Research progress of adhesive materials and co⁃extrusion adhesion technology for photovoltaic backsheet

doi:10.19491/j.issn.1001-9278.2022.07.024

Abstract

Abstract:

The paper introduced the reasons， methods， and research results of modification for ethylene vinyl acetate copolymer （EVA） as an adhesive material for solar cell modules in terms of tensile strength， flame retardancy， UV aging resistance， and adhesion. In view of some defects of EVA materials， the research progress and development direction in new adhesive materials such as polyurethane and polyvinylbutyral were reviewed. Finally， the production technology of co?extruded solar backplane was briefly introduced.

Key words: solar backplane, ethylene vinyl?acetate copolymer, polyurethane, co?extrusion technology

CLC Number:

TQ325.5

ZHU Zixuan, LIU Haifen, FAN Jiazhao, LI Huafeng, WANG Lixin. Research progress of adhesive materials and co⁃extrusion adhesion technology for photovoltaic backsheet[J]. China Plastics, 2022, 36(7): 174-186.

Figures/Tables 11

References 82

1	付蒙，陈福林，岑兰. EVA的改性及应用研究进展［J］. 化工新型材料， 2014， 42（11）： 220⁃223.
	FU M， CHEN F L， CEN L. Research on modification and application of EVA［J］. New Chemical Materials， 2014， 42（11）： 220⁃223.
2	杨丽娟. 太阳能电池封装用透明热塑性聚氨酯薄膜的制备、性能与应用研究［D］. 广州：华南理工大学， 2017.
3	余鹏，李伟博，唐舫成，等. 太阳能电池封装材料研究进展［J］. 广州化工， 2011， 39（3）： 34⁃35.
	YU P， LI W B， TANG F C， et al. Research progress of encapsulants for solar cells［J］. Guangzhou Chemical Industry， 2011， 39（3）： 34⁃35.
4	PETER K， MYER E， GARY L， et al. Investigation of the degradation and stabilization of EVA⁃based encapsulant in field⁃aged solar energy modules［J］. Polymer Degradation and Stability， 1997， 55（3）： 347⁃365.
5	严长浩，王欢，吴翰，等. HDPE/EVA二元共混物敏化辐射交联与性能［J］. 塑料， 2017， 46（1）： 46⁃50.
	YAN C H， WANG H， WU H， et al. Sensitized irradiation cross⁃linking and properties of HDPE /EVA blends［J］. Plastics， 2017， 46（1）： 46⁃50.
6	王丽丽，徐佳. 改性钴镁铝类水滑石对乙烯⁃醋酸乙烯共聚物阻燃和力学性能的影响［J］.高分子材料科学与工程， 2018， 34（12）： 52⁃58.
	WANG L L， XU J. Effect of modified comgal⁃ldhs on flame retardance and mechanical properties of EVA［J］. Polymer Materials Science and Engineering， 2018， 34（12）： 52⁃58.
7	刘喜山，谷晓昱，赵斌，等. 硅酸盐纳米短纤维增强EVA复合材料的阻燃和力学性能［J］.中国塑料， 2012， 26（7）： 34⁃38.
	LIU X S， GU X Y， ZHAO B， et al. Flame retardancy and mechanical properties of silicate nanofiber reinforced EVA composites［J］. China Plastics， 2012， 26（7）： 34⁃38.
8	汪巧蕾，郑艳，丁纪恒，等. 碱木质素对 EVA 复合材料力学性能的影响［J］. 精细化工中间体， 2018， 48（3）： 55⁃60.
