技， 2016， 43（4）： 26⁃29+33.
	QIN Z Z， LI Y F， WANG S， et al. Overview of the process of poly methyl methacrylate bulk polymerization both in China and in the world［J］. Tianjin Science & Technology， 2016， 43（4）： 26⁃29+33.
15	刘金成，陈谦，刘玉佩，等. 甲基丙烯酸甲酯的合成技术研究进展［J］. 中国塑料， 2022， 36（1）： 178⁃183.
	LIU J C， CHEN Q， LIU Y P， et al. Research progress in synthesis technologies of methyl methacrylate［J］. China Plastics， 2022， 36（1）： 178⁃183.
16	Semen J， Lando J B. The acid hydrolysis of isotactic and syndiotactic poly（methyl methacrylate）［J］. Macromolecules， 1969， 2（6）： 570⁃575.
17	Baines F C， Bevington J C. A tracer study of the hydrolysis of methyl methacrylate and methyl acrylate units in homopolymers and copolymers［J］. Journal of Polymer Science Part A-1： Polymer Chemistry， 1968， 6（9）： 2433⁃2440.
18	周琳琳，王凤磊，耿红梅，等. 航空有机玻璃银纹分析及预防措施［J］. 玻璃， 2012， 39（12）： 16⁃18.
	ZHOU L L， WANG F L， GENG H M， et al. Study of silver craze on aviation PMMA glass and preventive measures［J］. Glass， 2012， 39（12）： 16⁃18.
19	王磊，王淦，吴越. 气相色谱法测定丙烯酸酯中三种阻聚剂含量［J］. 石油化工， 2020， 49（7）： 669⁃673.
	WANG L， WANG G， WU Y. Determination of three polymerization inhibitors in acrylic esters by gas chromatography［J］. Petrochemical Technology， 2020， 49（7）： 669⁃673.
20	陆赟涛，江力，蒋其民，等. 甲基丙烯酸甲酯自由基聚合歧化终止机理［J］. 高分子通报， 2023， 36（2）： 241⁃247.
	LU Y T， JIANG L， JIANG Q M， et al. Disproportionation termination mechanism in the free⁃radical polymerization of methyl methacrylate［J］. Polymer Bulletin， 2023， 36（2）： 241⁃247.

项目		值
色度		6
酸度/mg·kg^-1		18
水分/mg·kg^-1		262
MMA/%（质量分数）		99.96
杂质含量/mg·kg^-1	甲基丙烯酸乙酯	6
	2⁃羟基异丁酸甲酯	4
	MMA二聚体	90
	TBX（阻聚剂）	64

项目		值
色度		6
酸度/mg·kg^-1		18
水分/mg·kg^-1		262
MMA/%（质量分数）		99.96
杂质含量/mg·kg^-1	甲基丙烯酸乙酯	6
	2⁃羟基异丁酸甲酯	4
	MMA二聚体	90
	TBX（阻聚剂）	64

MMA		PMMA			PMMA板
水分/mg·kg^-1	转化率/%	M_n	PDI	T_g/℃	透光率/%
160	89.02	371 240	4.18	122.4	93.1
240	89.21	337 704	4.94	123.5	93.0
500	88.62	358 219	4.86	122.0	93.2
1 000	89.33	376 954	4.66	123.4	93.1

MMA		PMMA			PMMA板
水分/mg·kg^-1	转化率/%	M_n	PDI	T_g/℃	透光率/%
160	89.02	371 240	4.18	122.4	93.1
240	89.21	337 704	4.94	123.5	93.0
500	88.62	358 219	4.86	122.0	93.2
1 000	89.33	376 954	4.66	123.4	93.1

MMA			PMMA			PMMA板
阻聚剂/mg·kg^-1	t/min	转化率/%	M_n	PDI	T_g/°C	透光率/%
0	140	43.79	249 768	4.01	123.4	93.4
0	180	78.38	313 694	4.65	123.4	93.4
10	150	44.52	229 686	4.38	124.8	93.2
10	240	76.10	304 167	4.68	124.8	93.2
25	210	45.91	216 508	4.93	124.2	92.8
25	300	74.88	265 849	5.25	124.2	92.8