环氧树脂/碳纤维复合材料模压制品翘曲变形的影响因素分析

›› 2024, Vol. 38 ›› Issue (3): 59-66.

环氧树脂/碳纤维复合材料模压制品翘曲变形的影响因素分析

赵川涛¹,贾志欣²,刘立君²,李继强²,张臣臣¹,荣迪¹,高利珍³,姚吉尔⁴

1. 浙江大学
2. 浙大宁波理工学院
3. 浙江理工大学
4. 宁波天龙电子股份有限公司

收稿日期:2023-08-15 修回日期:2023-09-12 出版日期:2024-03-26 发布日期:2024-03-26
基金资助:
宁波市重点研发计划暨“揭榜挂帅”项目 (No. 2022Z044)

Analysis of influencing factors of warpage deformation of epoxy/carbon fiber composite?molded products

Received:2023-08-15 Revised:2023-09-12 Online:2024-03-26 Published:2024-03-26

摘要/Abstract

摘要： 围绕环氧树脂/碳纤维片状模塑料模压平板制品深入研究了翘曲变形问题。用三坐标测量仪测得平板制品的平面度以表征制品的翘曲变形量。通过邓肯法多重比较各因素的水平显著性影响差异并进一步分析了各工艺参数对制品翘曲变形的影响趋势；同时分析了纤维分布、孔隙特征、上下模具温度、型腔压力分布等对制品翘曲的影响机理。结果表明，制品翘曲量分布在0.302~1.29 mm之间；通过正交实验方差分析得到模压成型工艺参数对翘曲变形的影响大小顺序为：模压压力（P）>合模速度（v）>保压时间（t）>模压温度（T），影响制品翘曲变形的显著性因素是模压压力。

关键词: 环氧树脂, 碳纤维, 片状模塑料, 模压成型, 翘曲变形

Abstract: This article addressed the issue of warping deformation in epoxy resin/carbon fiber sheet-molded composite flat panel products.， the flatness of the panel products was measured to characterize the extent of warping deformation by using a three-coordinate measurement device. The results indicated that the warping deformation varied from 0.302 to 1.29 mm. Through an orthogonal experimental variance analysis， the significance of various molding process parameters on warping deformation was determined with molding pressure having the most significant impact， followed by demolding speed， holding pressure time， and molding temperature. Furthermore， a Duncan's multiple comparison method was used to assess the differences in the significance levels among these factors， the trends in the influence of each process parameter on warping deformation in the products was further analyzed. The mechanism of influence factors for the warping of the products was analyzed， and these factors include fiber distribution， pore characteristics， upper and lower mold temperatures， and cavity pressure distribution.

Key words: epoxy, carbon, sheet molding compound, compression molding, warping deformation

赵川涛贾志欣刘立君李继强张臣臣荣迪高利珍姚吉尔. 环氧树脂/碳纤维复合材料模压制品翘曲变形的影响因素分析[J]. , 2024, 38(3): 59-66.

参考文献

[1]ALTIN KARATA? M, G?KKAYA H. A review on machinability of carbon fiber reinforced polymer (CFRP) and glass fiber reinforced polymer (GFRP) composite materials[J]. Defence Technology, 2018,14(4): 318-326.
[2]段文, 孔祥鑫. 碳纤维复合材料在汽车轻量化领域中的应用进展[J]. 汽车零部件, 2023(4): 84-87.
[3]刘宾宾. 碳纤维汽车零部件快速模压成型工艺及其结构与性能研究[J]. 合成纤维工业, 2020,43(4): 7-10.
LIU Binbin. Rapid molding technology and structural performanceof carbon fiber automobile parts[J]. China Synthetic Fiber Industry, 2020,43(4): 7-10.
[4]黎盛寓. 环氧树脂/碳纤维复合材料在汽车悬架结构中的强化设计应用[J]. 塑料科技, 2020,48(09): 81-85.
[5]SUKMAJI I C, WIJANG W R, ANDRI S, et al. Application of sandwich honeycomb carbon/glass fiber-honeycomb composite in the floor component of electric car[J]. AIP Conference Proceedings, 2017,1788(1).
[6]ZULUETA K, ARRILLAGA A, STELZER P S, et al. An evaluation of the curing characteristics of thermosetting epoxy carbon fiber sheet molding compounds and validation through computer simulations and molding trials[J]. Journal of Applied Polymer Science, 2021,138(33): 50826.
[7]BENDURE S, SHARMA A, PATIL J, et al. Physico-chemical properties of compression molded glass fiber reinforced polypropylene polymer composites[J]. Journal of physics. Conference series, 2023,2426(1): 12067.
[8]LIU Z, ZHENG X, GAO L, et al. Comparative study on the effect of cure parameters on residual deformation for thermoset composite laminates[J]. Journal of Composite Materials, 2021,55(19): 2591-2604.
[9]GONCALVES P T, ARTEIRO A, ROCHA N. Micro-mechanical analysis of the effect of ply thickness on curing micro-residual stresses in a carbon/epoxy composite laminate[J]. Composite Structures, 2023,319: 117158.
[10]张纪奎, 郦正能, 关志东, 等. 热固性树脂基复合材料固化变形影响因素分析[J]. 复合材料学报, 2009,26(1): 179-184.
[11]岳广全, 张博明, 戴福洪, 等. 固化过程中模具与复合材料构件相互作用分析[J]. 复合材料学报, 2010,27(6): 167-171.
[12]JUN L, XUEFENG Y, YINGHUA L, et al. Thermo-viscoelastic analysis of the integrated T-shaped composite structures[J]. Composites Science and Technology, 2010,70(10): 1497-1503.
[13]RADFORD D W. Volume fraction gradient induced warpage in curved composite plates[J]. Composites Engineering, 1995,5(7): 923-934.
[14]BRAUNER C, BAUER S, HERRMANN A S. Analysing process-induced deformation and stresses using a simulated manufacturing process for composite multispar flaps[J]. Journal of Composite Materials, 2015,49(4): 387-402.
[15]OSORIO L, TRUJILLO E, LENS F, et al. In-depth study of the microstructure of bamboo fibres and their relation to the mechanical properties[J]. Journal of Reinforced Plastics and Composites, 2018,37(17): 1099-1113.
[16]STAMOPOULOS A G, TSERPES K I, PRUCHA P, et al. Evaluation of porosity effects on the mechanical properties of carbon fiber-reinforced plastic unidirectional laminates by X-ray computed tomography and mechanical testing[J]. Journal of Composite Materials, 2016,50(15): 2087-2098.
[17]SHIGANG A, DAINING F, RUJIE H, et al. Effect of manufacturing defects on mechanical properties and failure features of 3D orthogonal woven C/C composites[J]. Composites Part B: Engineering, 2015,71: 113-121.
[18]SMITH R A. Composite defects and their detection[J]. Materials science and engineering, 2009,3(1): 103-143.
[19]杨雷, 刘新, 高东岳, 等. 考虑纤维随机分布的复合材料热残余应力分析及其对横向力学性能的影响[J]. 复合材料学报, 2016,33(03): 525-534.
[20]易新, 张永, 吴长波, 等. 阻燃PA66复合材料翘曲性能研究[J]. 中国塑料, 2021,35(1): 19-24.