	WANG Q L， ZHENG Y， DING J H， et al. Effect of alkaline lignins on the mechanical properties of lignin/EVA composites［J］. Fine Chemical Intermediates， 2018， 48（3）： 55⁃60.
9	唐培，邓清田. 三聚氰胺⁃磷酸⁃氢氧化铝复合盐与氢氧化镁复配物对EVA的阻燃效果及力学性能影响研究［J］. 塑料工业， 2017， 45（10）： 125⁃128.
	TANG P， DENG Q T. Effect of the compound of melamine⁃phosphate⁃aluminum hydroxide salt and magnesium hydroxide on the flame retardant effect and mechanical properties of EVA［J］. China Plastics Industry， 2017， 45（10）： 125⁃128.
10	蒋龙，吴倩，王倩倩，等. 纤维素增强乙烯⁃乙酸乙烯酯橡胶的性能［J］. 合成橡胶工业， 2016， 39（4）： 322⁃326.
	JIANG L， WU Q， WANG Q Q， et al. Properties of cellulose⁃reinfored ethylene⁃vinyl acetate rubber［J］. China Synthetic Rubber Industry， 2016， 39（4）： 322⁃326.
11	徐迪均. 乙烯⁃甲基丙烯酸甲酯共聚物在光伏电池封装胶膜中的应用研究［D］. 温州：温州大学， 2017.
12	高喜平，李小童，王博，等. EVA无卤阻燃改性的研究进展［J］. 化工新型材料， 2019， 47（11）： 40⁃45.
	GAO X P， LI X T， WANG B， et al. Research progress in halogen⁃free flame retardancy of modified EVA［J］. New Chemical Materials， 2019， 47（11）： 40⁃45.
13	YEN Y Y， WANG H T， GUO W J. Synergistic flame retardant effect of metal hydroxide and nanoclay in EVA composites［J］. Polymer Degradation and Stability. 2012， 97（6）：863⁃869.
14	FENG C， LIANG M， JIANG J， et al. Synergistic effect of ammonium polyphosphate and triazine⁃based charring agent on the flame retardancy and combustion behavior of ethylene⁃vinyl acetate copolymer［J］. Journal of Analytical and Applied Pyrolysis， 2016， 119， 259⁃269.
15	WANG Y， ZHAO J， YUAN Y， et al. Synthesis of maleimido⁃substituted aromatic S⁃triazine and its application in flame⁃retarded epoxy resins［J］. Polymer Degradation and Stability， 2014， 99， 27⁃34.
16	许肖丽，陈彦昊，许保云，等. 邻苯二胺基环三磷腈阻燃剂在EVA材料中的性能及机理研究［J］. 上海塑料， 2021， 49（2）：39⁃44.
	XU X L， CHEN Y H， XU B Y， et al. Properties and mechanism of tri（o⁃phenylenediamine）⁃ cyclotriphosphazene flame retardant in EVA［J］. Shanghai Plastics， 2021， 49（2）：39⁃44.
17	陈镜融，谷晓昱，孙军，等. 氢氧化铝/氢氧化镁复配提高乙烯⁃醋酸乙烯共聚物阻燃性能［J］. 中国塑料， 2017， 31（9）： 68⁃72.
	CHEN J R， GU X Y， SUN J， et al. Improvement of flame retardancy of ethylene⁃vinyl⁃acetate copolymer with Al（OH）₃ and Mg（OH）₂ ［J］. China Plastics， 2017， 31（9）： 68⁃72.
18	刘帅东，崔永岩. 无卤复合协效阻燃乙烯⁃醋酸乙烯酯共聚物的性能研究［J］. 塑料科技， 2020， 48（11）： 37⁃41.
	LIU S D， CUI Y Y. Study on the performance of halogen⁃free composite synergistic flame retardant ethylene⁃vinyl acetate copolymer［J］. Plastics Science and Technology， 2020， 48（11）： 37⁃41.
19	黄健光，姜佳丽，梁敏仪，等. 三嗪成炭剂对EVA阻燃性能的影响［J］. 塑料， 2019， 48（6）： 23⁃26.
	HUANG J G， JIANG J L， LIANG M Y， et al. Effect of triazine charring agent on the flame retardant properties of EVA［J］. Plastics， 2019， 48（6）： 23⁃26.
