Development of heat shrinkable BOPP packaging film with low friction coefficient

Received:2023-09-11 Revised:2023-09-27 Online:2024-06-26 Published:2024-06-26

摘要/Abstract

摘要： 研究了一种高性能BOPP薄膜的开发，采用特殊的原料配方和加工工艺制备。通过与标准型BOPP薄膜对比，跟踪30天内第1天、第7天、第15天、第30天的摩擦因数、热收缩率、光学性能，分析数据得出新开发薄膜的各性能都有所优化。该BOPP薄膜具有低摩擦因数、高热收缩性能和良好的光学性能。

关键词: 双向拉伸聚丙烯, 薄膜, 摩擦因数, 光学性能, 热收缩

Abstract: A high-performance biaxially oriented polypropylene （BOPP） film was developed using a special raw material formulation with a special processing technique， and its friction coefficient， heat shrinkage， and optical properties were compared with a standard BOPP film at four selected times on the 1st， 7th， 15th， and 30th days within 30 days. The results indicated that the developed film obtained an improvement in all aspects of performance. The film exhibited a low friction coefficient， high heat shrinkage， and excellent optical properties.

Key words: biaxially oriented polypropylene, film, friction coefficient, optical properties, heat shrinkage

谢波涂志刚周先进张尚先熊立贵杨亭. 低摩擦因数热收缩BOPP包装薄膜的开发[J]. , 2024, 38(6): 78-81.

参考文献

[1] NUNTAPICHEDKUL B, TANTAYANON S, LAOHHASURAYOTIN K. Practical Approach in Surface Modification of Biaxially Oriented Polypropylene Films for Gravure Printability[J]. Applied Surface Science, 2014, 314: 331-340.
[2] 周亚男, 张秀梅, 陈烨. 聚丙烯无纺布活性包装材料的制备及性能研究[J]. 包装工程 , 2018, 39(15): 82-87.
ZHOU Ya-nan, ZHANG Xiu-mei, CHEN Ye. Preparation and Properties of Polypropylene Non-woven Fabric Active Packaging Materials[J]. Packaging Engineering, 2018, 39(15): 82-87
[3] 高达利, 张师军, 徐毅辉, 等. 原料结构对BOPP薄膜拉伸工艺及性能的影响[J]. 塑料科技, 2018, 46(5): 34-37.
GAO Da-li, ZHANG Shi-jun, XU Yi-hui, et al. Influence of the Molecular Structure on the Tensile Process and Properties of BOPP Films[J]. Plastics Science and Technology, 2018, 46(5): 34-37.
[4] 倪洋洋, 林月城, 江贵长, 等. 等规聚丙烯改性的研究进展[J]. 包装工程, 2016, 37(17): 144-149.
NI Yang-yang, LIN Yue-cheng, JIANG Gui-chang, et al. Research Progress of Isotactic Polypropylene Modification[J]. Packaging Engineering, 2016, 37(17): 144-149.
[5] 张莉琼, 刘晓艳, 赵素芬, 等. 低摩擦系数BOPP烟膜的研究[J]. 现代塑料加工应用 , 2017, 29(2): 36-38.
ZHANG Li-qiong, LIU Xiao-yan, ZHAO Su-fen, et al. The Development on the BOPP Cigarette Film with Low Friction Coefficient[J]. Modern Plastics Processing and Applications, 2017, 29(2): 36-38.
[6] 董莉. 高光泽低气味聚丙烯的结构与性能研究[D]. 兰州: 兰州理工大学, 2019: 12-15. DONG Li. Study on Structure and Properties of High Gloss and Low Odor Polypropylene[D]. Lanzhou: Lanzhou University of Technology, 2019: 12-15.
[7] 黄捷, 王波, 杨金明. 高光泽度聚丙烯的研究[J]. 现代塑料加工应用, 2017, 29(4): 17-20.
HUANG Jie, WANG Bo, YANG Jin-ming. Research on High Gloss Polypropylen[J]. Modern Plastics Processing and Applications, 2017, 29(4): 17-20.
[8] 涂志刚, 熊立贵, 陈利伟, 等. 添加剂对BOPP薄膜光学性能的影响[J]. 包装工程, 2020, 41(31): 139-144.
TU Zhi-gang, XIONG Li-gui, CHEN Li-wei, et al. Effects of Additives on Optical Properties of BOPP Films[J]. Packaging Engineering, 2020, 41(31): 139-144.
[9] 高达利, 张师军, 唐毓婧, 等. 拉伸倍率对BOPP薄膜性能的影响[J]. 中国塑料, 2015, 29(06): 78-81.
GAO Dali, ZHANG Shijun, TANG Yujing, et al. Influence of Stretching Ratio on Properties of BOPP Films[J]. China Plastics, 2015, 29(06): 78-81.
[10] 柯君豪, 封水彬, 蒋文军. 双向拉伸聚丙烯薄膜专用料的结构与性能[J]. 石化技术与应用, 2017, 35(3): 234-237.
KE Jun-hao, FENG Shui-bin, JIANG Wen-jun. Structure and Property of Biaxially Oriented Polypropylene Special Resin[J]. Petrochemical Technology & Application, 2017, 35(3): 234-237.

