Effect of Talc on Properties of Flame⁃retardant Polycarbonate

doi:10.19491/j.issn.1001-9278.2021.05.017

Abstract

Abstract:

Talc was used to modify the flame retardancy of polycarbonate （PC） filled with titanium dioxide. The effects of talc on the thermal stability， combustion and mechanical properties， flame retardancy and anti-aging performance of resultant PC compounds were investigated. The results indicated that the PC compounds presented a decrease in impact strength. With the addition of 0.5 wt%~2 wt% talc， the flame?retardancy of the compounds reached the UL 94 V?0 classification， the total heat release decreased by 4~8 MJ/m²， and the initial decomposition temperature increased by 8~10 °C. Meanwhile， the compounds exhibited an improvement in the ability to resist the heat oxygen aging and damp heat aging in the presence of adding talc.

Key words: polycarbonate, talc, thermal oxidative aging, hydrothermal aging

CLC Number:

TQ323.4⁺1

YING Jie, QIU Qihao, ZHANG Xing, GU Hainan, LUO Rui. Effect of Talc on Properties of Flame⁃retardant Polycarbonate[J]. China Plastics, 2021, 35(5): 107-112.

Figures/Tables 8

References 16

1	窦立岩，汪丽梅.聚碳酸酯在现代塑料工业的应用及研究进展［J］.山东化工，2019，48（23）：84⁃85.
	DOU L Y，WANG L M.Application and Research Advancement of Polycarbonate in Modern Plastics Industry［J］.Shandong Chemical Industry，2019，48（23）：84⁃85.
2	中国合成树脂供销协会.我国聚碳酸酯产业发展现状［J］.中国塑料，2019，33（10）：105⁃109.
	China Synthetic Resin Supply and Sale Association Current Situation of Polycarbonate Industry in China［J］.China Plastics，2019，33（10）：105⁃109.
3	王钰玮.聚碳酸酯生产技术与国内外市场需求问题研究［J］.化工设计通讯，2019，45（9）：141⁃142.
	WANG Y W. Research on Polycarbonate Production Technology and Market Demand Problems at Home and Abroad［J］. Chemical Engineering Design Communications，2019，45（9）：141⁃142.
4	柴瑞丹，包建宁，倪桓，等.环保型阻燃PC的研究进展［J］.云南化工，2019，46（10）：32⁃34，36.
	CHAI R D，Bao J N，Ni H，et al. Investigation Progress of Environment⁃friendly Fire⁃retardant Polycarbonate［J］. Yunnan Chemical Technology，，2019，46（10）：32⁃34，36.
5	崔明.无卤阻燃剂在聚碳酸酯中的应用研究进展［J］.精细与专用化学品，2020，28（6）：29⁃31.
	CUI M.Advances in the Application Research of Halogen⁃free Flame Retardants in Polycarbonate［J］.Fine and Specialty Chemicals，2020，28（6）：29⁃31.
6	唐荣芝，何航，马雅琳，等.聚碳酸酯用阻燃剂研究进展［J］.四川化工，2019，22（4）：14⁃17.
	TANG S Z，HE H，MA Y L，et al.Research Progress of Flame Retardants for Polycarbonate［J］.Sichuan Chemical Industry，2019，22（4）：14⁃17.
7	宁淑慧，李凯，何吉来，等.含磷硫的三嗪衍生物阻燃剂在聚碳酸酯中的应用［J］.塑料工业，2019，47（12）：102⁃106.