20	魏红，李丽，梁习习，等. 增强EVA复合材料阻燃性能的PGS@P⁃N阻燃剂的制备［J］.精细化工， 2019， 36（8）： 1 513⁃1 518.
	WEI H， LI L， LIANG X X， et al. Preparation of PGS@P⁃N flame retardant for EVA composites［J］. Fine Chemicals， 2019， 36（8）： 1 513⁃1 518.
21	陈小青，申明霞. 光伏组件用EVA封装胶膜的老化研究进展［J］. 粘接， 2010， 31（12）： 65⁃69.
	CHEN X Q， SHEN M X. Research progress on aging of EVA encapsulant in photovoltaic modules［J］. Adhesion， 2010， 31（12）： 65⁃69.
22	BOGUSKI J， PRZYBYTNIAK G， LYCZKO K. New monitoring by thermogravimetry for radiation degradation of EVA［J］. Radiation Physics and Chemistry， 2014， 100， 49⁃53.
23	KOJIMA T， YANAGISAWA T. Ultraviolet⁃ray irradiation and degradation evaluation of the sealing agent EVA film for solar cells under high temperature and humidity［J］. Solar Energy Materials and Solar Cells， 2005， 85（1）： 63⁃72.
24	于淑娟，罗振静，陆树文，等. 基于点击反应大分子紫外线吸收剂的合成及在EVA中的应用［J］. 高分子材料科学与工程， 2019， 35（1）： 161⁃167.
	YU S J， LUO Z J， LU S W， et al. Synthesis of click reactive macromolecular UV absorbers and their applications in EVA［J］. Polymer Materials Science and Engineering， 2019， 35（1）： 161⁃167.
25	李建喜，张聪，陈涛，等. 接枝型耐紫外线老化乙烯⁃乙酸乙烯酯共聚物的制备及其性能研究［J］. 辐射研究与辐射工艺学报， 2014， 32（6）： 35⁃40.
	LI J X， ZHANG C， CHEN T， et al. Preparation of the permanent anti⁃UV⁃aging ethylene⁃vinyl acetate copolymer［J］. Journal of Radiation Research and Radiation Processing， 2014， 32（6）： 35⁃40.
26	曾金栋，何胡送，张好宾，等. 有机转光剂在EVA光伏胶膜中的应用及耐老化性能研究［J］. 中国胶粘剂， 2017， 26（8）： 33⁃37.
	ZENG J D， HE H S， ZHANG H B， et al. Study on application and aging resistance of organic light conversion agent in EVA photovoltaic film［J］. China Adhesives， 2017， 26（8）： 33⁃37.
27	黄方千，李强林，杨东洁，等. 有机紫外线吸收剂研究进展［J］. 印染， 2011， 37（20）： 47⁃52.
	HUANG F Q， LI Q L， YANG D J . et al. Development of organic ultraviolet absorbers［J］. Dyeing and Finishing， 2011， 37（20）： 47⁃52.
28	赵梓年，王蕊，梁李爽. 助剂对EVA胶膜黏接性能与耐老化性能的影响［J］. 天津科技大学学报， 2013， 28（6）： 32⁃35.
	ZHAO Z N， WANG R， LIANG L S. Effect of auxiliaries on the bond property and aging resistant properties of EVA sheet［J］. Journal of Tianjin University of Science & Technology， 2013， 28（6）： 32⁃35.
29	徐雪青，沈辉，邓润坤，等. 若干太阳电池封装用粘接剂的耐老化性能评价［J］. 太阳能学报， 2004， 25（4）： 438⁃442.
	XU X Q， SHEN H， DENG R K， et al. Study on stability of encapsulant for solar cells［J］. Acta Energiae Solaris Sinica， 2004， 25（4）： 438⁃442.
30	祝丽娟. 助交联剂对EVA胶膜性能的影响［J］. 山东化工， 2020， 49（5）： 19⁃20.
	ZHU L J. Effect of co⁃crosslinking agent on the properties of EVA adhesive film［J］. Shandong Chemical Industry， 2020， 49（5）： 19⁃20.
31	丁盛，张海鹏. 光伏组件用EVA封装胶膜的性能研究［J］. 粘接， 2021， 45（1）： 32⁃34.