[1]	谢波, 涂志刚, 周先进, 张尚先, 熊立贵, 杨亭. 低摩擦因数热收缩BOPP包装薄膜的开发[J]. 中国塑料, 2024, 38(6): 78-81.
[2]	孔德金, 廖旭, 李南希, 雷静怡, 刘阔, 李洪飞, 唐武飞. 壳聚糖/聚乙烯醇/明胶复合薄膜的阻隔和阻燃性能研究[J]. 中国塑料, 2024, 38(5): 28-32.
[3]	杨超永, 郭金强, 王富玉, 张玉霞. 挤出吹塑工艺对PBAT/PLA共混体系微观结构与性能的影响[J]. 中国塑料, 2024, 38(5): 82-87.
[4]	汪鹏, 姚成, 刘刚, 蔡希鹏, 贾磊, 王铠, 陈龙. 不同拉伸方式引起BOPP薄膜的结构特征与绝缘介电性能[J]. 中国塑料, 2024, 38(3): 54-58.
[5]	纪建超, 颜悦, 陈宇宏, 哈恩华, 郝常山, 雷沛. 在PMMA上低温沉积TiO₂薄膜的光学性能及显微结构[J]. 中国塑料, 2024, 38(3): 7-12.
[6]	吴志峰, 姜锐涛, 丁永跃, 潘新飞, 王志伟. 钢塑转换防腐层老化性能研究[J]. 中国塑料, 2024, 38(2): 76-81.
[7]	关国涛, 刘晨泽, 何世权, 宋超洋, 张响, 赵娜, 王超. 抗菌可降解聚乳酸薄膜制备与性能测试[J]. 中国塑料, 2023, 37(9): 8-13.
[8]	马小丰董金明李洪娟郑志恒田东林申浩海王亚涛汪晓东. 高耐磨聚甲醛粉末静电喷涂涂层的配方设计及喷涂工艺研究[J]. , 2023, 37(6): 83-90.
[9]	高奇奇, 郝艳玲, 程龙, 宋小双, 王世慧. 玉米淀粉/TiO₂纳米复合薄膜制备与性能[J]. 中国塑料, 2023, 37(2): 45-50.
[10]	王从晓, 郑家欣, 赵玉印, 苏振乾, 任峰. 螺杆构型对PBAT/Talc复合材料性能的影响[J]. 中国塑料, 2023, 37(12): 101-108.
[11]	戴熙瀛, 张翀, 万彩霞, 杨威, 邢照亮. 影响BOPP电容膜击穿场强的微观结构及与制备工艺的关系探究[J]. 中国塑料, 2023, 37(12): 29-34.
[12]	王从晓郑家欣赵玉印苏振乾任峰. 螺杆构型对PBAT/Talc复合材料性能的影响[J]. , 2023, 37(12): 101-108.
[13]	张策, 杨卫民, 谭晶, 丁玉梅, 程礼盛. 微波强化脱除聚丙烯腈薄膜中残留二甲基亚砜的实验研究[J]. 中国塑料, 2023, 37(10): 1-7.
[14]	董玥, 董霄, 朱德兆, 杨延翔, 罗琛, 李阳, 李锦山. 聚酰亚胺发展概况与应用展望[J]. 中国塑料, 2022, 36(9): 85-95.
[15]	杨超永, 郭金强, 王富玉, 张玉霞. 高性能塑料薄膜制备方法及改性研究进展[J]. 中国塑料, 2022, 36(9): 167-179.