	NING S H，LI K，MA Y L，et al. Application of a Triazine Derivative Containing Phosphorus⁃Sulfur as Flame Retardant in Polycarbonat［J］. China Plastics Industry， 2019，47（12）：102⁃106.
8	谢松.有机硅系阻燃剂和溴系阻燃剂在聚碳酸酯中的应用［J］.江西化工，2019（5）：183⁃184.
	XIE S. Application of Organosilicon Fame Retardant and Bromine Flame Retardant in Polycarbonate［J］.Jiangxi Chemical Industry，2019（5）：183⁃184.
9	吴鸿飞.聚合物/层状硅酸盐纳米复合材料的阻燃性能研究进展［J］.广州化工，2015，43（23）：59⁃61.
	WU H F.Research Progress on Flame⁃retarded Properties of Polymer Layered⁃silicate Nanocomposites［J］.Guangzhou Chemical Industry，2015，43（23）：59⁃61.
10	JANG K S. Mineral Filler Effect on the Mechanics and Flame Retardancy of Polycarbonate Composites： Talc and Kaolin［J］. E⁃Polymers， 2016， 16（5）：379⁃386.
11	HU Z， CHEN L， ZHAO B， et al. A Novel Efficient Halo⁃gen⁃free Flame Retardant System for Polycarbonate［J］. Polymer Degradation & Stability， 2011， 96（3）：320⁃327.
12	刘晓亮，孙东海，刘贤文，等.云母粉与磺酸盐协效阻燃聚碳酸酯的研究［J］.塑料工业，2013，41（3）：108⁃112.
	LIU X L，SUN D H，LIU X W，et al. Study on the Synergistic Flame Retardant of Mica and Sulfonate on the PCB［J］. China Plastics Industry，2013，41（3）：108⁃112.
13	沈俊才，张秀菊，林志丹，等.硅酸盐填充型无卤阻燃聚碳酸酯的性能研究［J］.塑料工业，2010，38（11）：51⁃54.
	SHEN J C，ZHANG X J，LIN Z D，et al.Study on Properties of Halogen⁃free Flame⁃retardant Polycarbonate Composite Filled with Silicate［J］. China Plastics Industry， 2010，38（11）：51⁃54.
14	严敏仪，刘述梅，赵建青.滑石粉和间苯二酚双（二苯基磷酸酯）协效阻燃PC/ABS合金的研究［J］.广东化工，2020，47（8）：1⁃4.
	YAN M Y，LIU S M，ZHAO J Q. Study on Synergistic Effect of Talcum Powder and Resorcinol Bis（Diphenyl Phosphate） on the Flame⁃retardant Properties of PC/ABS Alloy［J］. Guangzhou Chemical Industry，2020，47（8）：1⁃4.
15	杨业昕，李迎春，王盼，等.滑石粉对PA6/MCA体系阻燃性能的影响［J］.塑料科技，2016，44（1）：64⁃68.
	YANG Y X，LI Y C，WANG P，et al.Effect of Talc on Flame Retardant Property of PA6/MCA Composites［J］. Plastics Science and Technology， 2016，44（1）：64⁃68.
16	莫锦鹏，麦伟宗，李景，等.改性聚碳酸酯材料热氧降解行为研究［J］.合成材料老化与应用，2019，48（6）：10⁃14.
	MO J P，MAI W Z，LI J， et al.Research of Aerobic Thermal Degradation Behavior of Modified Polycarbonate［J］.Synthetic Materials Aging and Application， 2019，48（6）：10⁃14.

样品编号	PC02?20 含量/%	R69 含量/%	SD?9242 含量/%	EM500 含量/%	FR309 含量/%	1010 含量/%	168 含量/%	PETS 含量/%	TF?1645 PA5935 含量/%
1^#	93	7	0	1	0.15	0.1	0.2	0.5	0.6
2^#	93	6.5	0.5	1	0.15	0.1	0.2	0.5	0.6
3^#	93	6	1	1	0.15	0.1	0.2	0.5	0.6
4^#	93	5	2	1	0.15	0.1	0.2	0.5	0.6
5^#	92.5	7	0.5	1	0.15	0.1	0.2	0.5	0.6
6^#	92	7	1	1	0.15	0.1	0.2	0.5	0.6
7^#	91	7	2	1	0.15	0.1	0.2	0.5	0.6