	DING S， ZHANG H P. Study on the performance of EVA encapsulating film for photovoltaic modules［J］. Adhesion， 2021， 45（1）： 32⁃34.
32	赖伟东，吴翠姑，刘莹，等. EVA胶膜对晶硅太阳电池的封装特性研究［J］. 信息记录材料， 2020， 21（6）： 1⁃3.
	LAI W D， WU C G， LIU Y， et al. Encapsulation effect of the EVA film on the silicon photovoltaic solar cell［J］. Information Recording Material， 2020， 21（6）： 1⁃3.
33	施雯. EVA拉伸性能影响因素分析［J］. 电子世界， 2018， 23（18）： 41⁃42.
	SHI W. Analysis of influencing factors of EVA tensile properties［J］. Electronics World， 2018， 23（18）： 41⁃42.
34	CZANDERNA A W， PERN F J. Encapsulation of PV modules using ethylene vinyl acetate copolymer as a pottant： a critical review［J］. Solar Energy Materials and Solar Cells， 1996， 43（2）： 101⁃181.
35	郑文耀，张继伟，刘贤豪. 太阳能电池封装材料及技术研究进展［J］. 信息记录材料， 2011， 12（2）： 28⁃33.
	ZHENG W Y， ZHANG J W， LIU X H. Solar cells pro⁃gress in encapsulation materials and technology［J］. Information Recording Material， 2011， 12（2）： 28⁃33.
36	FU K， LU C， LIU Y， et al. Mechanically robust， self⁃healing superhydrophobic anti⁃icing coatings based on a novel fluorinated polyurethane synthesized by a two⁃step thiol click reaction［J］. Chemical Engineering Journal， 2021， 404： 127110.
37	MA H， LIU Y， GUO J， et al. Synthesis of a novel silica modified environmentally friendly waterborne polyurethane matting coating［J］. Progress in Organic Coatings， 2020， 139： 105441.
38	王乔逸，展雄威，陆少锋，等. 聚氨酯发展及改性研究现状［J］. 纺织科技进展， 2021， 4： 1⁃10.
	WANG Q Y， ZHAN X W， LU S F， et al. Research status of development and modification of polyurethane［J］. Pro⁃gress in Textile Science & Technology， 2021， 4： 1⁃10.
39	叶青萓. 以脂肪族异氰酸酯为基的聚氨酯［J］. 化学推进剂与高分子材料， 1993， 1： 47⁃51.
	YE Q Y. Polyurethane based on aliphatic isocyanate［J］. Chemical Propellants & Polymeric Materials， 1993， 1： 47⁃51.
40	WAMPRECHT C， SONNTAG M. Polyester polyols and their use as a binder component in two⁃component polyurethane coating compositions：US 6423816［P］.2002⁃09⁃01.
41	蓝立文. 高分子物理［M］. 第二版. 西安：西北工业大学出版社， 1993： 67⁃99.
42	HOOD M A， WANG B， SANDS J M， et al. Morphology control of segmented polyurethanes by crystallization of hard and soft segments［J］. Polymer， 2010， 51（10）： 2 191⁃2 198.
43	曹慧林，苑会林，王凤霞. 聚乙烯醇缩丁醛薄膜老化机理研究［J］. 塑料， 2006， 35（1）： 68⁃72.
	CAO H L， YUAN H L， WANG F X. Aging mechanism of polyvinyl butyral film［J］. Plastics， 2006， 35（1）： 68⁃72.
44	朱晓亮. 太阳电池封装用 PVB 胶膜的制备及性能研究［D］. 广州：华南理工大学， 2013.
45	MCINTOSH K R， POWELL N E， NORRIS A W， et al. The effect of damp⁃heat and UV aging tests on the optical properties of silicone and EVA encapsulants［J］. Prog Photovoltaics， 2011， 19（3）： 294⁃300.
46	曹合适，张斌珍，赵龙. PDMS仿生疏水表面的制备［J］. 微纳电子技术， 2015（5）： 329⁃333.
