China Plastics ›› 2009, Vol. 23 ›› Issue (08): 48-52 .DOI: 10.19491/j.issn.1001-9278.2009.08.011
Previous Articles Next Articles
LI Hai-dong;LIN Yu-han;NIE Wei;JI Xiang-ling
Received:
Revised:
Online:
Published:
Abstract: PLLA-PDLA copolymer film was obtained through spin-coating and crystallized at constant temperature. Thermal property, crystalline morphology, and crystalline structure of the film were studied uisng DSC、AFM, and XRD. At 128-153℃, an obvious crystallization peak was observed. AFM was applied to characterize the crystalline morphology of the film from different crystallization temperature, solution concentration, time, solvent, and substrate. Several rod-shaped and branching crystals with different size were observed. Especially, branching and entangled structures were observed on glass substrate, with a higher coverage density than on the silicon substrate. The XRD gave diffraction peaks at 2q values of 12.01°, 20.88°, and 24.18°.
Key words: FONT-FAMILY: Arial, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体">L-lactide/D-lactideFONT-FAMILY: 宋体, mso-ascii-font-family: Arial, mso-hansi-font-family: Arial, mso-bidi-font-family: Arial, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">, FONT-FAMILY: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体">copolymerFONT-FAMILY: 宋体, mso-ascii-font-family: Arial, mso-hansi-font-family: Arial, mso-bidi-font-family: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">, FONT-FAMILY: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体">filmFONT-FAMILY: 宋体, mso-ascii-font-family: Arial, mso-hansi-font-family: Arial, mso-bidi-font-family: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">, FONT-FAMILY: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体">atomic force microscopeFONT-FAMILY: 宋体, mso-ascii-font-family: Arial, mso-hansi-font-family: Arial, mso-bidi-font-family: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA">, FONT-FAMILY: Arial, mso-font-kerning: 1.0pt, mso-ansi-language: EN-US, mso-fareast-language: ZH-CN, mso-bidi-language: AR-SA, mso-fareast-font-family: 宋体">crystalline morphology
LI Hai-dong, LIN Yu-han, NIE Wei, JI Xiang-ling. Crystalline Morphology of PLLA-PDLA Copolymers Films[J]. China Plastics, 2009, 23(08): 48-52 .
0 / / Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://www.plaschina.com.cn/EN/10.19491/j.issn.1001-9278.2009.08.011
https://www.plaschina.com.cn/EN/Y2009/V23/I08/48