Determination of content of transparent nucleating agent in polypropylene using infrared spectroscopy

doi:10.19491/j.issn.1001-9278.2022.08.019

Abstract

Abstract:

In this work， a method for determining the content of sorbitol acetal?type transparent nucleating agent in polypropylene PP through infrared spectrometry was established on the basis of its characteristic absorption peak at 1 073 cm^-1 using an injection?molded specimen for calibration and test. This method eliminated the influence of sheet thickness on test results. The results showed that there was a good linear relationship between the content of transparent nucleating agent and the absorbance of characteristic peak with a correlation coefficient of 0.999 4. The recovery of the content was between 98.59 % and 100.02 %. This method exhibited the advantages of high speed， high precision and environmental protection， and it was suitable for determining the content of transparent nucleating agent in PP.

Key words: NX8000 transparent nucleating agent, polypropylene, infrared spectrometry

CLC Number:

TQ320.77

LIU Yi, WANG Ye, SUN Wei, QU Guoxing, XU Xia, YANG Shaolin, YUAN Ning. Determination of content of transparent nucleating agent in polypropylene using infrared spectroscopy[J]. China Plastics, 2022, 36(8): 115-118.

Figures/Tables 7

References 10

1	张志秋，王华，李翠勤，等.木糖醇类成核剂与山梨醇类成核剂对聚丙烯改性性能的比较［J］.中国塑料，2017，31（10）：94⁃98.
	ZHANG Z Q， WANG H， LI C Q，et al.Comparison of properties of polypropylene modified by xylitol nucleating agent and sorbitol nucleating agent［J］.China Plastics，2017，31（10）：94⁃98.
2	张志秋.山梨醇类透明成核剂合成工艺的研究［D］.大庆：大庆石油学院，2007.
3	赵秉寅.成核剂Millad NX8000的制备及其应用研究进展［J］.合成树脂及塑料，2019，36（4）：106⁃110.
	ZHANG B Y.Progress in the preparation and application of nucleating agent Millad NX8000［J］. Synthetic Resins and Plastics， 2019，36（4）： 106⁃110.
4	王丹丹.1⁃烯丙基山梨醇类聚丙烯成核剂的催化合成研究［D］.太原：山西大学，2014.
5	王立，冯开才，彭红，等.聚丙烯中二苄叉山梨醇类透明剂含量的红外光谱法测定［J］.分析测试学报，2008，4：443⁃444，447.
	WANG L， FENG K C， PENG H，et al.The determination of dibenzylidene sorbitol transparent agent in polypropylene by infrared spectroscopy ［J］. Journal of Analytical Measurement，2008，4：443⁃444，447.
6	黄秀娴.红外光谱定量聚丙烯中山梨醇缩醛类透明剂［J］.广州化工，2018，46（14）：81⁃82，99.
	HUANG X X.Determination of sorbitol acetal clarifying agent in polypropylene by fourier transform infrared spectrophotometry［J］.Guangzhou Chemical Industry，2018，46（14）：81⁃82，99.
7	马洪杰，张清，张兴国，等.一种红外光谱FTIR检测透明剂NX8000含量的方法：CN201811010157.7［P］.2018⁃08⁃31.
8	佚名. 美利肯推出新一代Millad NX8000透明剂［J］.塑料科技，2013，41（9）：89.
9	王正熙. 聚合物红外光谱分析和鉴定［M］. 成都：四川大学出版社，1989： 38⁃ 79.
10	孟令芝，何永炳. 有机波谱分析［M］. 武汉：武汉大学出版社，1997： 32⁃33.

样品	真实值/mg·kg^-1	实测值平均值/mg·kg^-1	回收率/%
2^#	1 557	1 535	98.59
3^#	2 036	2 027	99.56
4^#	3 085	3 146	100.02
5^#	4 070	4 067	99.93
6^#	5 090	5 068	99.57

样品	真实值/mg·kg^-1	实测值平均值/mg·kg^-1	回收率/%
2^#	1 557	1 535	98.59
3^#	2 036	2 027	99.56
4^#	3 085	3 146	100.02
5^#	4 070	4 067	99.93
6^#	5 090	5 068	99.57

项目	2^#样品	5^#样品
重复1/mg·kg^-1	1 554	4 045
重复2/mg·kg^-1	1 534	4 068
重复3/mg·kg^-1	1 542	4 055
重复4/mg·kg^-1	1 538	4 080
重复5/mg·kg^-1	1 546	4 075
平均值/mg·kg^-1	1 542.8	4 064.6
极差	20	35
相对标准偏差/%	0.50	0.36

项目	2^#样品	5^#样品
重复1/mg·kg^-1	1 554	4 045
重复2/mg·kg^-1	1 534	4 068
重复3/mg·kg^-1	1 542	4 055
重复4/mg·kg^-1	1 538	4 080
重复5/mg·kg^-1	1 546	4 075
平均值/mg·kg^-1	1 542.8	4 064.6
极差	20	35
相对标准偏差/%	0.50	0.36

样品	红外光谱法/mg·kg^-1	色谱法/mg·kg^-1
1	2 012	2 011
2	1 993	1 997
3	2 005	2 005
4	2 000	2 003
5	1 998	2 000
6	1 990	1 992
7	2 003	2 000
8	2 004	1 998
9	2 017	2 015
10	2 005	2 000
11	2 008	2 004