样品编号	PC02?20 含量/%	R69 含量/%	SD?9242 含量/%	EM500 含量/%	FR309 含量/%	1010 含量/%	168 含量/%	PETS 含量/%	TF?1645 PA5935 含量/%
1^#	93	7	0	1	0.15	0.1	0.2	0.5	0.6
2^#	93	6.5	0.5	1	0.15	0.1	0.2	0.5	0.6
3^#	93	6	1	1	0.15	0.1	0.2	0.5	0.6
4^#	93	5	2	1	0.15	0.1	0.2	0.5	0.6
5^#	92.5	7	0.5	1	0.15	0.1	0.2	0.5	0.6
6^#	92	7	1	1	0.15	0.1	0.2	0.5	0.6
7^#	91	7	2	1	0.15	0.1	0.2	0.5	0.6

样品编号	拉伸强度/ MPa	断裂伸长/ %	弯曲强度/ MPa	弯曲模量/ MPa	冲击强度（ISO 180）/ kJ^.m^-2	冲击强度 (ASTM P256)/J^.m^-1	t₁+t₂/ s	滴落根数 (n/5)	UL 94级别（1.6 mm）
1^#	54.2±1.1	102±11	91.1±0.8	2 603±25	52.2±2.4	733±15	62	0/5	V?1
2^#	54.2±1.3	85±5	91.1±1.2	2 661±36	45.3±0.5	642±20	28	0/5	V?0
3^#	54.0±1.2	102±9	89.4±1.5	2 616±14	46.0±3.0	686±15	39	0/5	V?0
4^#	54.3±0.9	82±4	88.0±2.1	2 768±28	47.0±3.2	596±16	35	0/5	V?0
5^#	53.0±2.1	83±7	86.7±0.7	2 687±15	49.1±2.6	650±21	59	0/5	V?1
6^#	53.5±1.5	97±12	87.8±0.4	2 785±29	39.2±1.5	665±10	85	0/5	V?1
7^#	54.4±1.7	97±6	89.0±1.2	2 818±27	19.3±1.6	671±25	105	0/5	V?1

样品编号	拉伸强度/ MPa	断裂伸长/ %	弯曲强度/ MPa	弯曲模量/ MPa	冲击强度（ISO 180）/ kJ^.m^-2	冲击强度 (ASTM P256)/J^.m^-1	t₁+t₂/ s	滴落根数 (n/5)	UL 94级别（1.6 mm）
1^#	54.2±1.1	102±11	91.1±0.8	2 603±25	52.2±2.4	733±15	62	0/5	V?1
2^#	54.2±1.3	85±5	91.1±1.2	2 661±36	45.3±0.5	642±20	28	0/5	V?0
3^#	54.0±1.2	102±9	89.4±1.5	2 616±14	46.0±3.0	686±15	39	0/5	V?0
4^#	54.3±0.9	82±4	88.0±2.1	2 768±28	47.0±3.2	596±16	35	0/5	V?0
5^#	53.0±2.1	83±7	86.7±0.7	2 687±15	49.1±2.6	650±21	59	0/5	V?1
6^#	53.5±1.5	97±12	87.8±0.4	2 785±29	39.2±1.5	665±10	85	0/5	V?1
7^#	54.4±1.7	97±6	89.0±1.2	2 818±27	19.3±1.6	671±25	105	0/5	V?1

样品编号	120 ℃/0 d				120 ℃/6 d				120 ℃/12 d				120 ℃/18 d
样品编号	L	a	b	Y_I	L	a	b	Y_I	L	a	b	Y_I	L	a	b	Y_I
1^#	98.28	-0.68	1.51	11.19	97.68	-0.74	3.7	14.16	95.36	?0.05	8.97	21.27	92.22	1.03	11.54	24.95
2^#	98.38	-0.65	1.51	11.18	97.59	-0.77	3.73	14.2	96.32	?0.34	7.7	19.53	93.27	0.76	10.92	24.02
3^#	98.39	-0.69	1.51	11.18	97.58	-0.76	3.96	14.51	95.19	?0.07	8.18	20.26	93.7	0.74	10.01	22.8
4^#	98.42	-0.7	1.53	11.21	97.84	-0.8	3.54	13.95	96.0	?0.16	7.74	19.61	92.53	1.0	11.04	24.27