	CAO H S， ZHANG B Z， ZHAO L. Fabrication of a PDMS bionic hydrophobic surface［J］. Micronanoeletronic Technology， 2015（5）： 329⁃333.
47	片冈一郎，森隆弘，山田聪，等. 透光树脂密封的半导体［P］. 中国： 1119787A， 1996⁃04⁃03.
48	杜达文，汪永彬，苏玲，等.聚氨酯弹性体的研究进展［J］. 化工中间体，2013，10（11）：9⁃14.
	DU D W， WANG Y B， SU L， et al. Research process of polyurethane elastomer［J］. Chemical Intermediates， 2013，10（11）：9⁃14.
49	李绍雄，刘益军. 聚氨酯树脂及其应用［M］. 北京：化学工业出版社， 2005： 310⁃311.
50	SHEMBEL E M， SHMYRYEVA A， TODOSIICHUK T， et al. Transparent polymer materials for encapsulation of optical devices and photovoltaic module that uses this polymer： US， 0017268A1［P］. 2011⁃01⁃27.
51	张彦，汪诚，简伟任，等. 一种氟碳涂布液、一种耐UV型透明氟碳涂层及包括该涂层的透明太阳能电池背板： CN112226120A［P］. 2021⁃01⁃15.
52	张军瑞，涂伟萍，戴子林. 高性能透明聚氨酯薄膜的制备及微相分离结构［J］. 高分子材料科学与工程， 2013， 29（11）： 119⁃123.
	ZHANG J R， TU W P， DAI Z L. Synthesis and microstructure of high performance transparent polyurethane films［J］. Polymer Materials Science and Engineering， 2013， 29（11）： 119⁃123.
53	胡韬. 新型太阳能光伏电池封装材料的制备［D］. 广州：华南理工大学， 2011.
54	赵雨花，贾林才，亢茂青，等. 高性能浇筑型聚氨酯弹性体的动态性能研究［J］. 中国塑料， 2003， 17（6）： 52⁃55.
	ZHAO Y H， JIA L C， KANG M Q， et al. Study on dynamic performance of cast polyurethane elastomers with high property［J］. China Plastics， 2003， 17（6）： 52⁃55.
55	王进文.混炼型聚氨酯的新进展［J］. 世界橡胶工业，2008（4）：28⁃35.
	WANG J W. New development of mixed polyurethane［J］. World Rubber Industry， 2008（4）：28⁃35.
56	YANG Y， HAN L， ZHANG Q， et al. Monocomponent waterborne polyurethane adhesives： influence of the crosslinking agent on their properties［J］. Journal of Macromolecular Science， Part A， 2011， 48（4）： 277⁃283.
57	LIU P， LIN Y， LIU Y， et al. Preparation and properties of the main⁃chain⁃fluorinated thermoplastic polyurethane elastomer［J］. Polym Bull， 2011， 66（4）： 503⁃515.
58	张继钢，秦高原，文淑美，等. 太阳能电池封装材料聚乙烯醇缩丁醛合成工艺研究［J］. 精细与专用化学品， 2018， 26（6）： 29⁃32.
	ZHANG J G， QIN G Y， WEN S M， et al. Study on synthetic process of polyvinyl butyral in the packaging materials of PV cells［J］. Fine and Specially Chemicals， 2018， 26（6）： 29⁃32.
59	张东亮，马晓敏，李红莲，等. 纳米ATO/PVB隔热透明原位复合材料的制备及性能［J］.复合材料学报， 2013， 30（5）： 41⁃48.
	ZHANG D L， MA X M， LI H L， et al. Preparation and properties of heat⁃insulated and transparent nano⁃ATO/PVB in⁃situ composites［J］. Acta Materiae Compositae Sinica， 2013， 30（5）： 41⁃48.
60	谈秋一，陈卫，王怀峰. 一种共挤型太阳能组件背板及其制备方法： CN112659708A［P］. 2021⁃04⁃16.
61	惠振京，石亚东. 一种多层共挤型在线热压贴合太阳能背板及其制备方法： CN111844937A［P］. 2020⁃10⁃30.
62	杜晓娜，周良. 多层共挤太阳能电池背板及其生产方法： CN102779874A［P］. 2012⁃11⁃14.
63	陶国良，夏艳平. 一种无氟太阳能电池背板及其制备方法： CN103456817B［P］. 2015⁃09⁃16.
