Study on polymerization modification of ground calcium carbonate and its application in poly（vinyl chloride）

doi:10.19491/j.issn.1001-9278.2024.05.011

Abstract

Abstract:

Ground calcium carbonate was modified through water grinding and polymerization modification to fit the application in poly（vinyl chloride）（PVC） pipes， and its structure and performance were investigated by using particle size analyzer， thermogravimetric analyzer， infrared spectrometer， pendulum impact testing machine， universal tensile testing machine， colorimeter， and gloss meter. The results indicated that the surface coating modification of calcium carbonate with polyvinyl acetate could be performed through in situ polymerization in calcium carbonate slurry. Compared to conventional stearic acid⁃modified calcium carbonate， polyvinyl acetate⁃modified calcium carbonate exhibited better appearance and mechanical properties in the PVC application. This is due to the fact that polyvinyl acetate can better enhance the compatibility between calcium carbonate and polyvinyl chloride.

Key words: ground calcium carbonate, poly（vinyl chloride）, polymerization modification, poly（vinyl acetate）

CLC Number:

TQ325.3

LAN Qing, HOU Xinyi, LI Yifan, PAN Kai, ZHOU Jiaju, HUANG Danmeng, HUANG Haobing. Study on polymerization modification of ground calcium carbonate and its application in poly（vinyl chloride）[J]. China Plastics, 2024, 38(5): 61-65.

Figures/Tables 8

References 11

1	Malak S A. Tensile stress strain model of polyvinyl chloride/calcium carbonate （PVC/CaCO₃） nanocomposite plank［J］. Results in Materials， 2021， 10： 100193.
2	Shaikh F U A， Supit S W M. Mechanical and durability properties of high volume fly ash （HVFA） concrete containing calcium carbonate （CaCO₃） nanoparticles［J］. Construction & Building Materials， 2014， 70（15）： 309⁃321.
3	Ali S F A， El Batouti M， Abdelhamed M， et al. Formulation and characterization of new ternary stable composites： Polyvinyl chloride⁃wood flour⁃calcium carbonate of promising physicochemical properties［J］. Journal of Materials Research and Technology， 2020， 9（6）： 12 840⁃12 854.
4	Liang C， Zheng S， Chen Z， et al. Study on surface modification of ground calcium carbonate with novel modifier and its PVC filling performance［J］. Powder Technology， 2022， 412： 118028.
5	Bao L， Yang S， Luo X， et al. Fabrication and characterization of a novel hydrophobic CaCO₃ grafted by hydroxylated poly （vinyl chloride） chains［J］. Applied Surface Science， 2015， 357： 564⁃572.
6	彭龙，何丽秋，扈廷勇. 两种不同粒度分布重质碳酸钙在PVC⁃U管材的应用对比［J］. 聚氯乙烯，2018，46（6）：23⁃26.
	PENG L， HE L Q， HU T Y. Application comparison of two kinds of ground calcium carbonate with different particle size distribution in PVC⁃U pipes［J］. Polyvinyl Chloride，2018，46（6）：23⁃26.
7	邓剑如，毛萃，孙大鹏. 桐酸酸酐水解物对重质碳酸钙表面改性的研究［J］. 湖南大学学报（自然科学版），2010，37（4）：58⁃61.
	DENG J R， MAO C， SUN D P.Study of surface modification of ground calcium carbonate by eleostearic acid anhydride hydrolyzate［J］.Journal of Hunan University（Natural Science），2010，37（4）；58⁃61.
8	谢建玲，许国志，孙辉. 塑料管道国际标准新进展［J］. 中国塑料，2011，25（2）：96⁃103.
	XIE J L， XU G Z， SUN H.Recent advances in international standards for plastic pipes［J］.China Plastics，2011，25（2）： 96⁃103.
9	李佳容，朱建国，朱书骏，等. 快速加热条件下碳酸钙分解动力学［J］.中国粉体技术，2018，24（6）： 1⁃7.
	LI J R， ZHU J G， ZHU S J，et al.Kinetics of calcium carbonate decomposition under rapid heating condition［J］.China Powder Science and Technology，2018.24（6）：1⁃7.
10	Di X， Zhang Y， Zhang N， et al. Toughening action in marble tailings/PVC composite plates： Rheological and mechanical properties［J］. Construction and Building Materials， 2022， 340： 127680.
11	徐建波，邬智勇，夏金魁，等. 极性化SBS与PVC的抗冲改性［J］. 高分子材料科学与工程，2005（3）：196⁃200.
	XU J B， WU Z Y， XIA J K，et al.The pyridyl⁃functionalized SBS and impact modification of PVC［J］.Polymer Materials Science and Engineering，2005（3）：196⁃200.

物料名称	质量份
SG5⁃PVC	100.0
二盐热稳定剂	1.8
三盐热稳定剂	2.8
硬脂酸	2.0
单甘酯	1.6
ACR⁃401	6.0
PE蜡	6.0
环氧大豆油	6.0
碳酸钙	40.0

物料名称	质量份
SG5⁃PVC	100.0
二盐热稳定剂	1.8
三盐热稳定剂	2.8
硬脂酸	2.0
单甘酯	1.6
ACR⁃401	6.0
PE蜡	6.0
环氧大豆油	6.0
碳酸钙	40.0

物料名称	质量份
PVC树脂	100
碳酸钙	60
钙锌稳定剂	6
ACR⁃801	5
CPE	2
单甘酯	4
钛白粉	2
PE蜡	3
DOP	5
红色染料	1

物料名称	质量份
PVC树脂	100
碳酸钙	60
钙锌稳定剂	6
ACR⁃801	5
CPE	2
单甘酯	4
钛白粉	2
PE蜡	3
DOP	5
红色染料	1

样品编号	助研磨剂用量/ %	D₂₅/μm	D₅₀/μm	D₇₅/μm	D₉₇/μm
1	0	0.723 5	1.136 1	1.816 6	2.979 0
2	0.1	0.635 3	0.984 3	1.597 3	2.461 0
3	0.3	0.658 2	0.877 4	1.426 1	2.192 3
4	0.5	0.613 9	0.853 3	1.286 6	2.053 6
5	0.7	0.584 7	0.826 4	1.211 3	1.992 1