柔性环氧树脂的制备及其性能研究

doi:10.19491/j.issn.1001-9278.2019.11.001

中国塑料 ›› 2019, Vol. 33 ›› Issue (11): 1-5.DOI: 10.19491/j.issn.1001-9278.2019.11.001

• 材料与性能 • 下一篇

柔性环氧树脂的制备及其性能研究

何小强¹,邹威¹,王洪¹,李超²,张晨¹

1. 北京化工大学
2. 中铁检验认证中心有限公司

收稿日期:2019-05-09 修回日期:2019-06-26 出版日期:2019-11-26 发布日期:2019-12-27

Study on Preparation and Properties of Flexible Epoxy Resin

HE Xiaoqian¹, ZOU Wei¹, WANG Hong¹, LI Chao², ZHANG Chen¹

1.Key Laboratory of Carbon Fiber and Functional Polymers,Ministry of Education,College of Materials Science and Engineering,Beijing University of Chemical Technology,Beijing 100029,China;
2.China Railway Test & Certification CenterBeiing 100081,China

Received:2019-05-09 Revised:2019-06-26 Online:2019-11-26 Published:2019-12-27

摘要/Abstract

摘要： 通过在环氧树脂（EP）的侧链接枝柔性的聚丙二醇（PPG）制备了具有较高断裂伸长率的柔性EP。利用异佛尔酮二异氰酸酯（IPDI）中2个异氰酸酯（—NCO）基团的不同活性，首先在二月桂酸二丁基锡的催化作用下将IPDI引入EP，制备出带有NCO侧基的EP；然后再与不同相对分子质量的聚丙二醇（PPG400，PPG1000，PPG2000）进行反应，得到了具有不同长度柔性侧链的改性环氧树脂（PPG-g-EP）；使用聚醚胺（D400）作为固化剂，采用万能试验机测试固化树脂的力学性能。结果表明，柔性侧链的引入可以有效地降低材料的模量，提高其断裂伸长率，其中PPG2000改性EP的断裂伸长率最高可以达到98 %。

关键词: 环氧树脂, 柔性, 聚丙二醇, 断裂伸长率

Abstract: A type of flexible epoxy resin was synthesized by a two-step reaction, in which isophorone diisocyanate was first reacted with the hydroxyl group of epoxy resin to obtain a modified epoxy resin with the —NCO side groups and then polypropylene glycol (PPG) was grafted onto the side chains of the modified epoxy resin through the reaction between the hydroxyl groups of PPG and the —NCO groups on the modified epoxy resin to obtain polyether-grafted epoxy resin (PPG-g-EP) with different molecular weights (PPG400, PPG1000 and PPG2000). The structure of the resultant PPG-g-EP was characterized by titration and FTIR. The thermosetting PPG-g-EP was further prepared by using polyetheramine as a curing agent, and its mechanical properties were measured by a universal testing machine. The results indicated that the thermosetting PPG-g-EP with a longer PPG chain achieved higher elongation at break, and the PPG2000-modified epoxy resin gained the maximum elongation at break of 98 %.

Key words: epoxy resin, flexible, polypropylene glycol, elongation at break

中图分类号:

TQ323.5

何小强邹威王洪李超张晨. 柔性环氧树脂的制备及其性能研究[J]. 中国塑料, 2019, 33(11): 1-5.

HE Xiaoqian, ZOU Wei, WANG Hong, LI Chao, ZHANG Chen. Study on Preparation and Properties of Flexible Epoxy Resin[J]. China Plastics, 2019, 33(11): 1-5.