64	徐海燕，张鹏，方艳，等. 一种无氟两层共挤光伏背板： CN105176071A［P］. 2015⁃12⁃23.
65	陈洪野，王磊，吴小平，等. 一种三层结构的共挤型一次成型太阳能电池组件背板： CN105870237A［P］. 2016⁃08⁃17.
66	ORESKI G. Co⁃extruded backsheets for PV modules： Past approaches and recent developments［C］//Proc. NIST/UL Workshop Photovolt. Mater. Durability. 2019.
67	BLANCOALICE. Die with a shape［J］. Plastics Engineer，2007，63（ 4）：53.
68	肖运海，刘斌.浅析塑料异型材软硬共挤出技术［J］. 塑料科技，2008（8）：94⁃97.
	XIAO Y H， LIU B. Analysis on technology of soft⁃hard co⁃extrusion for plastic profiles［J］. Plastics Science and Technology， 2008（8）：94⁃97.
69	戚宁，柳和生，黄兴元.聚合物共挤出技术及其应用［J］. 工程塑料应用，2009，37（4）：83⁃87.
	QI N， LIU H S， HUANG X Y. The coextrusion techno⁃logy and its application［J］. Engineering Plastics Application， 2009，37（4）：83⁃87.
70	周宏志，江波，许澍华.浅析高聚物共挤出技术［J］. 橡塑技术与装备，2004（9）：4⁃14.
	ZHOU H Z， JIANG B， XU S H. Simply analyzed high polymer co⁃extrusion technique［J］. China Rubber/Plastics Technology and Equipment， 2004（9）：4⁃14.
71	谈述战，程真真，陈丽娜，等.多层共挤出薄膜技术的发展概况［J］. 塑料，2013，42（4）：42⁃45.
	TAN S Z， CHENG Z Z， CHEN L N， et al. Development of multilayer co⁃extruded film technology［J］. Plastics， 2013，42（4）：42⁃45.
72	Blow molding NPE news in blow molding ［EB/OL］. （2009⁃06⁃01）［2022⁃02⁃21］. .
73	Grande Joseph A. Outputs keep rising for PET， OPP， HDPE ［EB/OL］. （2005⁃01）［2022⁃02⁃21］. .
74	广东金明塑胶设备有限公司. BMJⅥ⁃100六层共挤塑料燃油箱中空成型机［EB/OL］.2022⁃02⁃21］. ＝67．
75	Grande Joseph A. K2007 ： What’s new at the show in blow molding ［EB/OL］.（2007⁃09⁃01）［2022⁃02⁃21］. .
76	秦川未来塑料机械有限公司.SCJC 500×6多层共挤塑料中空机［EB/OL］. ［2022⁃02⁃21］. .
77	Anonymous ．Small bottle system with dual parisons［J］. Canadian Plastics， 2009， 67（5）：14.
78	Stephen Moore ．All electric options aplenty from Japan’s blowmolding machine suppliers［EB/OL］. （2009⁃01⁃14）［2022⁃02⁃21］. .
79	PEREZ P， IYER S， THELLEN C， et al. Thermomechanical and sequential stress performance of photovoltaic backsheets［J］. Solar Energy， 2021， 216： 133⁃144.
80	THELLEN C， ROTHACKER A， SANTOLERI D， et al. Co⁃extrusion of a novel multilayer photovoltaic backsheet based on polyamide⁃ionomer alloy skin layers［C］//Proc. 33rd Eur. Photovolt. Sol. Energy Conf. Exhib. 2017： 68⁃72.
81	THELLEN C， SANTOLERI D， ROTHACKER A， et al. Cost efficient and highly weather⁃resistant solar panel backsheet produced through continuous co⁃extrusion processing［R］. Chadds Ford， PA （United States）： Tomark⁃Worthen LLC， 2020.
82	张传吉，戴建民，成三弟，等. 太阳能电池背板的现状和发展趋势［J］. 电力与能源， 2012， 33（2）： 177⁃180.
	ZHANG C J， DAI J M， CHENG S D， et al. Progress on research of photovoltaic cell backsheet［J］. Power & Energy， 2012， 33（2）： 177⁃180.

