Effect of Injection Molding Process on Environmental Stress Cracking Behavior of Polycarbonate Parts

doi:10.19491/j.issn.1001-9278.2010.04.016

China Plastics ›› 2010, Vol. 24 ›› Issue (04): 76-79 .DOI: 10.19491/j.issn.1001-9278.2010.04.016

Previous Articles Next Articles

Effect of Injection Molding Process on Environmental Stress Cracking Behavior of Polycarbonate Parts

HAN Jian HAN Dongxue LIU Chuntai CHEN Jingbo SHEN Changyu

Received:2009-12-31 Revised:1900-01-01 Online:2010-04-26 Published:2010-04-26

Abstract

Abstract: This work investigates the environment stress cracking behavior of polycarbonate (PC) injection molded plates with different process conditions. When exposed to carbon tetrachloride, crack appeared at the edge surface of the molded parts. Higher injection temperature increases resistance to the environmental stress crack, while higher packing pressure makes the cracking more serious. Additional study was concentrated on the effect of molecular orientation and residual stresses on crack formation of the parts.

Key words: polycarbonate, environment stress cracking, molecular orientation, birefringence, residual stress

CLC Number:

TQ320.66 + 2

HAN Jian HAN Dongxue LIU Chuntai CHEN Jingbo SHEN Changyu. Effect of Injection Molding Process on Environmental Stress Cracking Behavior of Polycarbonate Parts[J]. China Plastics, 2010, 24(04): 76-79 .

[1]	HE Hezhi, XU Li, YANG Yike. Effect of prestress on mechanical properties of PC/CF laminates [J]. China Plastics, 2022, 36(4): 1-5.
[2]	YU Zhixing, LI Yingcheng, WANG Hongxue, PANG Xinlei, WANG Yuyao. Study on laser direct structuring materials based on polyamide 6 and polycarbonate and their fabrication of parts with heterostructure [J]. China Plastics, 2022, 36(2): 8-12.
[3]	LUO Fei, LI Cuijuan, LIU Zhuojia, LIU Yuxin, SHI Suyu, DANG Xudan, LIU Chuntai, ZHAO Yongtao. Study on Relationship between Molecular Orientation and Dynamic Viscoelasticity of Polycarbonate [J]. China Plastics, 2021, 35(9): 81-86.
[4]	YING Jie, QIU Qihao, ZHANG Xing, GU Hainan, LUO Rui. Effect of Talc on Properties of Flame⁃retardant Polycarbonate [J]. China Plastics, 2021, 35(5): 107-112.
[5]	SUN Qiwei, CHEN Yuhong, DONG Shuyuan, LANG Jianlin, ZHOU Xiaowei, ZHANG Yun. Warpage Simulation of Overmolding Injection Compression Molded PMMA/PC Composite Panels [J]. China Plastics, 2021, 35(4): 53-59.
[6]	WANG Cheng, WENG Nanchang, NIE Yan, QIN Hongliang. Study on Application of PBT/PC Film in Document Manufacturing [J]. China Plastics, 2021, 35(2): 71-76.
[7]	LUO Fei, HAO Lingao, WANG Tengfei, LIU Hongpeng, DANG Xudan, WANG Yaming, LIU Chuntai, SONG Yan. High⁃temperature Stretching Induced Multi⁃structural Deformation of PLA⁃based Composites [J]. China Plastics, 2021, 35(2): 77-83.
[8]	WANG Suwei, ZHANG Wenxin, XUE Ping, ZHANG Guangpu, HU Yubing, JIANG Wei. An overview in self⁃reinforced polymer⁃based composites prepared using solid⁃state molding technology [J]. China Plastics, 2021, 35(12): 166-173.
[9]	CHEN Yuhong, ZHAN Maosheng. Effect of compression process parameters on residual stress of injection⁃ compression⁃molded polycarbonate transparencies [J]. China Plastics, 2021, 35(12): 9-15.
[10]	BI Weifeng, LIU Jiaoshi, CHEN Shaojun, YUAN Hao, ZHANG Yanxia. Effect of Composition Factors on Mechanical Properties of PC/ABS Alloy Exposed to Alkylbenzene [J]. China Plastics, 2021, 35(11): 44-48.
[11]	YIN Hongmei, LIU Yongli, WANG Jianan, MEI Ye. Study on Design Method of Structural Optimization for Air Bag Plastic Cover Plate Based on ISIGHT [J]. China Plastics, 2020, 34(9): 61-65.
[12]	Jie YING, Qihao QIU, Haojie ZHANG, Hainan GU, Hao ZHOU. Effect of Different Types of Toughening Agent on Properties of Polycarbonate [J]. China Plastics, 2020, 34(7): 30-35.
[13]	QIAO Wenyu, WANG Chenglei, HU Hao. Research on Modification of PETG Series Filament for FDM [J]. China Plastics, 2020, 34(10): 24-31.
[14]	. Research on flexible substrate microneedle process parameters for micro-injection compression molding [J]. China Plastics, 2018, 32(12): 80-85.
[15]	. Mechanism and Development Trend of Halogen-free Flame Retardants for Polycarbonate [J]. China Plastics, 2017, 31(03): 1-6 .

Effect of Injection Molding Process on Environmental Stress Cracking Behavior of Polycarbonate Parts

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments