Effect of injection molding process parameter on haze of polypropylene transparent material

doi:10.19491/j.issn.1001-9278.2024.11.016

Abstract

Abstract:

In this study， different injection molding methods were adopted to prepare the test samples of polypropylene （PP） transparent material for the measurement of fog degree. The key factors affecting the fog degree of the transparent material， such as injection pressure， injection speed， melt temperature， and pressure holding pressure were investigated. The optimal process parameters for preparing the test samples for fog degree were determined to be an injection pressure of 55.52 MPa， an injection rate of 40 mm/s， a melt temperature of 200 ℃， a mold temperature of 40 ℃， and a holding pressure of 48.58 MPa.

Key words: polypropylene transparent material, injection molding, technological parameter, haze

CLC Number:

TQ320.6

WANG Ye, LIU Yi. Effect of injection molding process parameter on haze of polypropylene transparent material[J]. China Plastics, 2024, 38(11): 93-96.

Figures/Tables 9

References 12

1	齐姝婧，刘宏吉，刘畅宇，等.我国透明聚丙烯市场供需分析及发展趋势［J］.化学工业，2023，41（02）：6⁃9.
	QI S J， LIU H J， LIU C Y，et al. Supply⁃demand analysis and development tendency of transparent polypropylene in China［J］. Chemical Industry，2023，41（02）：6⁃9.
2	刘义，王叶，孙伟，等.红外光谱法测定聚丙烯中透明成核剂含量研究［J］.中国塑料，2022，36（08）：115⁃118.
	LIU Y， WANG Y， SUN W，et al.Determination of content of transparent nucleating agent in polypropylene using infrared spectroscopy［J］China Plastics，2022，36（08）：115⁃118.
3	刘义，孙伟，曲国兴，等.薄壁注塑透明聚丙烯专用料的结构与性能分析［J］.中国塑料， 2022，36（07）：37⁃43.
	LIU Y， SUN W， QU G X，et al.Structure and performance analysis of transparent polypropylene special material for thin⁃wall injection molding ［J］.China Plastics，2022，36（07）：37⁃43.
4	全国塑料标准化技术委员会. 塑料聚丙烯（PP）模塑和挤出材料第2部分：试样制备和性能测定：［S］.北京：中国标准出版社，2022.
5	全国塑料标准化技术委员会. 塑料热塑性塑料材料注塑试样的制备第3部分：小方试片：［S］.北京：中国标准出版社，2003.
6	全国塑料标准化技术委员会. 透明塑料透光率和雾度的测定：［S］.北京：中国标准出版社，2009.
7	谢雯新，陈萍.注塑工艺对透明聚丙烯制品雾度的影响［J］.塑料包装，2013，24（3）：24⁃27.
	XIE W X， CHEN P.Influence of injection molding conditions on haze of transparent polypropylene products［J］.Plastics Packaging，2013，24（3）：24⁃27.
8	李春雷．注塑成型条件对无规共聚透明料雾度的影响研究［J］.中国煤炭，2022，48 （9）：127⁃132.
	LI C L.Research on the influence of injection molding conditions on the haze of random copolymer transparent material［J］.China Coal， 2022，48（9）：127⁃132.
9	王超先，陈宏愿，蔡春飞，等.ISO 294⁃1注塑试样制备标准的术语和注塑机操作参数［J］.塑料工业，2022，50（07）：119⁃124.
	WANG C X， CHEN H Y， CAI C F，et al.Terminology of ISO 294⁃1 for preparation of injection moulding specimens and operating parameters of injection molding machines［J］.China Plastics Industry，2022，50（07）：119⁃124.
10	王超先，王少鹏，蔡春飞，等.注塑试样制备过程中注射速率的设定方法［J］.塑料工业，2022，50（08）：84⁃88.
	WANG C X， WANG S P， CAI C F，et al.Method of injection velocity setting in the preparation of injection moulding specimens［J］.China Plastics Industry，2022，50（08）：84⁃88.
11	王欣.注塑工艺对透明聚丙烯结构性能的影响规律研究［D］.兰州：兰州理工大学，2019.
12	封春艳，黄莉，刘国强，等.制样参数对聚丙烯透明料雾度的影响［J］.理化检验（物理分册），2020，56（08）：16⁃18，22.
	FENG C Y， HUANG L， LIU G Q，et al.Effect of sample preparation parameters on haze of polypropylene transparent material［J］.Physical Testing and Chemical Analysis（Part A：Physical Testing），2020，56（08）：16⁃18，22.

熔体温度/℃		190	200	210
雾度测试结果	1	11.6	12.5	12.9
	2	11.6	12.2	12.9
	3	11.4	12.4	12.8
	4	11.3	12.3	12.7
	5	11.5	12.2	13.0
	6	11.4	12.3	13.1
平均值		11.5	12.3	12.9
极差		1.4

熔体温度/℃		190	200	210
雾度测试结果	1	11.6	12.5	12.9
	2	11.6	12.2	12.9
	3	11.4	12.4	12.8
	4	11.3	12.3	12.7
	5	11.5	12.2	13.0
	6	11.4	12.3	13.1
平均值		11.5	12.3	12.9
极差		1.4

注射压力/MPa		41.64	55.52	69.40
雾度测试结果	1	11.4	12.4	13.5
	2	11.3	12.5	13.7
	3	11.2	12.5	13.7
	4	11.3	12.4	13.5
	5	11.4	12.5	13.6
	6	11.3	12.5	13.7
平均值		11.3	12.5	13.6
极差		2.3

注射压力/MPa		41.64	55.52	69.40
雾度测试结果	1	11.4	12.4	13.5
	2	11.3	12.5	13.7
	3	11.2	12.5	13.7
	4	11.3	12.4	13.5
	5	11.4	12.5	13.6
	6	11.3	12.5	13.7
平均值		11.3	12.5	13.6
极差		2.3

注射速度/mm·s^-1		40	50	60
雾度测试结果	1	11.4	12.1	12.8
	2	10.9	12.0	13.0
	3	11.1	11.9	13.1
	4	11.0	11.7	12.8
	5	10.9	11.8	13.1
	6	11.2	11.8	12.9
平均值		11.1	11.9	13.0
极差		1.9