样品	剥离力/N	剥离强度/N·mm^-1
纯EVA	24.98	1.03
EVA+2 %萜烯树脂	37.35	1.64
EVA+2 %TBEC	26.13	1.22
EVA+2 %DCP	25.13	1.13
EVA+2 %TBEC+2 %萜烯树脂	159.71	6.83
EVA+2 %DCP+2 %萜烯树脂	38.01	1.69

样品	剥离力/N	剥离强度/N·mm^-1
纯EVA	24.98	1.03
EVA+2 %萜烯树脂	37.35	1.64
EVA+2 %TBEC	26.13	1.22
EVA+2 %DCP	25.13	1.13
EVA+2 %TBEC+2 %萜烯树脂	159.71	6.83
EVA+2 %DCP+2 %萜烯树脂	38.01	1.69

类型	特点及性能
聚氨酯^{［39⁃42］}	分子主链由氨基甲酸酯的重复结构单元组成，耐候性高、绝缘性好且化学稳定性好，具有较好的柔韧性。
聚乙烯醇缩丁醛（PVB）^{［43⁃44］}	通过缩合反应得到的一种热塑性高分子聚合物，在透明性、耐热性和成膜性具有优良表现，与非金属材料表现出较好的粘接性。
聚二甲基硅氧烷（PDMS）^{［45⁃46］}	分子主链中含有无机键，侧链含有有机基团，具备良好的耐热性和疏水性且体现了较低的吸湿性。
氟树脂^［47］	其中所含的氟原子电负性，使得碳氟键键能大，从而具有优异的耐候性、出色的稳定性和较高的力学强度。

类型	特点及性能
聚氨酯^{［39⁃42］}	分子主链由氨基甲酸酯的重复结构单元组成，耐候性高、绝缘性好且化学稳定性好，具有较好的柔韧性。
聚乙烯醇缩丁醛（PVB）^{［43⁃44］}	通过缩合反应得到的一种热塑性高分子聚合物，在透明性、耐热性和成膜性具有优良表现，与非金属材料表现出较好的粘接性。
聚二甲基硅氧烷（PDMS）^{［45⁃46］}	分子主链中含有无机键，侧链含有有机基团，具备良好的耐热性和疏水性且体现了较低的吸湿性。
氟树脂^［47］	其中所含的氟原子电负性，使得碳氟键键能大，从而具有优异的耐候性、出色的稳定性和较高的力学强度。

分类依据	类别	特点及性能
加工特性	浇筑型聚氨酯^［54］	不易挥发，原料选择范围大，适合大型产品的生产，其韧性较好、耐磨性优良，可在高低温条件下使用。
	热塑型聚氨酯^{［50⁃51］}	分子呈线型，化学交联较少，对温度的变化不敏感，具有较好的耐腐蚀性、抗水解能力和耐霉菌性。
	混炼型聚氨酯^［55］	力学性能稳定，可长时间保持一定的流动性，耐油性和抵抗化学品侵蚀的能力出色，气体渗透性低。
使用形式	单组份聚氨酯^［56］	无需添加交联剂得到相应的水性聚氨酯就可使用，易储藏、稳定性好，耐酸碱腐蚀，可在较大温度范围内工作。
使用形式	双组分聚氨酯^［53］	必须添加交联剂使得聚氨酯原料与其构成双组分才可使用，固化后流动性较好，易复原，耐油性优良，柔韧性较高。
设计合成	透明型聚氨酯^{［52，57］}	具有传统聚氨酯优异的力学性能，透明型好，具有良好的光学性能，防水性较好，可在高温条件下工作。