参考文献

[1]Emel Y, ?zdemir ?, Tülay Y?, Abdülkadir K, et al.Toughening of Epoxy Resins by Amine Terminated Poly(arylene ether ketone)s having Pendant Tertiary Butyl Groups[J].Polymer Bulletin, 2007, 58(3):503-511
[2]Dhevi D M, Prabu A A, Kim H, et al.Studies on the toughening of epoxy resin modified with varying hyperbranched polyester-toluene diisocyanate content[J].Journal of Polymer Research, 2014, 21(7):503-512
[3]Zhang Y, Shang C, Yang X, et al.Morphology and properties of TGDDMDDS epoxy systems toughened by amino-bearing phenyl silicone resins[J].Journal of Materials Science, 2012, 47(10):4415-4427
[4]Hong S G, Chan C K.The curing behaviors of the epoxydicyanamide system modified with epoxidized natural rubber[J].Thermochimica Acta, 2004, 417(1):99-106
[5]Pham T D, Vu C M, Choi H J.Enhanced fracture toughness and mechanical properties of epoxy resin with rice husk-based nano-silica[J].Polymer Science, Series A, 2017, 59(3):437-444
[6]Mathew V S, Sinturel C, George S C, et al.Epoxy resinliquid natural rubber system: secondary phase separation and its impact on mechanical properties[J].Journal of Materials Science, 2010, 45(7):1769-1781
[7]Lin K F, Yow‐Der Shieh.Core‐shell particles designed for toughening the epoxy resinsII. Core‐shell‐particle‐toughened epoxy resins[J].Journal of Applied Polymer Science, 2015, 70(12):2313-2322
[8]Wang J L, Lee M H, Yao K J, et al.Polybutylacrylatepoly (methyl methacrylate) core-shell elastic particles as epoxy resin toughener: Part IIToughness on DGEBADDM system[J].Journal of Materials Science and Technology -Shenyang, 2004, 20(6):787-790
[9]王翔, 刘韩星, 欧阳世翕, 等.环氧树脂弹性体的制备及性能研究[J].武汉理工大学学报, 2008, 30(4):16-18
[10]李久龙, 张春爱, 张孝阿, 等.高柔韧性环氧树脂胶粘剂的制备与性能[J]. 中国胶粘剂, 2016,12:25-29.[J].CHINA ADHESIVES, 2016, (12):25-29
[11] 郁文汉.一种柔性环氧树脂的制备[J]. 粘接, 2012(12):68-69.[J].Adhesion in China, 2012, (12):68-69

[1]	李正典, 宋乐, 李明昊, 何雪涛, 谢鹏程, 杨卫民. 注射成型柔性制造模具系统的设计与实验研究[J]. 中国塑料, 2022, 36(7): 104-108.
[2]	宋银宝, 杨建军, 李传敏. PDMS/SiC功能梯度复合材料性能与制造精度研究[J]. 中国塑料, 2022, 36(7): 30-36.
[3]	乔宗文, 邓嘉琪, 冀威. 用于甲醇燃料电池的聚砜阳离子交换膜的构⁃效关系[J]. 中国塑料, 2022, 36(5): 62-67.
[4]	王志刚, 杨波, 曾辰, 李智, 邓健怡. 高温内压环境下聚乙烯燃气管道老化性能评价研究[J]. 中国塑料, 2022, 36(10): 84-89.
[5]	宋仁达, 武高健, 陈俊祥, 朱金柏, 张有忱, 杨卫民, 谢鹏程. 电磁屏蔽材料的发展现状及未来发展趋势[J]. 中国塑料, 2021, 35(11): 138-143.
[6]	马昱吉, 方梅, 李贵勋, 黄明, 刘春太, 张娜. 汽车前挡玻璃夹层PVB膜厚度及含水率对性能的影响[J]. 中国塑料, 2020, 34(12): 25-28.
[7]	周念庭, 周豪, 卫茂平, 朱军, 买买提江.依米提. 不同紫外光对无机纳米材料改性聚丙烯老化行为的影响[J]. 中国塑料, 2016, 30(06): 28-33 .
[8]	刘琪, 何祥, 吕通建, 王鹏, 吴树岭. 乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯三元共聚物增韧PBT的研究[J]. 中国塑料, 2016, 30(02): 54-58 .
[9]	买买提江.依米提塞娜瓦尔·阿布拉张胜军艾买提江·萨伍提邸书新. 滴灌带紫外光人工加速老化实验方法的研究[J]. 中国塑料, 2013, 27(12): 89-93 .
[10]	买买提江.依米提邸书新艾买提江·萨伍提魏艳娇塞娜瓦尔·阿布拉. 单翼迷宫式滴灌带的老化与防老化研究[J]. 中国塑料, 2013, 27(05): 60-64 .
[11]	林微周超蔡诗俊张会轩陶朝阳. ABS树脂拉伸性能及形变机理的研究[J]. 中国塑料, 2013, 27(05): 73-76 .
[12]	于忠东. 水泥复膜塑编袋老化性能研究[J]. 中国塑料, 2011, 25(01): 80-82 .
[13]	马玉春孟庆荣张留成. 环氧树脂/液晶双马来酰胺复合材料的研究[J]. 中国塑料, 2008, 22(03): 49-51.

柔性环氧树脂的制备及其性能研究

Study on Preparation and Properties of Flexible Epoxy Resin

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 13

编辑推荐

Metrics

本文评价