Properties of Epoxy Resin/Aluminum Methylcyclohexyl Phosphinate Flame Retardant Composites

doi:10.19491/j.issn.1001-9278.2011.12.005

China Plastics ›› 2011, Vol. 25 ›› Issue (12): 17-20 .DOI: 10.19491/j.issn.1001-9278.2011.12.005

Previous Articles Next Articles

Properties of Epoxy Resin/Aluminum Methylcyclohexyl Phosphinate Flame Retardant Composites

Xueqing LIU Jiyan LIU Shan SUN Jia CHEN Shaojun CAI

Received:2011-08-29 Revised:1900-01-01 Online:2011-12-26 Published:2011-12-26

Abstract

Abstract: In this study, a novel aluminum salt of methylcyclohexylphosphinate (AMHP) was used as a flame retardant filler in EP. The flame retardant, thermal, mechanical properties, and morphology of EP/AMHP composites were investigated. It was found that the EP/AMHP composite with only 15 % AMHP achieved the optimal flame retardancy (LOI value of 28.8 and UL-94 V-0 rating). In addition, a char yield of 16.34% at 700℃ of EP/AMHP was observed. However, the addition of AMHP slightly decreased the impact and flexible properties.

Key words: flame retardant, epoxy resin, aluminum methylcyclohexyl phosphinate, thermal stability, mechanical property

Xueqing LIU Jiyan LIU Shan SUN Jia CHEN Shaojun CAI. Properties of Epoxy Resin/Aluminum Methylcyclohexyl Phosphinate Flame Retardant Composites[J]. China Plastics, 2011, 25(12): 17-20 .

[1]	YANG Jin, CHEN Pengran, GAO Peixin. Preparation and flame-retardant mechanism of epoxy foams synergistically modified with DIDOPO and POSS/EG [J]. China Plastics, 2022, 36(9): 38-45.
[2]	SONG Dejian, YU Peng, PENG Jinsong, XU Miaojun. Preparation of flame retardant EVA hot melt adhesive and its application in repairing cables [J]. China Plastics, 2022, 36(9): 53-56.
[3]	MENG Xin, WANG Xiaolong, GONG Weiguang, JIN Yi. Preparation of three⁃sources⁃in⁃one shell⁃core structural flame retardants and its application in poly（lactic acid） [J]. China Plastics, 2022, 36(9): 96-104.
[4]	JIAO Zhiwei, WANG Kechen, ZHANG Yang, YANG Weimin. Performance of PVC/ABS composites filled with carbon black and talc powders based on carbon nano coating deposition [J]. China Plastics, 2022, 36(8): 10-15.
[5]	LI Yafei, SUN Xiaojie, REN Yueqing, ZHANG Yinling. Preparation and properties of flame⁃retarded anti⁃static polyolefin plates [J]. China Plastics, 2022, 36(8): 23-27.
[6]	ZHANG Taozhong, CHEN Xiaolong, HAO Xiaoyu, YU Fujia. Comparison of mechanical properties and interfacial interactions of polypropylene composites filled with talc， calcium carbonate， and barium sulfate [J]. China Plastics, 2022, 36(8): 36-41.
[7]	CHEN Baiquan, ZHENG Youming, TIAN Jibo, XHANG Lei, WANG Jinsong, LIN Xiajie, DUAN Yapeng. Preparation and properties of polyamide flame⁃retardant composite reinforced with high content of glass fiber [J]. China Plastics, 2022, 36(8): 42-48.
[8]	WU Wei, HU Huanbo, SHEN Hui, ZHAO Tianyu. Dual⁃synergistic effect of 4A zeolite and Ca⁃Mg⁃Al hydrotalcite on intumescent flame retardant PP and its mechanism [J]. China Plastics, 2022, 36(7): 1-7.
[9]	YU Changyong, XIN Zhong. Effect of α/β complex nucleating agent based on hexahydrophthalate on properties of polypropylene [J]. China Plastics, 2022, 36(7): 121-128.
[10]	WEI Simiao, SHAO Lushan, XU Zhun, LIU Yanting, ZHAO Siheng, XU Bo. Flame⁃retardant performance of PA6 modified with hypophosphite/siloxane bi⁃functional compound and diethyl aluminum hypophosphite compound [J]. China Plastics, 2022, 36(7): 129-135.
[11]	TAN Liqin, LIU Weiqu, LIANG Liyan, WANG Shuo, FENG Zhiqiang, LIN Jiaming. Preparation and performance of epoxy resin modified with mercaptan polysiloxane [J]. China Plastics, 2022, 36(7): 21-29.
[12]	XU Jie, ZHONG Jinfu, TONG Xiaoqian, LI Guangfu, FU Dongliang, LI Chengcheng. Preparation and performance of carboxyl⁃terminated tannic acid/gallic acid⁃based epoxy composite [J]. China Plastics, 2022, 36(7): 44-50.
[13]	LI Kaize, XIN Yong. Properties of thermoplastic polyurethane composites modified with carbon nanotubes [J]. China Plastics, 2022, 36(6): 1-5.
[14]	CHEN Ke, LIU Mingfei, ZHAO Biao, PAN Kai. Research progress in flame retardancy and ablation resistance of silicone⁃modified polymeric materials [J]. China Plastics, 2022, 36(6): 149-154.
[15]	WANG Shuai, ZHANG Yudi, YANG Fukai, XU Xinyu. Preparation and properties of polyimide/multi⁃walled carbon nanotubes composite foams [J]. China Plastics, 2022, 36(6): 39-45.

Properties of Epoxy Resin/Aluminum Methylcyclohexyl Phosphinate Flame Retardant Composites

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments